Aluminum alloy cutting fluid and preparation method thereof

A technology of cutting fluid and aluminum alloy, applied in lubricating composition, petroleum industry, etc., can solve the problems of endangering human health, chronic poisoning, etc., and achieve the effect of strong antibacterial and bactericidal ability, low toxicity, and improved stability

Active Publication Date: 2020-02-21
ALNAN ALUMINIUM CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the same fungicide is used for a long time, the microorganisms will develop drug resistance, and the current fungicide is very toxic. After long-term contact, it will be absorbed from the skin of the human body, causing chronic poisoning and seriously endangering human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy cutting fluid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Raw materials of aluminum alloy cutting fluid (by weight): naphthenic oil 15%, sulfur-nitrogen borate 5%, potassium borate 3%, triethanolamine oleate 2%, nonionic surfactant 4%, anionic surface Active agent 2%, corrosion inhibitor 1%, rust inhibitor 1%, stabilizer 0.5%, defoamer 0.1%, compound bactericide 0.1%, and the balance is deionized water.

[0027] Anionic surfactant is composed of fatty alcohol polyoxyethylene ether sodium sulfate and polyoxyethylene ether disodium sulfosuccinate, and the weight ratio of fatty alcohol polyoxyethylene ether sodium sulfate to polyoxyethylene ether disodium sulfosuccinate is 1 -2:1.

[0028] The corrosion inhibitor is polyaspartic acid.

[0029] The rust inhibitor is a water-based rust inhibitor, and the water-based rust inhibitor is composed of diethylene glycol monobutyl ether, sorbitol, triethanolamine, diethanolamine borate, acrylate and deionized water. The weight ratio of butyl ether, sorbitol, triethanolamine, diethanolami...

Embodiment 2

[0036] Raw materials of aluminum alloy cutting fluid (by weight): naphthenic oil 20%, sulfur-nitrogen borate 6%, potassium borate 4%, triethanolamine oleate 3%, nonionic surfactant 5%, anionic surface Active agent 3%, corrosion inhibitor 2%, rust inhibitor 2%, stabilizer 1.0%, defoamer 0.5%, compound bactericide 0.2%, and the balance is deionized water.

[0037] Anionic surfactant is composed of fatty alcohol polyoxyethylene ether sodium sulfate and polyoxyethylene ether disodium sulfosuccinate, and the weight ratio of fatty alcohol polyoxyethylene ether sodium sulfate to polyoxyethylene ether disodium sulfosuccinate is 1 -2:1.

[0038] The corrosion inhibitor is a mixture of polyaspartic acid and benzotriazole.

[0039] The rust inhibitor is a water-based rust inhibitor, and the water-based rust inhibitor is composed of diethylene glycol monobutyl ether, sorbitol, triethanolamine, diethanolamine borate, acrylate and deionized water. The weight ratio of butyl ether, sorbitol...

Embodiment 3

[0044] Raw materials of aluminum alloy cutting fluid (by weight): naphthenic oil 30%, sulfur-nitrogen borate 8%, potassium borate 5%, triethanolamine oleate 4%, nonionic surfactant 8%, anionic surface Active agent 4%, corrosion inhibitor 3%, rust inhibitor 3%, stabilizer 2%, defoamer 1.0%, compound fungicide 0.5%, and the balance is deionized water.

[0045]Anionic surfactant is composed of fatty alcohol polyoxyethylene ether sodium sulfate and polyoxyethylene ether disodium sulfosuccinate, and the weight ratio of fatty alcohol polyoxyethylene ether sodium sulfate to polyoxyethylene ether disodium sulfosuccinate is 1 -2:1.

[0046] The corrosion inhibitor is a mixture of sodium metasilicate, tetraethoxysilane and methyltrimethoxysilane.

[0047] The rust inhibitor is a water-based rust inhibitor, and the water-based rust inhibitor is composed of diethylene glycol monobutyl ether, sorbitol, triethanolamine, diethanolamine borate, acrylate and deionized water. The weight ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an aluminum alloy cutting fluid and a preparation method thereof. The aluminum alloy cutting fluid is characterized by being prepared from the following raw materials in percentage by weight: 15-30% of naphthenic oil, 5-8% of borate containing sulfur and nitrogen, 3-5% of potassium borate, 2-4% of triethanolamine oleate, 4-8% of a non-ionic surfactant, 2-4% of an anionic surfactant, 1-3% of a corrosion inhibitor, 1-3% of an antirust agent, 0.5-2% of a stabilizer, 0.1-1.0% of a defoaming agent, 0.1-0.5% of a composite fungicide and the balance of deionized water. The aluminum alloy cutting fluid provided by the invention has good extreme pressure antiwear property, corrosion resistance, defoaming performance and stability, does not damage a cutting tool and is friction-free and wear-free to a workpiece, separation is easy during cutting, service life is long, and no pungent smell, low toxicity, environmental friendliness and easiness in cleaning and degradation are realized; and the aluminum alloy cutting fluid also has excellent cleaning and cooling performance and can rapidly take away a tremendous amount of heat and cutting powder produced during high-speed cutting processing.

Description

technical field [0001] The invention belongs to the technical field of metal cutting fluids, and in particular relates to an aluminum alloy cutting fluid and a preparation method thereof. Background technique [0002] In the prior art, aluminum alloys have low density, but relatively high strength, good plasticity, can be processed into various profiles, have excellent thermal conductivity and good corrosion resistance, and are widely used in industry. second to steel. However, aluminum alloys have strong chemical activity, soft texture and strong viscosity, and are prone to problems such as sticking and discoloration during processing. Therefore, the demand for special cutting fluids for aluminum alloy processing is also increasing. In the process of using the aluminum alloy cutting fluid on the market at present, the diluent will have oil soap, the emulsification speed will become slow, etc., and the oil droplets that are not fully emulsified will be adsorbed on the surfa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/00C10N40/22C10N30/06C10N30/10C10N30/16C10N30/18C10N30/12C10N30/04C10N30/08
CPCC10M173/00C10M2201/087C10M2201/102C10M2203/1065C10M2207/022C10M2207/046C10M2207/122C10M2207/281C10M2209/084C10M2209/104C10M2209/108C10M2209/109C10M2209/12C10M2215/04C10M2215/042C10M2215/223C10M2217/044C10M2219/104C10M2227/02C10M2227/061C10M2229/02C10N2020/081C10N2020/091C10N2030/04C10N2030/06C10N2030/08C10N2030/10C10N2030/12C10N2030/16C10N2030/18C10N2030/64C10N2030/72C10N2040/22C10N2040/245C10N2060/10C10N2010/02C10N2010/04C10N2060/14
Inventor 林秋仲雷素萍潘文阮海琼
Owner ALNAN ALUMINIUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com