Coating protective material and preparation method thereof

A technology for protecting materials and coatings, applied in the field of materials, can solve problems such as cumbersome processes, difficult repairs, high labor costs, etc., and achieve the effect of simple operation process, convenient and simple maintenance, and easy mastery

Inactive Publication Date: 2018-03-13
郭艳玲
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Secondly, the above-mentioned materials are complex and cumbersome in the process of processing, requiring technicians equipped with various processing equipment and many years of work experience
Third, the coatings processed with the above materials have a thick lacquer feeling. They are afraid of being scalded by hot water and are difficult to repair. They lose the original nature, the air permeability of the material and the natural elegance.
However, this ancient process is highly technical, cumbersome, time-consuming, difficult to master, requires high labor costs, and increases costs; in addition, it also has the disadvantages of poor water resistance and fear of hot water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating protective material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The present embodiment provides a coating protection material, comprising the following raw materials:

[0027] 15g palm wax, 30g zinc stearate, 15g microcrystalline wax, 20g tea seed oil, 30g triethanolamine, 25g Tween 80, 15g Tween 20, 80g gum arabic powder, 40g diatomaceous earth, 25g paraben Ester, 20g methylparaben, 20g ethylparaben, 30g organic bentonite, 35g urea-formaldehyde resin, 40g polyethylene wax, 120gEEA resin, 40g chlorinated polyethylene, 80g chlorinated polypropylene, 220g water-soluble amino resin, 80g alkyd resin, 60g propylene glycol, 300g deionized water, 90g OP-10, 80g OP-4.

[0028] The preparation method of above-mentioned coating protective material, comprises the following steps:

[0029] (1) Mix palm wax, microcrystalline wax and tea seed oil according to the proportion and heat to 80°C to obtain mixture I;

[0030] (2) Zinc stearate, triethanolamine, and Tween 80 were mixed according to the proportion and heated to 30°C to obtain mixture I...

Embodiment 2

[0043] The present embodiment provides a coating protection material, comprising the following raw materials:

[0044] 10g palm wax, 20g zinc stearate, 20g microcrystalline wax, 15g tea seed oil, 10g triethanolamine, 15 Tween 80, 10g Tween 20, 50 gum arabic powder, 20 diatomaceous earth, 15g paraben Ester, 10g methylparaben, 30g ethylparaben, 20g organic bentonite, 20g urea-formaldehyde resin, 20g polyethylene wax, 80g EEA resin, 20g chlorinated polyethylene, 50g chlorinated polypropylene, 150g water-soluble amino resin , 50g alkyd resin, 50g propylene glycol, 200g deionized water, 60g OP-10, 50g OP-4.

[0045] The preparation method of above-mentioned coating protective material, comprises the following steps:

[0046] (1) Mix palm wax, microcrystalline wax and tea seed oil according to the proportion and heat to 75°C to obtain mixture I;

[0047] (2) Zinc stearate, triethanolamine, and Tween 80 were mixed according to the proportion and heated to 27°C to obtain mixture II;...

Embodiment 3

[0060] The present embodiment provides a coating protection material, comprising the following raw materials:

[0061] 20g palm wax, 40g zinc stearate, 10g microcrystalline wax, 30g tea seed oil, 50g triethanolamine, 30g Tween 80, 20g Tween 20, 100g gum arabic powder, 60g diatomaceous earth, 30g paraben Ester, 25g methylparaben, 10g ethylparaben, 50g organic bentonite, 50g urea-formaldehyde resin, 60g polyethylene wax, 160g EEA resin, 60g chlorinated polyethylene, 100g chlorinated polypropylene, 300g water-soluble amino resin , 100g alkyd resin, 80g propylene glycol, 400g deionized water, 120g OP-10, 100g OP-4.

[0062] The preparation method of above-mentioned coating protective material, comprises the following steps:

[0063] (1) Mix palm wax, microcrystalline wax and tea seed oil according to the proportion and heat to 85°C to obtain mixture I;

[0064] (2) Zinc stearate, triethanolamine, and Tween 80 were mixed according to the proportion and heated to 33°C to obtain mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a coating protective material and a preparation method thereof. The coating protective material comprises the following raw materials: palm wax, zinc stearate, microcrystallinewax, tea-seed oil, triethanolamine, tween 80, tween 20, Arabic gum powder, diatomite, butylparaben, methylparaben, ethylparaben, organic bentonite, urea resin, polyethylene wax, EEA resin, chlorinated polyethylene, chlorinated polypropylene, water-soluble amino resin, alkyd resin, propylene glycol, deionized water, OP-10 and OP-4. The coating protective material does not have paint feeling, is exactly like the old waxing process, is maintained by wax durably, enables furniture not to lose glossy elegance, has warm and humid hand feeling and generates feeling exactly like slurry wrapping. Thecoating protective layer can resist 100-DEG C boiling water pouring, avoids color changing and whitening and does not have any tracks; and the late maintenance is extremely convenient and simple, andthe repairing effect is as before.

Description

technical field [0001] The application belongs to the field of material technology, and in particular relates to a coating protection material and a preparation method thereof. Background technique [0002] At present, wood products and other products on the market need to be painted with materials for maintenance. The materials used include various paints, polyester paints, and water-based wood wax oil varnishes. First of all, the above materials mostly contain formaldehyde, benzene, xylene or other chemical components or heavy metals that are harmful to the human body. Secondly, the processing of the above-mentioned materials is complex and cumbersome, requiring technicians equipped with various processing equipment and years of work experience. Third, the coatings processed with the above materials all have a thick lacquer feeling, which is difficult to repair because they are afraid of being scalded by hot water, and lose the original naturalness, air permeability and n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/20C09D123/08C09D167/08C09D123/28C09D7/61C09D7/63C09D7/65
CPCC08L2205/035C09D161/20C08L23/0869C08L67/08C08L23/28C08L23/286C08L23/06C08L61/24C08L5/00C08L91/06C08K13/02C08K5/098C08K5/17C08K3/346C08K5/1345
Inventor 赵树本郭艳玲
Owner 郭艳玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap