PC/ABS alloy material with excellent chemical substance resistance, and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An alloy material, chemical resistance technology, applied in the field of PC/ABS alloy material and its preparation, can solve the problems of poor chemical resistance, corrosion, etc., and achieve the effect of excellent hydrophobicity
Inactive Publication Date: 2017-06-16
SHANGHAI KUMHO SUNNY PLASTICS
View PDF6 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Simultaneously this invention utilizes PMMA resin itself to have better scratch resistance, promptly the addition of PMMA resin makes up for the deficiency of the scratch resistance of high-gloss PC / ABS composition, but the chemical resistance of this product is not good, because although PMMA It has certain chemical resistance, but there are still PC phase and ABS phase on the surface, and chemicals can still corrode the surface of the material
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] A PC / ABS alloy material with excellent chemical resistance and a preparation method thereof, the method comprising the following steps:
[0028] (2) Mix the components with a mixer and feed them from the main feeding port, melt and extrude at 200-260°C, the screw extruder speed is 500rpm, the pressure is 2MPa, after melt extrusion, granulation to obtain the product .
Embodiment 2
[0030] A PC / ABS alloy material with excellent chemical resistance and a preparation method thereof, the method comprising the following steps:
[0032] (2) Mix the components with a mixer and feed them from the main feeding port, melt and extrude at 200-260°C, the screw extruder speed is 500rpm, the pressure is 2MPa, after melt extrusion, granulation to obtain the product .
Embodiment 3
[0034] A PC / ABS alloy material with excellent chemical resistance and a preparation method thereof, the method comprising the following steps:
[0035] (1) Weigh each component by weight: silicon-containing PC: 60kg; ABS: 40kg; toughening agent: 5; antioxidant: 0.2; lubricant: 0.3;
[0036] (2) Mix the components with a mixer and feed them from the main feeding port, melt and extrude at 200-260°C, the screw extruder speed is 500rpm, the pressure is 2MPa, after melt extrusion, granulation to obtain the product .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a PC / ABS alloy material with excellent chemical substance resistance, and a preparation method thereof. The PC / ABS alloy material comprises, by weight, 60-80 parts of silicon-containing PC resin, 15-40 parts of ABS resin, 5-25 parts of PMMA resin, 0.1-5 parts of a flexibilizer, 0.1-1 part of an antioxidant and 0.1-1 part of a lubricant. The preparation method comprises the following steps: 1, adding the silicon-containing PC resin, the ABS resin, the PMMA resin, the flexibilizer, the antioxidant and the lubricant into a mixing stirrer, and mixing all added materials; and 2, feeding a mixture obtained in step 1 to a double screw extruder through a main feeding opening, and carrying out blend granulation to prepare the PC / ABS alloy material with excellent chemical substance resistance. The silicon-containing PC resin with excellent chemical substance resistance is used, the PMMA resin is added, and the PMMA in a molten state has a lower viscosity than the PC and the ABS and can easily aggregate on the surface of a product in the injection molding process to form a protection layer on the surface of the product in order to improve the chemical substance resistance of the PC / ABS resin.
Description
technical field [0001] The invention belongs to the fields of polymer blending and polymer molding processing, and in particular relates to a PC / ABS alloy material with excellent chemical resistance and a preparation method thereof. Background technique [0002] PC / ABS alloy material has excellent impact resistance, heat resistance and other physical properties, and is widely used in the fields of automobiles and electronic products. In recent years, under the trend of lightweight automobiles and the replacement of steel with plastics, more and more automobile interior and exterior decoration materials have begun to use PC / ABS. In the automotive industry, more and more manufacturers have begun to pay attention to environmental protection and cost reduction, and have begun to abandon the post-treatment process of painting and electroplating, and directly use plastic parts. [0003] Directly exposed plastic parts are easily exposed to some chemicals, such as car glass washer ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.