Silicone rubber for insulators and method for preparing silicone rubber

A technology for silicone rubber and insulators, which is applied in the field of insulator silicone rubber and its manufacturing, and can solve the problems that the strength of silicone rubber is difficult to meet the requirements of insulators.

Inactive Publication Date: 2017-12-29
JIANGSU TIANCHEN NEW MATERIALS
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Silicone rubber has many excellent properties such as good high and low temperature resistance, ozone resistance, weather resistance, insulation and production inertia, and is widely used in various fields of the national economy; the characteristics of silicone rubber itself and its excellent processing performance determine It has the conditions to become a material suitable for making insulators; but to be used in insulators, the strength of silicone rubber is difficult to meet the requirements of insulators. Therefore, it is very positive to study high-strength insulator silicone rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicone rubber for insulators and method for preparing silicone rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The manufacture method of the insulator silica gel of the present embodiment comprises the following steps:

[0023] a. Add methyl vinyl raw rubber with a vinyl molar content of 0.2% into the kneader and stir for 2 minutes;

[0024] b. Add white carbon black, aluminum hydroxide, stearic acid, hydroxy silicone oil and vinyl hydroxy silicone oil several times, and stir thoroughly after each addition to obtain a silicone rubber compound;

[0025] c. After kneading and molding, heat up to 140°C, vacuumize, pass cooling water to cool down to 70°C, and produce glue to obtain mixed silicone rubber;

[0026] d. Cool to room temperature after the glue is released to obtain the product.

[0027] During use, vulcanizing agent can be added for vulcanization, vulcanization at 160 degrees Celsius for 4 minutes, and secondary vulcanization at 190 degrees Celsius for 2 hours.

[0028] The parts by weight of the above-mentioned raw materials are:

[0029] 100 parts of raw rubber with...

Embodiment 2

[0036] The manufacture method of the insulator silica gel of the present embodiment comprises the following steps:

[0037] a. Add methyl vinyl raw rubber with a vinyl molar content of 0.2% into the kneader and stir for 3 minutes;

[0038] b. Add white carbon black, aluminum hydroxide, stearic acid, hydroxy silicone oil and vinyl hydroxy silicone oil several times, and stir thoroughly after each addition to obtain a silicone rubber compound;

[0039] c. After kneading and molding, heat up to 150°C, vacuumize, pass cooling water to cool down to 80°C, and produce glue to obtain mixed silicone rubber;

[0040] d. Cool to room temperature after the glue is released to obtain the product.

[0041] Vulcanizing agent can be added to vulcanize during use, vulcanized at 170 degrees Celsius for 5 minutes, and secondary vulcanized at 200 degrees Celsius for 4 hours.

[0042] The parts by weight of the above-mentioned raw materials are:

[0043] 100 parts of raw rubber with a vinyl mol...

Embodiment 3

[0052] The manufacture method of the insulator silicon rubber of the present embodiment, comprises the following steps:

[0053] a. Add methyl vinyl raw rubber with a vinyl molar content of 0.2% into the kneader and stir for 4 minutes;

[0054] b. Add white carbon black, aluminum hydroxide, stearic acid, hydroxy silicone oil and vinyl hydroxy silicone oil several times, and stir thoroughly after each addition to obtain a silicone rubber compound;

[0055] c. After kneading and forming, heat up to 160°C, vacuumize, pass cooling water to cool down to 90°C, and produce glue to obtain mixed silicone rubber;

[0056] d. Cool to room temperature after the glue is released to obtain the product.

[0057] During use, vulcanizing agent can be added for vulcanization, vulcanization at 180 degrees Celsius for 6 minutes, and secondary vulcanization at 210 degrees Celsius for 5 hours.

[0058] The parts by weight of the above-mentioned raw materials are:

[0059] 100 parts of raw rubber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a technology for manufacturing silicone rubber materials, and particularly relates to silicone rubber for insulators and a method for manufacturing the silicone rubber. The silicone rubber comprises, by weight, 100 parts of raw rubber with the vinyl molar content of 0.2%, 30-80 parts of gas-phase white carbon black, 100-500 parts of aluminum hydroxide, 3-6 parts of hydroxyl silicone oil, 3-6 parts of vinyl hydroxyl silicone oil and 2-4 parts of stearic acid. The silicone rubber in a formula and the method have the advantages that various raw materials are reasonably selected and are reasonably matched with one another, the specific method is implemented, various parameters are strictly controlled in preparation procedures, accordingly, the silicone rubber is high in strength, sufficient in hardness and processability and difficult to deform, and requirements of the composite insulators can be completely met.

Description

technical field [0001] The invention relates to a manufacturing technology of a silicon rubber material, in particular to an insulator silicon rubber and a manufacturing method thereof. Background technique [0002] Silicone rubber has many excellent properties such as good high and low temperature resistance, ozone resistance, weather resistance, insulation and production inertia, and is widely used in various fields of the national economy; the characteristics of silicone rubber itself and its excellent processing performance determine It has the conditions to become a material suitable for making insulators; but to be used in insulators, the strength of silicone rubber is difficult to meet the requirements of insulators. Therefore, the study of high-strength insulator silicone has very positive significance. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an insulator silicon rubber which not only has high str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08L83/06C08K3/36C08K3/22C08K5/09
CPCC08K2003/2227C08L83/04C08L2205/02C08L2205/025C08L2205/03C08L83/06C08K3/36C08K3/22C08K5/09
Inventor 孙宏李朋朋施贤斌耿政
Owner JIANGSU TIANCHEN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap