Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Phosphorus-free composite scale and corrosion inhibitor and application thereof, and treating method for circulating cooling water

A technology of scale and corrosion inhibitor and circulating cooling water, which is applied in non-polluted water treatment, water/sludge/sewage treatment, descaling and water softening, etc. It can solve the problem that carboxymethyl inulin is not easily soluble in water, etc. , achieve good scale and corrosion inhibition performance, meet the requirements of scale and corrosion inhibition, and avoid environmental problems

Active Publication Date: 2017-12-29
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, carboxymethyl inulin is not easily soluble in water, and there is no existing literature on the corrosion inhibition performance of carboxymethyl inulin and its application in circulating cooling water to form a composite corrosion and scale inhibitor compounded with other phosphorus-free polymer water treatment agents Reports processed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorus-free composite scale and corrosion inhibitor and application thereof, and treating method for circulating cooling water
  • Phosphorus-free composite scale and corrosion inhibitor and application thereof, and treating method for circulating cooling water
  • Phosphorus-free composite scale and corrosion inhibitor and application thereof, and treating method for circulating cooling water

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the copolymer used in the present invention may include: mixing monomers, initiators and molecular weight regulators at 50-95°C, and continuing to react at 75-95°C for 1-4h, wherein the single Solids include thiourea derivatives, unsaturated carboxylic acids and unsaturated sulfonic acids.

[0026] Wherein, the dosage and specific selection of the thiourea derivatives, unsaturated carboxylic acid and unsaturated sulfonic acid as the monomers are as mentioned above, and will not be repeated here.

[0027] According to a preferred embodiment, the mixing method when preparing the copolymer is:

[0028] (a) the solution of the monomer and the solution of the initiator are respectively added dropwise to the solution of the molecular weight regulator, or

[0029] (b) adding dropwise the solution of the monomer and the solution of the molecular weight regulator into the solution of the initiator respectively, or

[0030] (c) The solution of the init...

Embodiment 1

[0073] Weigh 30g sodium carboxymethylinulin (substitution degree is 1), 10g carboxymethyl-α-cyclodextrin and 30g copolymer 1 (the limiting viscosity at 30°C is 0.078dl / g, which is 7.2g sodium metabisulfite solution) In 20ml of water, 1.2g of ammonium persulfate was dissolved in 40ml of water, obtained by polymerization of 24.5g of monomer allylthiourea, 18g of methylene succinic acid, 18g of styrenesulfonic acid and 100ml of water, with a solid content of 30.1% by weight) , add 30g of water, and shake well to obtain the stock solution S1 of compound scale and corrosion inhibitor agent.

[0074] Take 1g of the prepared composite scale and corrosion inhibitor stock solution S1 and add them to 10L of test water 1 and 2 respectively, so that the contents of carboxymethylinulin sodium, carboxymethyl-α-cyclodextrin and copolymer in the water are respectively 6mg / L, 10mg / L and 9mg / L, then carry out the calcium carbonate scale inhibition performance measurement and the corrosion inhi...

Embodiment 2

[0076] Weigh 3.14g of zinc chloride, dissolve it in 15g of copolymer 2 (at 30°C, the limiting viscosity is 0.099dl / g, 2.4g of sodium metabisulfite is dissolved in 40ml of water, 6g of ammonium persulfite is dissolved in 20ml of water, and monomer propylene 27.6g of thiourea, 21g of acrylic acid, 12g of ethylenesulfonic acid and 100ml of water are polymerized, and the solid content is 29.6% by weight), and then 45g of sodium carboxymethylinulin (the degree of substitution is 0.6) and 18g of methyl-β-ring dextrin, and then add 8.86g of water, and shake well to obtain the composite scale and corrosion inhibitor stock solution S2.

[0077] Take 0.9g of the prepared composite scale and corrosion inhibitor stock solution S2 and add them to 10L of test water 1 and 2 respectively, so that the content of sodium carboxymethylinulin, methyl-β-cyclodextrin, copolymer and zinc ions in the water 9mg / L, 18mg / L, 4.5mg / L and 1.5mg / L respectively, and then the calcium carbonate scale inhibition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a phosphorus-free composite scale and corrosion inhibitor and application thereof, and a treating method for circulating cooling water, belonging to the field of treatment of circulating cooling water. The phosphorus-free composite scale and corrosion inhibitor contains sodium carboxymethyl inulin, a cyclodextrin derivative and a copolymer, wherein the copolymer contains a constitutional unit provided by a thiourea derivative as shown in a formula (I), a constitutional unit provided by C3-10 unsaturated carboxylic acid and a constitutional unit provided by C2-10 unsaturated sulfonic acid. The invention also provides application of the phosphorus-free composite scale and corrosion inhibitor to treatment of circulating cooling water. The treating method for circulating cooling water comprises a step of adding the phosphorus-free composite scale and corrosion inhibitor into circulating cooling water. The phosphorus-free composite scale and corrosion inhibitor provided by the invention presents good comprehensive scale and corrosion inhibition performance; and when the phosphorus-free composite scale and corrosion inhibitor is applied to treatment of circulating cooling water, requirements of circulating cooling water on scale inhibition and corrosion mitigation are met, and environmental problems caused by conventional phosphorus-containing reagents can be avoided.

Description

technical field [0001] The invention relates to the field of circulating cooling water treatment, in particular to a phosphorus-free composite scale and corrosion inhibitor, its application and a treatment method for circulating cooling water. Background technique [0002] In the circulating cooling water system, there are mainly scaling and corrosion problems. In order to prevent system scaling and corrosion, the most convenient and effective method is to add corrosion and scale inhibitors to the circulating cooling water. However, during the use of cooling water, with the continuous circulation and concentration, the mineral content in the water will continue to increase, which will intensify the corrosion and scaling of pipes and equipment. Therefore, it is necessary to add corrosion and scale inhibitors to improve the quality of cooling water and ensure The equipment operates safely. These chemicals will eventually be released into the environment as waste. However, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F5/12C02F103/02
Inventor 郦和生秦会敏冯婕吴颖谢文州楼琼慧
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com