Preparation and application of a rapid film-forming energy-saving and environmental protection machine spray fine decoration mortar

An energy-saving, environment-friendly, and film-forming technology, applied in the field of phase-change mortar materials, can solve the problems of single phase-change materials and mortar with low film-forming properties, and achieve high throwing power, improved flexibility, and stable and uniform phase change properties. Effect

Active Publication Date: 2020-10-09
绍兴职业技术学院
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the above prior art that most of the phase-change microcapsules are added to the mortar at present, using a single phase-change material, and the film-forming properties of the mortar are not considered much.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of a rapid film-forming energy-saving and environmental protection machine spray fine decoration mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Mix pentaerythritol particle solid phase change material and saturated fatty acid liquid phase change material according to the mass percentage of 30%:70%, heat and melt at 170°C, add antioxidant and ceramsite adsorption material, and adsorb at 80°C for 6h After reaching saturation, according to the mass ratio of film-forming agent and adsorbent as 1:1.8, add porous graphite sheet thermal conductivity additive and polybutadiene-modified epoxy resin film-forming agent, mix evenly, solidify and form, and cool to room temperature , to obtain a solid-liquid phase change material.

[0025] (2) In parts by weight, 150 parts of white cement, 120 parts of diatomaceous earth, 10 parts of non-ionic emulsifier, molecular weight of 1800-2300, epoxy oxygen content of 7-8% epoxy polybutane 50 parts of alkene, 100 parts of gypsum and 160 parts of solid-liquid phase change material were added to 250 parts of water, mixed evenly, solidified and molded, removed from the mold, and mai...

Embodiment 2

[0027] (1) The high-density polyethylene particle solid phase change material and the capric acid liquid phase change material are mixed according to the mass percentage of 70%:30%, heated and melted at 190° C., adding antioxidants and diatomite adsorption materials, at 90 After adsorption at ℃ for 8 hours to saturation, according to the mass ratio of film-forming agent and adsorbent as 1:2, add short carbon fiber thermal conductivity additive and polybutadiene-modified epoxy resin film-forming agent, mix evenly, and cure and form , cooled to room temperature to obtain a solid-liquid phase change material.

[0028] (2) In parts by weight, 200 parts of white cement, 150 parts of diatomaceous earth, 20 parts of nonionic emulsifier, molecular weight of 1800-2300, epoxy oxygen content of 7-8% epoxy polybutylene 80 parts of alkene, 150 parts of gypsum and 180 parts of solid-liquid phase change material were added to 400 parts of water, mixed evenly, solidified and molded, removed f...

Embodiment 3

[0030] (1) Mix the sliced ​​paraffin solid phase change material and the stearic acid liquid phase change material according to the mass percentage of 45%:55%, heat and melt at 180°C, add antioxidants and ceramsite adsorption materials, and adsorb at 85°C After 7 hours to saturation, according to the mass ratio of film-forming agent and adsorbent as 1:1.9, add short carbon fiber thermal conductivity additive and polybutadiene-modified epoxy resin film-forming agent, mix evenly, solidify and form, and cool to At room temperature, a solid-liquid phase change material is obtained.

[0031](2) In parts by weight, 180 parts of white cement, 140 parts of diatomaceous earth, 15 parts of nonionic emulsifier, molecular weight of 1800-2300, epoxy oxygen content of 7-8% epoxy polybutylene 60 parts of alkene, 130 parts of gypsum and 170 parts of solid-liquid phase change material were added to 300 parts of water, mixed evenly, solidified and molded, removed from the mold, and maintained f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides the preparation and application of a rapid film-forming energy-saving and environmental protection machine spray fine decoration mortar. The preparation method is: mixing the solid phase change material and the liquid phase change material, heating and melting, adding antioxidants and adsorption materials, and after the adsorption is saturated, Mix evenly with thermal conductivity additives and film-forming agents, solidify and form, cool to room temperature, and obtain solid-liquid phase change materials; white cement, diatomaceous earth, emulsifier, epoxidized polybutadiene, gypsum and solid-liquid phase change materials The materials are added into water, mixed evenly, cured and molded, removed from the mold, and cured for 28 days to obtain fast film-forming energy-saving and environmental protection machine spray fine decoration mortar. The refined decoration mortar prepared by the invention has high content of phase-changing materials, excellent energy storage effect, good thermal conductivity, good dispersion with mortar, good constant temperature effect, and rapid film-forming performance of epoxy-modified polybutadiene polymer Excellent, also has waterproof and anti-corrosion, therefore, the refined decoration mortar prepared by the present invention is green and constant temperature, energy-saving and durable, safe and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of phase-change mortar materials, and in particular relates to the preparation and application of a rapid film-forming energy-saving and environment-friendly spray finishing mortar. Background technique [0002] With the continuous development of new building materials, lightweight and high-efficiency thermal insulation materials are used more and more in building roof and wall materials. Phase change materials are substances that use the latent heat of phase change to realize heat storage, conversion and utilization. They can store a lot of heat energy in a small volume and keep the temperature basically unchanged during the heat absorption and heat release process. The indoor walls or the roof of the building maintain a relatively constant temperature, so that the room can maintain a good thermal comfort temperature. The comfortable temperature of the human body is 20-25°C, so it is necessary to add phase...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/20C04B111/27C04B111/34
CPCC04B28/04C04B2111/00155C04B2111/00293C04B2111/00482C04B2111/20C04B2111/27C04B2111/343C04B2201/20C04B2201/32C04B2201/50C04B24/02C04B24/08C04B18/027C04B14/024C04B20/0008C04B14/08C04B24/281C04B14/365C04B2103/608C04B2103/0068C04B24/2611C04B24/04C04B14/386C04B20/0048
Inventor 汤薇洪峰李果孙秋砚孔爱散
Owner 绍兴职业技术学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com