Positive temperature coefficient heat-sensitive material and preparation method thereof

A technology of positive temperature coefficient and heat-sensitive material, applied in resistors with positive temperature coefficient, electrochemical generators, electrical components, etc. Exothermic reaction, avoid short-circuit discharge, improve the effect of anti-overcharge

Active Publication Date: 2018-01-26
DO FLUORIDE NEW ENERGY TECHNOLOGY CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the structure of this heat-sensitive material is mostly similar to ceramic materials, and when used in lithium-ion batteries, it will have a certain impact on the internal resistance of the battery
Therefore, when using it, it is necessary to limit the amount of this material used, and if the amount used is too small, the improvement of battery safety is very limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Positive temperature coefficient heat-sensitive material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The positive temperature coefficient thermosensitive material of this embodiment is made of the following raw materials: strontium source, titanium source, manganese source, metal oxide, sintering aid; the above-mentioned strontium source, titanium source, manganese source, metal oxide, sintering aid The molar ratio is 0.9915:1.0095:0.0004:0.002:0.001; the strontium source is strontium titanate, the titanium source is titanium dioxide, and the manganese source is Mn(NO 3 ) 2 , Metal oxide is Nd with a molar ratio of 1:3 2 O 3 And La 2 O 3 The sintering aid is a mixture of alumina, silica, and zirconium dioxide in a molar ratio of 0.03:0.03:0.62.

[0034] The preparation method of the positive temperature coefficient thermosensitive material of this embodiment includes the following steps:

[0035] 1) Mixing

[0036] Strontium titanate, titanium dioxide, Nd with a molar ratio of 0.9915:1.0095:0.0005:0.0015 2 O 3 , La 2 O 3 Put it into the ball mill, add water and wet mill for 6...

Embodiment 2

[0043] The positive temperature coefficient thermosensitive material of this embodiment is made of the following raw materials: strontium source, titanium source, manganese source, metal oxide, sintering aid; the above-mentioned strontium source, titanium source, manganese source, metal oxide, sintering aid The molar ratio is 0.99:1.0085:0.0005:0.005:0.002; the strontium source is strontium titanate, the titanium source is titanium dioxide, and the manganese source is Mn(NO 3 ) 2 , Metal oxide is Nd with a molar ratio of 1:3 2 O 3 And Sb 2 O 3 The sintering aid is a mixture of alumina, silica, and zirconium dioxide in a molar ratio of 0.03:0.03:0.62.

[0044] The preparation method of the positive temperature coefficient thermosensitive material of this embodiment includes the following steps:

[0045] 1) Mixing

[0046] Strontium titanate, titanium dioxide, Nd with a molar ratio of 0.99: 1.0085: 0.0005: 0.0015 2 O 3 , Sb 2 O 3 Put it into the ball mill, add water and wet mill for 6 ...

Embodiment 3

[0053] The positive temperature coefficient heat-sensitive material of this embodiment is made of the following raw materials: lead source, titanium source, manganese source, metal oxide, sintering aid; the above-mentioned lead source, titanium source, manganese source, metal oxide, sintering aid The molar ratio is 0.9915:1.0095:0.0004:0.002:0.001; the lead source is lead titanate, the titanium source is titanium dioxide, and the manganese source is Mn(NO 3 ) 2 , Metal oxide is Nd with a molar ratio of 1:3 2 O 3 And Y 2 O 3 The sintering aid is a mixture of alumina, silica, and zirconium dioxide in a molar ratio of 0.03:0.03:0.62.

[0054] The preparation method of the positive temperature coefficient thermosensitive material of this embodiment includes the following steps:

[0055] 1) Mixing

[0056] The molar ratio is 0.9915:1.0095:0.0005:0.0015 lead titanate, titanium dioxide, Nd 2 O 3 , Y 2 O 3 Put it into the ball mill, add water and wet mill for 6 hours to make it evenly mixed....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a positive temperature coefficient heat-sensitive material and a preparation method thereof, and belongs to the technical field of a heat-sensitive material. The positive temperature coefficient heat-sensitive material is prepared from a raw material comprising the following constituents: one of a strontium source and a lead source, a titanium source, a manganese source, ametal oxide and a combustion-assisted agent, wherein the mole ratio of the strontium source or the lead source, the titanium source, the manganese source, the metal oxide and the combustion-assistedagent is (99-99.5):(100.85-100.95):(0.04-0.05):(0.2-0.5):(0.1-0.2), and the metal oxide is an arbitrary oxide of Nb, Ta, Bi, Sb, Y and La or a combination of the oxide. A resistance value of the positive temperature coefficient heat-sensitive material is increased in a stepped way with temperature rising when a certain temperature (Curie temperature) is exceeded, the material has small resistanceat a temperature below the Curie temperature, and a positive temperature coefficient (PTC) layer has temperature sensitivity by the material.

Description

Technical field [0001] The invention relates to a positive temperature coefficient thermosensitive material and a preparation method thereof, and belongs to the technical field of thermosensitive materials. Background technique [0002] As an emerging technology, lithium-ion batteries have many advantages compared with traditional batteries. In the prior art, lithium-ion batteries have been widely used in various industries. The most prominent representative is that mobile phones use a single lithium-ion battery as a power source, while new energy electric vehicles basically use a lithium-ion battery pack as a power source. Based on the advantages of lithium-ion batteries at home and abroad, in recent years, they have focused on research and continuous breakthroughs in theory and engineering, and have basically mastered the application characteristics of the battery. Although lithium-ion battery packs can well meet the development needs of electric products, they have always hid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01C7/02H01M10/637
CPCY02E60/10
Inventor 杨阳李亚南赵永锋许飞罗传军刘兴福李小涛李莉仲启方
Owner DO FLUORIDE NEW ENERGY TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com