Anti-scaling ball and preparation method thereof

A technology of scale inhibition and quartz powder, applied in the field of scale inhibition ball and its preparation, can solve the problems of shortening the service life, human health impact, water purifier corrosion, etc., and achieve the effect of improving the ability of scale inhibition

Inactive Publication Date: 2018-09-07
宁波清水坊环保科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the complexes used tend to cause corrosion to the surface of the water purifier, shortening the service life of the product. On the other hand, Ca 2+ , Mg 2+ The complexes will also be drunk into the body along with the purified water, which will also affect the health of the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-scaling ball and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] S1. Weigh 110kg of quartz powder, 50kg of zeolite powder, 40kg of sepiolite powder and 150kg of adhesive and put them into a mixer, stir and mix to obtain mixture 1;

[0027] S2, add 140kg water and 17.5kg surfactant in the mixture one of mixer, and stir and mix again to obtain mixture two;

[0028] S3. Add mixture 2 to the ball forming machine to make 3-5mm spheres, and put the spheres in a kiln at 1200°C for 1 hour to harden, and put them at room temperature to gradually cool;

[0029] S4. Coat the cooled sphere obtained in S3 with a nano zirconium-titanium coating, and dry to obtain a finished antiscaling ball.

[0030] Among them, the adhesive is a mixture of kaolin, petrolatum and montmorillonite powder, and their weight ratio is 3:1:1. The surfactant is a mixture of polyammonium methacrylate and dimethyl vinyl propyl ammonium chloride, and their weight ratio is 1:1. In addition, nano-zirconium and titanium coatings are made of TiO 2 , ZrO 2 , lignin, polyacryl...

Embodiment 2

[0032] S1, take by weighing 130kg quartz powder, 60kg zeolite powder, 50kg sepiolite powder and 200kg adhesive and drop into the mixer, stir and mix to obtain mixture one;

[0033] S2, add 176kg water and 22kg tensio-active agent in the mixture one of mixer, and stir and mix again to obtain mixture two;

[0034] S3. Add mixture 2 to the ball forming machine to make 3-5mm spheres, and put the spheres in a kiln at 1200°C for 1 hour to harden, and put them at room temperature to gradually cool;

[0035] S4. Coat the cooled sphere obtained in S3 with a nano zirconium-titanium coating, and dry to obtain a finished antiscaling ball.

[0036] Among them, the adhesive is a mixture of kaolin, petrolatum and montmorillonite powder, and their weight ratio is 3:1:1. The surfactant is a mixture of polyammonium methacrylate and dimethyl vinyl propyl ammonium chloride, and their weight ratio is 1:1. In addition, nano-zirconium and titanium coatings are made of TiO 2 , ZrO 2 , lignin, pol...

Embodiment 3

[0038] S1, take by weighing 120kg of quartz powder, 55kg of zeolite powder, 45kg of sepiolite powder and 175kg of adhesive and put it into a mixer, stir and mix to obtain mixture one;

[0039] S2, add 158kg water and 19.75kg tensio-active agent in the mixture one of mixer, and stir and mix again to obtain mixture two;

[0040] S3. Add mixture 2 to the ball forming machine to make 3-5mm spheres, and put the spheres in a kiln at 1200°C for 1 hour to harden, and put them at room temperature to gradually cool;

[0041] S4. Coat the cooled sphere obtained in S3 with a nano zirconium-titanium coating, and dry to obtain a finished antiscaling ball.

[0042] Among them, the adhesive is a mixture of kaolin, petrolatum and montmorillonite powder, and their weight ratio is 3:1:1. The surfactant is a mixture of polyammonium methacrylate and dimethyl vinyl propyl ammonium chloride, and their weight ratio is 1:1. In addition, nano-zirconium and titanium coatings are made of TiO 2 , ZrO ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-scaling ball, which comprises, by weight, 110-130 parts of quartz powder, 50-60 parts of zeolite powder, 40-50 parts of sepiolite powder, and 150-200 parts of an adhesive. According to the present invention, by using the technical scheme, quartz powder, zeolite powder and sepiolite powder have a large amount of pores inside, such that Ca<2+> and Mg<2+> in water canbe effectively absorbed after the anti-scaling ball prepared by adhering the quartz powder, the zeolite powder and the sepiolite powder is added to the water purification device; and quartz powder has characteristics of good hardness, wear resistance, stable chemical property and the like, such that the strength and the corrosion resistance of the ball can be effectively enhanced so as to prolongthe service life of the ball.

Description

technical field [0001] The invention relates to the technical field of antiscaling of drinking water, in particular to an antiscaling ball and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, people have gradually begun to pay attention to their own diet problems. Therefore, in order to drink relatively pure drinking water in a timely and convenient manner, many people will install a water purifier on the tap. However, the descaling technology adopted by existing water purifiers in the process of water purification often adopts chemical complexation to remove Ca in the water body. 2+ , Mg 2+ , thereby inhibiting the formation of compound precipitation in water. However, the complexes used tend to cause corrosion to the surface of the water purifier, shortening the service life of the product. On the other hand, Ca 2+ , Mg 2+ The complexes will also be drunk into the body along with the purified wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/08C04B33/04C04B33/16C04B41/87C02F5/08
CPCC02F5/08C04B33/04C04B33/16C04B38/08C04B41/009C04B41/5042C04B41/87C04B2235/3445C04B2235/3463C04B41/5041C04B41/4834C04B41/48
Inventor 杜建耀
Owner 宁波清水坊环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com