Production process of plastic woven bag

A plastic woven bag, a production process technology, applied in the direction of textile, fabric, textile and paper, can solve the problems of easy aging, easy to creep, low tensile strength and rigidity of plastic woven bags, and achieve easy flattening , prevent high temperature creep and aging, improve the effect of stiffness

Inactive Publication Date: 2018-06-22
TIANJIN HUAQING BAISHENG PLASTIC INDAL
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of society and technology, plastic woven bags have played an irreplaceable role in people's lives, but the common plastic woven bags on the market can meet the performance to a certain extent, but some plastic woven bags stretch The strength and stiffness are low, and it is prone to creep when encountering high temperature, and it is prone to aging phenomenon under light conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of production technology of plastic woven bag, comprises the following steps:

[0038] (1) Raw material ratio

[0039] This raw material component and mass percent are as follows:

[0040] Polypropylene: 65%;

[0041] Linear low density polyethylene: 15%;

[0042] Antioxidant: 0.8%;

[0043] Filler masterbatch: 7%;

[0044] Compatibilizer: 7.4%;

[0045] Light stabilizer: 0.9%;

[0046] Heat stabilizer: 1.8%;

[0047] Lubricant: 1.8%;

[0048] Cross-linking agent: 0.3%;

[0049] The filler masterbatch in this raw material is nanometer calcium carbonate, and antioxidant is antioxidant 264;

[0050] (2) Mixing

[0051] Mix the raw materials evenly and pour them into the mixer. The mixing power of the mixer is 30KW, the drying time is 10min, and the drying temperature is 80°C;

[0052] (3) drawing

[0053] The mixed material is melted and extruded in film form through a screw extruder and water-cooled. The feeding speed of the mixed material is 110kg / min...

Embodiment 2

[0066] A kind of production technology of plastic woven bag, comprises the following steps:

[0067] (1) Raw material ratio

[0068] This raw material component and mass percent are as follows:

[0069] Polypropylene: 75%;

[0070] Linear low density polyethylene: 15.32%;

[0071] Antioxidant: 0.4%;

[0072] Filler masterbatch: 1%;

[0073] Compatibilizer: 5%;

[0074] Light stabilizer: 0.4%;

[0075] Heat stabilizer: 1.2%;

[0076] Lubricant: 1.4%;

[0077] Cross-linking agent: 0.28%;

[0078] The filler masterbatch in this raw material is nanometer calcium carbonate, and antioxidant is antioxidant 264;

[0079] (2) Mixing

[0080] Mix the raw materials evenly and pour them into the mixer. The mixing power of the mixer is 37KW, the drying time is 18min, and the drying temperature is 95°C;

[0081] (3) Drawing

[0082] The mixed material is melted and extruded in film form through a screw extruder and water-cooled. The feeding speed of the mixed material is 110kg / min...

Embodiment 3

[0095] A kind of production technology of plastic woven bag, comprises the following steps:

[0096] (1) Raw material ratio

[0097] This raw material component and mass percent are as follows:

[0098] Polypropylene: 65%;

[0099] Linear low density polyethylene: 20%;

[0100] Antioxidant: 0.5%;

[0101] Filler masterbatch: 1.9%;

[0102] Compatibilizer: 9%;

[0103] Light stabilizer: 0.5%;

[0104] Heat stabilizer: 1.3%;

[0105] Lubricant: 1.5%;

[0106] Cross-linking agent: 0.3%;

[0107] The filler masterbatch in this raw material is nanometer calcium carbonate, and antioxidant is antioxidant 264;

[0108] (2) Mixing

[0109] Mix the raw materials evenly and pour them into the mixer. The mixing power of the mixer is 34KW, the drying time is 14min, and the drying temperature is 88°C;

[0110] (3) Drawing

[0111] The mixed material is melted and extruded in film form through a screw extruder and water-cooled. The feeding speed of the mixed material is 110kg / min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
linear densityaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production process of plastic woven bags. The process comprises the steps of raw material proportioning, raw material mixing, filament drawing, fabric weaving, printing, kerf cutting, examining and packaging. The production process has the advantages that heat stabilizer and light stabilizer are added to raw materials to prevent high temperature creep and aging of the plastic woven bags, packing materials with an appropriate amount are added to make the tensile strength of ribbon-like filaments stronger, the main ingredient of the packing materials is calcium carbonate, the stiffness of the ribbon-like filaments is improved, the temperature of the cooling water is appropriate, thin films are soft when the thin films are taken out of the water, the thin films areeasy to flatten , and the width of the adopted ribbon-like filaments is higher, so that the surfaces of the woven bags are more flatten, the production efficiency of a circular weaving machine is improved, and integrated sewing and packaging of a packaging machine are adopted to improve the production efficiency.

Description

technical field [0001] The invention relates to the field of plastic production, in particular to a production process of a plastic woven bag. Background technique [0002] With the rapid development of society and technology, plastic woven bags have played an irreplaceable role in people's lives, but the common plastic woven bags on the market can meet the performance to a certain extent, but some plastic woven bags stretch The strength and stiffness are low, and it is prone to creep when encountering high temperature, and it is prone to aging phenomenon under light conditions. Contents of the invention [0003] The invention aims to solve the deficiencies of the prior art, and provides a production process of plastic woven bags. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: a production process of plastic woven bags, which is characterized in that it comprises the following steps: [0005] (1) Raw materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D01D5/42D01D10/02D01D5/12D01F8/06D03D15/283
CPCD01D5/12D01D5/426D01D10/02D01F8/06D03D15/47
Inventor 吴进波吴昱铮
Owner TIANJIN HUAQING BAISHENG PLASTIC INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products