Mold-proof anti-microbial tile joint mixture and preparation method thereof

An anti-mildew antibacterial agent, anti-mildew antibacterial technology, applied in the field of tile grout, can solve the problems of anti-mildew, unsatisfactory environmental protection effect, mildew breeding bacteria, trouble in life, etc. The effect of bonding force, reducing cracks, and improving the strength of caulking

Inactive Publication Date: 2017-07-07
FOSHAN LANRUI OUTE INFORMATION SERVICES CO LTD
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the effects of beautifying agents and caulking agents are not ideal in terms of mildew prevention and environmental protection, because beautifying agents and caulking agents are used in the gaps of tiles, or edge sealing such as balcony toilets, such as bathrooms, living rooms, etc. Wait
These places are prone to water accumulation, or are often cleaned with a mop, and the humidity is relatively heavy. In addition, the air pollution is relatively heavy now, and the PM data soars, so it will mold and breed bacteria, which will bring a lot of trouble to people's lives.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mold-proof anti-microbial tile joint mixture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of nano magnesium oxide modified chitosan antibacterial agent.

[0022] 1) Weigh MgCl 2 Dissolve in absolute ethanol, add PEG400 as dispersant. After mixing evenly, raise the temperature to 50-60°C, and slowly add a certain amount of ammonia-water-ethanol solution with a volume ratio of (1:1) dropwise under continuous magnetic stirring to form a white precipitate. After dripping, continue the heat preservation reaction for 1.5h, take it out, and let it stand at room temperature for aging. The precipitate was separated by filtration, and the filter cake was washed several times with water and ethanol respectively, and dried in vacuum at 60°C to obtain a white precursor. Finally, it was calcined at 500° C. for 1.5 h in an air atmosphere to obtain nano-magnesia powder.

[0023] 2) Add the nano-magnesia powder into absolute ethanol and stir evenly, ultrasonically disperse, the ultrasonic frequency is 40KHz, and the ultrasonic dispersion time is 15min, to form...

Embodiment 2

[0027] 1. Formula preparation (parts by weight)

[0028] 25 parts of vinyl acetate-ethylene copolymer emulsion;

[0029] Potassium methyl siliconate 0.8 parts;

[0030] 60 parts of 200-400 mesh quartz powder;

[0031] 0.3 parts of carbendazim;

[0032] 0.3 part of nano magnesium oxide modified chitosan antibacterial agent prepared by embodiment 1;

[0033] 0.3 parts of hydroxypropyl methylcellulose;

[0034] 0.2 parts of silicone water repellent;

[0035] 1.5 parts of glycerol;

[0036] 1.0 parts of film-forming aid

[0037] 2. Preparation:

[0038] According to the above formula, mix preservatives, anti-mold and antibacterial agents, silicone water-repellent agents, film-forming aids, and half the amount of elastic emulsion, then add them to the disperser for dispersion, and then add 200-400-mesh quartz powder, formazan Potassium silanolate and optional water glass, after feeding, increase the speed to 1000 rpm, disperse for 20 minutes; reduce the speed to 500 rpm, slow...

Embodiment 3

[0040] 1. Formula preparation (parts by weight)

[0041] 20 parts of vinyl acetate-ethylene copolymer emulsion;

[0042] Potassium methyl siliconate 1.0 part;

[0043] 55 parts of 200-400 mesh quartz powder;

[0044] Carbendazim 0.2 parts;

[0045] 0.3 part of nano magnesium oxide modified chitosan antibacterial agent prepared by embodiment 1;

[0046] 0.2 parts of hydroxypropyl methylcellulose;

[0047] 0.1 parts of silicone water repellent;

[0048] 2.0 parts of ethylene glycol;

[0049] Coalescing aid 1.5 parts

[0050] 2. Preparation:

[0051] According to the above formula, mix preservatives, anti-mold and antibacterial agents, silicone water-repellent agents, film-forming aids, and half the amount of elastic emulsion, then add them to the disperser for dispersion, and then add 200-400-mesh quartz powder, formazan Potassium silanolate and optional water glass, after feeding, increase the speed to 1000 rpm, disperse for 20 minutes; reduce the speed to 500 rpm, slow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mold-proof anti-microbial tile joint mixture and a preparation method thereof. The method comprises the following steps: taking easily acquired and low-cost nanometer magnesium oxide and chitosan as raw materials; performing chemical preparation, modifying treatment, water-bath heating compound, ice water cooling, centrifugal separation and vacuum freeze drying, thereby acquiring a nanometer magnesium oxide modified chitosan compound antibacterial agent; using the nanometer magnesium oxide modified chitosan compound antibacterial agent for preparing a tile joint mixture. The tile joint mixture prepared according to the invention has the advantages of low cost and good sterilizing effect. The color of the nanometer magnesium oxide modified chitosan is light when the nanometer magnesium oxide modified chitosan is applied to the joint mixture, so that the color of the joint mixture is not influenced.

Description

technical field [0001] The invention relates to the technical field of tile grouts, in particular to a mildew-proof and antibacterial tile grout and a preparation method thereof. Background technique [0002] At present, the effects of beautifying agents and caulking agents are not ideal in terms of mildew prevention and environmental protection, because beautifying agents and caulking agents are used in the gaps of tiles, or edge sealing such as balcony toilets, such as bathrooms, living rooms, etc. Wait. These places are prone to water accumulation, or are often cleaned with a mop, and the humidity is relatively heavy. In addition, the air pollution is relatively heavy now, and the PM data soars, so mold and bacteria will grow, which will bring a lot of trouble to people's lives. [0003] There are many types of antibacterial agents, and the classification methods are also different. Antibacterial materials can be divided into inorganic, organic and biological antibacter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/04A01N59/06A01N43/16A01P1/00A01P3/00C04B111/20
CPCC04B26/04A01N43/16A01N59/06C04B2111/00672C04B2111/2092C04B24/40C04B14/06C04B24/128C04B24/38C04B24/383C04B24/42C04B24/026C04B22/00C04B24/045A01N2300/00
Inventor 张晓辉孔令英
Owner FOSHAN LANRUI OUTE INFORMATION SERVICES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com