Guitar, guitar model body, and preparation method for guitar model body

A guitar and carbon fiber technology, applied to guitars, instruments, stringed instruments, etc., can solve the problems of mechanical strength, specific strength, and flexibility that are difficult to meet in the manufacture of guitars, achieve a wide range of temperature and humidity, ensure consistency, and reduce complexity The effect of manual work

Inactive Publication Date: 2018-04-24
KINGFA SCI & TECH CO LTD +1
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since other preparation materials are crucial to its sound quality and volume, the existing thermoplastic materials are difficult to meet the needs of manufacturing guitars in terms of mechanical strength, specific strength, and flexibility.
Therefore, there is no plastic material guitar that is made of thermoplastic material and can be played directly without electricity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Guitar, guitar model body, and preparation method for guitar model body
  • Guitar, guitar model body, and preparation method for guitar model body
  • Guitar, guitar model body, and preparation method for guitar model body

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of this carbon fiber reinforced composite material includes:

[0037] Step S1: Mix acrylonitrile-butadiene-styrene copolymer, acrylonitrile-styrene copolymer and auxiliary agents in parts by weight to obtain a mixed material.

[0038] Among them, the additives are antioxidants and lubricants.

[0039] More specifically, a premixing agent is used for mixing, that is, acrylonitrile-butadiene-styrene copolymer, acrylonitrile-styrene copolymer and additives are added to the premixer in parts by weight, and mixed for 3 to 5 minutes to obtain Mix ingredients evenly.

[0040] Step S2: After mixing the mixed material with the carbon fiber, extruding and granulating.

[0041] Further, this step includes: kneading and melting the mixed material at 200-230°C, then mixing with carbon fibers, kneading and melting at 180-220°C, extruding and granulating, and cooling at 25-45°C .

[0042] Further, the carbon fiber reinforced composite material is prepared by...

Embodiment 1

[0058] The present embodiment provides a kind of guitar body, and its preparation method comprises:

[0059] The carbon fiber reinforced composite material prepared by the above carbon fiber reinforced composite material preparation method is used as a raw material and prepared by an injection molding machine, and the clamping force tonnage of the injection molding machine is 800-1000 tons.

[0060] Injection molding process: After the raw materials are melted, they are kept warm in the barrel for a period of time, and then sprayed to the temperature of the guitar-shaped body mold for injection molding.

[0061] The specific gas-assisted injection molding parameters are as follows:

[0062] Injection temperature: T1 area (160-200°C), T2 area (230-270°C), T3 area (230-270°C), T4 area (230-270°C), nozzle area (240-280°C);

[0063] Injection pressure: P1 area (60-90%), P2 area (60-90%), P3 area (60-90%), P4 area (60-90%); the total pressure is 140kgf / cm 2 .

[0064] Injection ...

Embodiment 2

[0070] The present embodiment provides a kind of guitar body, and its preparation method comprises:

[0071] The carbon fiber reinforced composite material prepared by the above carbon fiber reinforced composite material preparation method is used as a raw material and prepared by an injection molding machine, and the clamping force tonnage of the injection molding machine is 1000-1200 tons.

[0072] Injection molding process: After the raw materials are melted, they are kept warm in the barrel for a period of time, and then sprayed to the temperature of the guitar-shaped body mold for injection molding.

[0073] The specific gas-assisted injection molding parameters are as follows:

[0074] Injection temperature: T1 area (160-190°C), T2 area (240-260°C), T3 area (250-270°C), T4 area (260-270°C), nozzle area (260-280°C);

[0075] Injection pressure: P1 area (60-90%), P2 area (60-90%), P3 area (60-90%), P4 area (60-90%); the total pressure is 140kgf / cm 2 .

[0076] Injection...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention provides a guitar, a guitar model body, and a preparation method for the guitar model body, and relates to the field of guitar preparation. The guitar model body comprises a back plate,a side plate and a neck of the guitar. The guitar model body is made of a carbon fiber composite reinforcing material, and is prepared in an integrated manner through the injection molding technology.The carbon fiber composite reinforcing material contains the following components by weight: 20 to 80 parts of acrylonitrile-butadiene-styrene copolymer, 15 to 35 parts of carbon fibers, and 5 to 30parts of acrylonitrile-styrene copolymer. The guitar model body can be bound with a panel and a sound beam to form an integrated guitar, thereby greatly improving the production efficiency of the guitar. The prepared guitar is better in sound quality, and the volume and acoustic performances of the prepared guitar are higher than the volume and acoustic performances of a wood guitar. Moreover, theguitar can be directly used for performance without power.

Description

technical field [0001] The invention relates to the field of guitar preparation, in particular to a guitar, a guitar shape and a preparation method thereof. Background technique [0002] At present, there are mainly two types of guitars on the market, wooden guitars and plastic material guitars. Among them, wooden guitars are usually prepared by manual processing of specific wood to obtain major components, such as back panels, panels, side panels, sound beams and necks, etc., and then use glue to manually bond the major components. The processing of this kind of wooden guitar requires nearly 200 processes, and the processing technology is cumbersome; and specific wood is required to meet the sound quality requirements of the guitar. For example, the most commonly used material for making panels is spruce, and the quality of the panels produced is different depending on the place of origin; The back and side panels need to be hard and strong, so commonly used woods include ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G10D3/00G10D1/08G10D3/06C08L55/02C08L33/20C08K7/06
CPCC08L55/02G10D1/08G10D3/00G10D3/06C08L33/20C08K7/06
Inventor 李名敏关安南陆子天黄明瑜王海兰谭松夏超郑明嘉宁方林叶南彪周起雄
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com