Steel antirust oil

A technology for anti-rust oil and steel, applied in the field of anti-rust oil for steel, can solve the problems of unsatisfactory anti-corrosion effect of anti-rust oil, labor-intensive, difficult to remove grease, etc., and achieves remarkable anti-corrosion effect, low cost, and anti-rust effect. Good results

Inactive Publication Date: 2018-05-22
青岛众福康制粉有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Many metal product manufacturing plants, especially those located in humid and high temperature, have suffered considerable losses due to rusting of their products or semi-finished products. Before the 1970s, a thick layer of wax or Vaseline was used to prevent rust, which cost a lot of manpower and made it difficult to remove grease before use.
The main problem of anti-rust products in China is that the anti-corrosion effect of anti-rust oil is not ideal during the storage period of steel products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A kind of antirust oil for steel made of materials with the following components:

[0012] 30 parts of heat transfer oil, 15 parts of polyester emulsion, 8 parts of isopropyl myristate, 5 parts of pentaerythritol oleate, 6 parts of fatty acid, 1 part of sodium benzoate, 2 parts of diammonium phosphate, and 1 part of triethanolamine oleate.

Embodiment 2

[0014] A kind of antirust oil for steel made of materials with the following components:

[0015] 35 parts of heat transfer oil, 16 parts of polyester emulsion, 9 parts of isopropyl myristate, 6 parts of pentaerythritol oleate, 8 parts of fatty acid, 1.6 parts of sodium benzoate, 3.4 parts of diammonium phosphate, and 2 parts of triethanolamine oleate.

Embodiment 3

[0017] A kind of antirust oil for steel made of materials with the following components:

[0018] 40 parts of heat transfer oil, 17 parts of polyester emulsion, 10 parts of isopropyl myristate, 7 parts of pentaerythritol oleate, 9 parts of fatty acid, 2 parts of sodium benzoate, 3 parts of diammonium phosphate, and 4 parts of triethanolamine oleate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a steel antirust oil, which is prepared from the following materials in parts by weight: 30 to 40 parts of heat conduction oil, 15 to 17 parts of polyester emulsion, 8 to 10 parts of isopropyl myristate, 5 to 7 parts of pentaerythritol oleate, 6 to 9 parts of fatty acid, 1 to 2 parts of sodium benzoate, 2 to 3 parts of diammonium phosphate, and 1 to 4 parts of triethanolamine oleate. The steel antirust oil has a good antirust effect and prevents steel from being rusted by dampness. The antirust period is long, the anticorrosion effect is obvious, the cost is low, and the efficiency is high.

Description

technical field [0001] The invention relates to the technical field of antirust agents, in particular to an antirust oil for steel products. Background technique [0002] Corrosion is one of the main forms of damage to fasteners, and it will cause great losses to automobiles, motorcycles and various vehicles and machinery. According to statistics, the annual direct economic loss caused by metal corrosion accounts for about 2% to 4% of the total output value of the national economy. Many metal product manufacturing plants, especially those located in humid and high temperature, have suffered considerable losses due to rusting of their products or semi-finished products. Before the 1970s, a thick layer of wax or Vaseline was used to prevent rust, which cost a lot of manpower and also caused difficulties in removing grease before use. The main problem of anti-rust products in China is that the anti-corrosion effect of anti-rust oil is not ideal during the preservation of stee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/12
CPCC10M169/048C10M2201/085C10M2207/12C10M2207/141C10M2207/281C10M2207/283C10M2209/102C10M2215/042C10N2030/12C10N2040/48
Inventor 徐广鑫
Owner 青岛众福康制粉有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products