FeNiCo oxygenated chemical nanosheet with adjustable metal proportion as well as preparation method and application thereof
A compound and nanosheet technology, applied in the field of nanomaterials and electrochemistry, can solve the problems of high price, limited large-scale application, lack of resources, etc., and achieve the effects of low cost, low cost, and sufficient contact area.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] 1) A metal-organic framework ZIF-67 with a particle size of 800 nm was prepared by a static precipitation method;
[0030] 2) Weigh 0.4mmol FeSO 4 ·7H 2 O with 0.6mmol NiSO 4 ·6H 2 O, fully dissolved in 20ml of deionized water to obtain liquid A;
[0031] 3) Weigh 40mg of metal-organic framework ZIF-67 powder, fully disperse it in 5ml of absolute ethanol to obtain liquid B;
[0032] 4) Pour liquid B into liquid A quickly, and stir magnetically at room temperature for 30 minutes;
[0033] 5) The product obtained in step 4) was washed four times with a mixed solution of absolute ethanol / deionized water, and then freeze-dried to obtain FeNiCo oxygenate nanosheets with uniform morphology, namely Fe4Ni6-ZIF nanosheets.
[0034] The formation process of FexNiy-ZIF nanosheet of the present invention is as follows figure 1 Shown: After liquid A and liquid B are mixed, ZIF-67 will dissociate in the solution environment, releasing 2-methylimidazolium ions and Co 2+ , the 2...
Embodiment 2
[0039] 1) A metal-organic framework ZIF-67 with a particle size of 800 nm was prepared by a static precipitation method;
[0040] 2) Weigh 0.6mmol FeSO 4 ·7H 2 O with 0.4mmol NiSO 4 ·6H 2 O, fully dissolved in 20ml of deionized water to obtain liquid A;
[0041] 3) Weigh 40mg of metal-organic framework ZIF-67 powder, fully disperse it in 5ml of absolute ethanol to obtain liquid B;
[0042] 4) Pour liquid B into liquid A quickly, and stir magnetically at room temperature for 30 minutes;
[0043] 5) The product obtained in step 4) was washed four times with a mixed solution of absolute ethanol / deionized water, and freeze-dried to obtain FeNiCo oxygenate nanosheets with uniform morphology, namely Fe6Ni4-ZIF nanosheets.
[0044] The Fe6Ni4-ZIF nano sheet of present embodiment gained, crystallinity is low ( figure 2 It can be seen from the XRD diffraction results), the morphology is uniform ( image 3 c), ICP element analysis shows that the molar ratio of metals is Fe / Ni / Co...
Embodiment 3
[0046] 1) A metal-organic framework ZIF-67 with a particle size of 800 nm was prepared by a static precipitation method;
[0047] 2) Weigh 1.0mmol FeSO 4 ·7H 2 O, fully dissolved in 20ml of deionized water to obtain liquid A;
[0048] 3) Weigh 40mg of metal-organic framework ZIF-67 powder, fully disperse it in 5ml of absolute ethanol to obtain liquid B;
[0049] 4) Pour liquid B into liquid A quickly, and stir magnetically at room temperature for 30 minutes;
[0050] 5) The product obtained in step 4) was washed four times with a mixed solution of absolute ethanol / deionized water, and then freeze-dried to obtain FeNiCo oxygenate nanosheets with uniform morphology, namely Fe-ZIF nanosheets.
[0051] The Fe6Ni4-ZIF nano sheet of present embodiment gained, crystallinity is low ( figure 2 It can be seen from the XRD diffraction results), the morphology is uniform ( image 3 a), ICP elemental analysis shows that the molar ratio of the metal is Fe / Ni / Co≈100 / 0 / 0, which has a ce...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com