Good appearance halogen-free flame retardant pc/pet composite material and preparation method thereof

A composite material and appearance technology, applied in the field of good appearance halogen-free flame retardant PC/PET composite material and its preparation, PC/PET composite material and its preparation field, can solve the problems of low flame retardant efficiency, composition toughness damage, compatibility Poor performance and other problems, to achieve the effect of improving appearance, improving fluidity, flame retardancy and high mechanical properties

Active Publication Date: 2019-07-09
JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with pure PC resin or mainstream PC / ABS composite materials, PC / PET composite materials are limited by halogen-free flame retardancy when used in electronics, electrical appliances and other industries, which greatly reduces the scope of use of the composite material.
At present, halogen-free flame retardants such as metal salts and phosphate esters are often used in PC resin and PC / ABS composite materials in the prior art, but any use of the above-mentioned halogen-free flame retardants will greatly affect the mechanical properties of PC / PET composite materials , and low flame retardant efficiency
In addition, the compatibility between PC resin and PET resin is poor. Due to the incompatibility between the two and the large difference in fluidity during the molding process, appearance defects such as obvious weld lines or even blackening are prone to occur, which seriously limits the composite. Application of material as weld line material
[0003] At present, in the prior art, polymeric phosphorus-containing flame retardants are used as halogen-free flame retardants to obtain halogen-free flame-retardant PC / thermoplastic polyester compositions with high flame retardancy and toughness, but polymeric phosphorus-containing flame retardants The damage to the toughness of the composition is huge. In order to make up for the loss of toughness caused by the above-mentioned polymeric phosphorus-containing flame retardants, researchers in the prior art use a large number of siloxane tougheners and polycarbonate-polydimethylsiloxane Oxyalkylene copolymer to improve toughness, although it supplements the toughness of the composition, it greatly increases the material cost of the mixture. In addition, the prior art does not involve practical application appearance evaluation, especially does not involve the appearance when it is used as a weld line material Evaluation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Good appearance halogen-free flame retardant pc/pet composite material and preparation method thereof
  • Good appearance halogen-free flame retardant pc/pet composite material and preparation method thereof
  • Good appearance halogen-free flame retardant pc/pet composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] In order to be able to understand the technical means of the present invention more clearly and implement it according to the contents of the description, the specific embodiments of the present invention will be further described in detail below in conjunction with specific examples. The following examples are used to illustrate the present invention, but not to limit it scope of the invention.

[0017] Each raw material used in the following specific examples and comparative examples is as follows:

[0018] PC resin: the viscosity average molecular weight is 20,000, the brand is S-3000F, and the manufacturer is Mitsubishi.

[0019] PET resin: the viscosity is 0.68dl / g, the grade is PET SB500, and the manufacturer is Yizheng Petrochemical.

[0020] Polystyrene resin: the grade is HIPS 622P, and the manufacturer is Shanghai Secco Petroleum.

[0021] Toughener: SBG-001, manufactured by Shanghai Rizhisheng;

[0022] M-701, the manufacturer is Zhongyuan, Japan.

[0023...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a halogen-free flame retardant PC / PET composite material with a good appearance, which comprises 60-75 parts of PC resin, 8-12 parts of PET resin, 3-10 parts of polystyrene resin, 3.0-13.0 parts of a flexibilizer, 8-20 parts of a halogen-free flame retardant, 0.05-0.3 part of an antioxidant and 0.5-0.8 part of other additives, wherein the halogen-free flame retardant is a solid poly-condensed type halogen-free phosphate flame retardant. The PC / PET composite material prepared according to the preparation method disclosed by the invention selects high impact polystyrene, so that the liquidity of the composite material is greatly promoted, the appearance of the welded wire is improved while the toughness of the composite material is not influenced, the acquired composite material is higher in liquidity, fire resistance and mechanical property and the composite material is suitable for a thin-wall part and especially is suitable for the occasion with higher requirement for use environment.

Description

technical field [0001] The invention relates to a PC / PET composite material and a preparation method thereof, in particular to a halogen-free flame-retardant PC / PET composite material with good appearance and a preparation method thereof, belonging to the technical field of polymer composite materials and processing thereof. Background technique [0002] PC / PET composite material combines the toughness, heat resistance of PC resin and solvent resistance of PET resin, etc., and has attracted more and more attention. However, compared with pure PC resin or mainstream PC / ABS composite materials, PC / PET composite materials are limited by halogen-free flame retardancy when they are used in electronics, electrical appliances and other industries, which greatly reduces the scope of use of the composite materials. At present, halogen-free flame retardants such as metal salts and phosphate esters are often used in PC resin and PC / ABS composite materials in the prior art, but any use ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L67/02C08L51/04B29C48/92
CPCB29C48/92B29C2948/9258B29C2948/92704C08L69/00C08L2201/02C08L2201/22C08L2205/035C08L67/02C08L51/04
Inventor 董相茂蒋刚军杜赏田征宇刘贤文张永夏建盟殷年伟
Owner JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products