Yellowing resistant modified acrylic automotive coating

An acrylic and anti-yellowing technology, used in epoxy resin coatings, coatings, etc., to solve the problems of easy discoloration, poor weather resistance, and easy discoloration

Inactive Publication Date: 2018-04-06
英德市仕曼奇化学工业有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most acrylic automotive coatings on the market have problems such as poor weather resistance, unsatisfactory coating workability, easy discoloration and discoloration when baked at high temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of anti-yellowing modified acrylic car paint, its preparation method is as follows:

[0020] The raw materials of the following weight components are put into the tank, and obtained after high-speed dispersion and stirring;

[0021] 40 parts of acrylic resin; 7 parts of epoxy resin; 4 parts of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer; 2 parts of organic bentonite; 1.5 parts of polydimethylsiloxane; 3 parts of dry agent; 0.4 parts of barium sulfate; 25 parts of deionized water;

[0022] The hydroxypropyl acrylate, methyl acrylate and lauryl acrylate copolymers are obtained through solution polymers, wherein the weight ratio of hydroxypropyl acrylate, methyl acrylate and lauryl acrylate is 1:1.5:0.4.

[0023] The preparation method of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer is as follows:

[0024] Add a total of 100 parts by weight of hydroxypropyl acrylate, methyl acrylate, and lauryl acrylate monomers to 150 ...

Embodiment 2

[0026] A kind of anti-yellowing modified acrylic car paint, its preparation method is as follows:

[0027] The raw materials of the following weight components are put into the tank, and obtained after high-speed dispersion and stirring;

[0028] 40 parts of acrylic resin; 7 parts of epoxy resin; 3 parts of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer; 1 part of castor oil derivative; 2 parts of polydimethylsiloxane; 2 parts of defoamer ; 2 parts of drying agent; 0.1 part of barium sulfate; 20 parts of deionized water;

[0029] The hydroxypropyl acrylate, methyl acrylate, and lauryl acrylate copolymers are obtained through solution polymers, wherein the weight ratio of hydroxypropyl acrylate, methyl acrylate, and lauryl acrylate is 1:2:0.5.

[0030] The preparation method of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer is as follows:

[0031] Add a total of 100 parts by weight of hydroxypropyl acrylate, methyl acrylate, and lauryl ...

Embodiment 3

[0033] A kind of anti-yellowing modified acrylic car paint, its preparation method is as follows:

[0034] The raw materials of the following weight components are put into the tank, and obtained after high-speed dispersion and stirring;

[0035] 35 parts of acrylic resin; 5 parts of epoxy resin; 5 parts of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer; 3 parts of castor oil derivatives; 1 part of polyether polyester modified organosiloxane; defoaming 1 part of drying agent; 4 parts of drying agent; 0.5 part of barium sulfate; 30 parts of deionized water;

[0036] The hydroxypropyl acrylate, methyl acrylate and lauryl acrylate copolymers are obtained through solution polymerisation, wherein the weight ratio of hydroxypropyl acrylate, methyl acrylate and lauryl acrylate is 1:1.1:0.2.

[0037] The preparation method of hydroxypropyl acrylate, methyl acrylate, lauryl acrylate copolymer is as follows:

[0038] Add a total of 100 parts by weight of hydroxypro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
hardnessaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of water-based automotive coatings and discloses a yellowing resistant modified acrylic automotive coating. The automotive coating contains the following componentsin parts by weight: 35-45 parts of acrylic resin, 5-10 parts of epoxy resin, 3-5 parts of a hydroxypropyl cycloacrylate, methyl acrylate and lauryl acrylate copolymer, 1-3 parts of an anti-settling agent, 1-2 parts of a flatting agent, 1-2 parts of an antifoaming agent, 2-4 parts of a dry promoter, 0.1-0.5 part of barium sulfate and 20-30 parts of deionized water, wherein the hydroxypropyl cycloacrylate, methyl acrylate and lauryl acrylate copolymer is prepared from a solution polymer; and a weight ratio of the hydroxypropyl cycloacrylate to methyl acrylate to lauryl acrylate is 1:(1-2):(0.2-0.5). The invention aims to provide the yellowing resistant modified acrylic automotive coating with excellent advantages of fullness, glossiness, hardness, solvent resistance, weather resistance and resistance to discoloring and yellowing during high-temperature baking.

Description

technical field [0001] The invention relates to the field of water-based automotive coatings, in particular to an anti-yellowing modified acrylic automotive coating. Background technique [0002] Nowadays, coatings are used in many fields. Because they are often exposed to the atmosphere and are eroded by oxygen and moisture, it is easy to cause metal corrosion, wood decay, and cement weathering. With the improvement of people's living standards, the requirements for various aspects of coatings All have improved, especially the requirements for the hardness, wear resistance, fullness, impact resistance, aging resistance, anti-corrosion, waterproof, oil-proof, chemical resistance, light resistance, temperature resistance and other properties of the coating are increasing. The higher it is, so it is necessary to study more advanced coatings to meet people's needs. [0003] Currently on the market, most acrylic automotive coatings have problems such as poor weather resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D163/00C09D133/08C09D7/61
CPCC09D133/04C08K2003/3045C08L2201/08C08L2205/035C08L63/00C08L33/08C08K3/30
Inventor 谢军
Owner 英德市仕曼奇化学工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com