Steel sheets, hot-dip galvanized steel sheets, and alloyed hot-dip galvanized steel sheets, and methods for their manufacture

A technology for hot-dip galvanized steel sheets and steel sheets, which is applied to steel sheets, hot-dip galvanized steel sheets and alloyed hot-dip galvanized steel sheets, and their manufacturing fields, and can solve the problem of difficulty in applying the TRIP effect, and difficulty in improving formability and delay resistance. Fracture characteristics and other problems, to achieve the effect of excellent delayed fracture resistance

Active Publication Date: 2020-05-12
NIPPON STEEL CORP
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the martensite generated after forming promotes the occurrence of delayed fracture, so it is difficult to apply the TRIP effect to a steel sheet that is intended to improve formability and delayed fracture resistance (see Non-Patent Document 2)
Thus, it is difficult to improve both formability and delayed fracture resistance of the steel sheet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel sheets, hot-dip galvanized steel sheets, and alloyed hot-dip galvanized steel sheets, and methods for their manufacture
  • Steel sheets, hot-dip galvanized steel sheets, and alloyed hot-dip galvanized steel sheets, and methods for their manufacture
  • Steel sheets, hot-dip galvanized steel sheets, and alloyed hot-dip galvanized steel sheets, and methods for their manufacture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0227] Next, examples of the present invention will be described, but the conditions in the examples are examples of conditions adopted for confirming the practicability and effects of the present invention, and the present invention is not limited to the examples of conditions. The present invention can adopt various conditions, as long as it does not depart from the gist of the present invention and achieves the purpose of the present invention, it is just.

[0228] The manufacturing method of the embodiment of the steel plate comprises: (a) directly supplying the cast slab (a1) having the composition disclosed in the table to hot rolling, followed by coiling, or (a2) heating after cooling once, and supplying to hot rolling, followed by coiling, (b) pickling, cold rolling, and annealing, (c) cooling the annealed steel sheet in two stages, and then tempering, and (d) The tempered steel plate is then cooled in two stages.

[0229] The manufacturing method of the example of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A steel sheet according to one embodiment of the present invention has a predetermined chemical composition, and the microstructure of a 1 / 4 portion of the sheet thickness of the steel sheet contains, by volume percentage, tempered martensite: 30 to 70%, and ferrite and bainite. One or two types of: the total amount is 20% or more and 70% or less, and in the structure of the above-mentioned 1 / 4 part of the plate thickness, the retained austenite is less than 10% by volume percentage, and the fresh martensite is 10% or less, Pearlite is 10% or less, their total volume percentage is 15% or less, and the number density of iron-based carbides with a major diameter of 5 nm or more in the tempered martensite at the 1 / 4 part of the plate thickness is 5×10 7 Pieces / mm 2 In the above, the ratio of the number of ε-based carbides in the 1 / 4 part of the sheet thickness to the number of the iron-based carbides with a major diameter of 5 nm or more is 20% or more, and the tensile strength of the steel sheet is 780 MPa or more. .

Description

technical field [0001] The present invention relates to a steel sheet, a hot-dip galvanized steel sheet, an alloyed hot-dip galvanized steel sheet, and a steel sheet having a tensile strength of 780 MPa or more and excellent delayed fracture resistance, which are preferable as structural members of automobiles, buildings, and home appliances, and their Manufacturing method. Background technique [0002] In recent years, steel sheets used as structural members of automobiles, buildings, home appliances, etc. have been required to have excellent delayed fracture resistance in addition to required strength and formability. Delayed fracture is a phenomenon in which hydrogen infiltrated into the steel accumulates at stress-concentrated areas and destroys the steel. [0003] Delayed fracture has long been known to occur in high-strength steel such as high-strength bolts, PC steel wire, and line pipe. Various measures for improving the delayed fracture resistance characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/58C23C2/06C23C2/28C21D8/02C21D9/46
CPCC21D8/02C23C2/06C22C38/04C22C38/58C21D9/46B32B15/013C21D6/001C21D6/002C21D6/005C21D6/008C21D8/0205C21D8/0226C21D8/0236C21D8/0247C21D2211/002C21D2211/005C21D2211/008C22C38/001C22C38/002C22C38/005C22C38/02C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/38C23C2/29C22C38/18C23C2/40C21D2211/004
Inventor 户田由梨东昌史上西朗弘川田裕之丸山直纪重里元一
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products