Argon blowing refining method for producing steel plate heat commercial (SPHC) steel

A technology of argon blowing refining and steel grades, which is applied in the manufacture of converters, etc., can solve the problems of inability to carry out mass production, nesting, and heavy corrosion of converter linings, so as to prevent secondary oxidation of molten steel and slag entrainment, and slow down The liquid level of molten steel fluctuates greatly, promoting the effect of floating and removing

Active Publication Date: 2017-10-10
LAIWU STEEL YINSHAN SECTION CO LTD
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to reduce the production cost of SPHC, the existing technology adopts the slag washing material added with the steel flow during the tapping process of the converter, that is, the slag washing technology, and the LF refining furnace adopts the argon blowing straight up process, but the following problems exist in actual production: (1 ) The tapping temperature of the converter is required to be 1680-1700°C, and the lining of the converter is severely eroded, which cannot withstand continuous and mass production; The cost of continuous casting refractory materials is high; (3) The inclusions in molten steel are high, resulting in quality defects such as peeling of rolled products, and the quality of rolled products is difficult to guarantee
The disadvantages of this patented technology: poor castability of molten steel, easy occurrence of over-holes in the nozzle of the continuous casting tundish, low number of continuous casting furnaces, and mass production cannot be carried out

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Argon blowing refining method for producing steel plate heat commercial (SPHC) steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of argon blowing refining method for producing SPHC steel grade, comprises the following steps:,

[0029] 1) Desulfurization of molten iron with a sulfur content of 0.012%;

[0030] 2) Al-Mn-Fe alloy is used for deoxidation when tapping the converter, and the addition amount is 3.3kg / t steel, so that the content of acid-soluble aluminum in the steel is controlled at 0.02%;

[0031] 3) When tapping the converter, add SPHC special pre-slag 500kg / furnace and 800Kg granular lime along with the steel flow, use a sliding plate to stop the slag when tapping, so that the thickness of the steel slag in the ladle is 60mm, the end point of the converter: carbon content 0.03%, oxygen content 600ppm, Tapping temperature 1630°C;

[0032] 4) Enter the LF refining furnace to measure the temperature and determine the oxygen: enter the LF refining furnace, blow the permeable brick at the bottom of the ladle into the station and stir for 2 minutes, the argon pressure is 0.8Mpa, an...

Embodiment 2

[0044] A kind of molten steel purification method that is used for SPHC steel class as described in embodiment 1, difference is:

[0045] A kind of argon blowing refining method for producing SPHC steel grade, comprises the following steps:,

[0046] 1) Desulfurization of molten iron with a sulfur content of 0.010%;

[0047] 2) Al-Mn-Fe alloy is used for deoxidation when tapping the converter, and the addition amount is 3.5kg / t steel, so that the content of acid-soluble aluminum in the steel is controlled to 0.04%;

[0048] 3) When tapping the converter, add 800kg / furnace of special SPHC slag and 500Kg of granular lime along with the steel flow. The slag in the early stage and the slag in the later stage are all used to block the slag with a slide plate, so that the thickness of the steel slag in the ladle is 50mm. The control target of the converter end point: carbon content 0.04%, the oxygen content is 500ppm, and the tapping temperature is 1650℃;

[0049] 4) Enter the LF ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a liquid steel purification method for steel plate heat commercial (SPHC) steel. A continuous casting tundish argon blowing upper nozzle pocket block is adopted, argon is blown in, liquid about to enter an upper nozzle is subjected to gas washing, upward floating and removing of inclusions are facilitated, a certain number of argon bubbles enter a submersed nozzle along the inner wall of the upper nozzle along with steel flow, stable and continuous annular gas flow is formed, and the problem of nodulation of the tundish nozzles is restrained. Meanwhile, an appropriate number of high-alkalinity tundish covering agents are added onto the tundish liquid face in the area over the argon blowing upper nozzle pocket block in each furnace, thus the inclusions are driven by the argon bubbles to float upward to the tundish liquid face to be absorbed in time and removed effectively by the high-alkalinity tundish covering agents, and the inclusion removing rate is increased. By applying the argon blowing refining method, the problem of eye sleeving of the continuous casting tundish nozzles is solved, the number of continuous furnace casting reaches 30 furnaces or above, thus the quantity of the metallographical inclusions in a rolled material is reduced by 40% or above on the year-on-year basis, and the quality defect caused by the inclusions in the steel is overcome.

Description

technical field [0001] The invention relates to an argon blowing refining method for producing SPHC steel grades, and belongs to the technical field of iron and steel metallurgy continuous casting tundish metallurgical technology. Background technique [0002] In order to reduce the production cost of SPHC, the existing technology adopts the slag washing material added with the steel flow during the tapping process of the converter, that is, the slag washing technology, and the LF refining furnace adopts the argon blowing straight up process, but the following problems exist in actual production: (1 ) The tapping temperature of the converter is required to be 1680-1700°C, and the lining of the converter is severely eroded, which cannot withstand continuous and mass production; The cost of continuous casting refractory materials is high; (3) The inclusions in molten steel are high, resulting in quality defects such as peeling of rolled products, and the quality of rolled prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22D1/00C21C7/072C21C5/28
CPCB22D1/002C21C5/28C21C7/072
Inventor 武光君
Owner LAIWU STEEL YINSHAN SECTION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products