CSF-RBF-ALF3 Flux Containing Nanometer Rare Earth Fluoride

A csf-rbf-alf3, nano-rare earth technology, applied in the direction of welding/welding/cutting items, welding equipment, manufacturing tools, etc., to achieve stable performance, simple preparation process, and excellent wetting effect

Active Publication Date: 2018-12-28
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Although the above-mentioned fluxes can realize the reliable connection of "aluminum-copper", "aluminum-steel" and "aluminum-aluminum", there are still many shortcomings and needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CSF-RBF-ALF3 Flux Containing Nanometer Rare Earth Fluoride

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] CsF-RbF-AlF Containing Nanometer Rare Earth Fluoride 3 Flux, by mass percentage (wt.%), the chemical composition is: 0.02% rubidium fluoride (RbF), 48.0% cesium fluoride (CsF), 0.01% aluminum oxide (Al 2 o 3 ), 1.0% potassium fluoride (KF), 0.001% nano cerium tetrafluoride (CeF 4 ), the balance is aluminum fluoride (AlF 3 ).

[0039] The new CsF-RbF-AlF containing nano-rare earth fluoride obtained by the above ratio 3 Brazing flux, using propane as combustible gas for flame brazing, with Zn85-Al15 solder, Al88-Si12 solder, combined with 5052 aluminum alloy plate + Q235 steel plate, 6063 aluminum alloy plate + T2 red copper, according to GB / T 11363- 2008 "Brazed Joint Strength Test Method" was tested, and the shear strength of the brazed joint reached 130MPa-150MPa respectively.

Embodiment 2

[0041] CsF-RbF-AlF Containing Nanometer Rare Earth Fluoride 3 Flux, by mass percentage (wt.%), the chemical composition is: 0.2% rubidium fluoride (RbF), 20.0% cesium fluoride (CsF), 2.0% aluminum oxide (Al 2 o 3 ), 0.01% potassium fluoride (KF), 0.05% nano cerium tetrafluoride (CeF 4 ), the balance is aluminum fluoride (AlF 3 ).

[0042] The new CsF-RbF-AlF containing nano-rare earth fluoride obtained by the above ratio 3 Brazing flux, using propane as combustible gas for flame brazing, with Zn85-Al15 solder, Al88-Si12 solder, combined with 5052 aluminum alloy plate + Q235 steel plate, 6063 aluminum alloy plate + T2 red copper, according to GB / T 11363- 2008 "Brazed Joint Strength Test Method" was tested, and the shear strength of the brazed joint reached 130MPa-150MPa respectively.

Embodiment 3

[0044] CsF-RbF-AlF Containing Nanometer Rare Earth Fluoride 3 Flux, by mass percentage (wt.%), chemical composition is: 0.15% rubidium fluoride (RbF), 40.0% cesium fluoride (CsF), 1.0% aluminum oxide (Al 2 o 3 ), 0.5% potassium fluoride (KF), 0.02% nano cerium tetrafluoride (CeF 4 ), the balance is aluminum fluoride (AlF 3 ).

[0045]The new CsF-RbF-AlF containing nano-rare earth fluoride obtained by the above ratio 3 Brazing flux, using propane as combustible gas for flame brazing, with Zn85-Al15 solder, Al88-Si12 solder, combined with 5052 aluminum alloy plate + Q235 steel plate, 6063 aluminum alloy plate + T2 red copper, according to GB / T 11363- 2008 "Brazed Joint Strength Test Method" was tested, and the shear strength of brazed joints reached 130MPa-150MPa respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a CsF-RbF-AlF3 brazing flux containing nano rare-earth fluoride. The CsF-RbF-AlF3 brazing flux is characterized by comprising the following chemical components, by weight percent (wt.%), 0.02-0.2% of rubidium fluoride (RbF), 20.0-48.0% of cesium fluoride (CsF), 0.01-2.0% of aluminum oxide (Al2O3), 0.01-1.0% of potassium fluoride (KF), 0.001-0.05% of nano ceric fluoride (CeF4), and the balance aluminum fluoride (AlF3). The CsF-RbF-AlF3 brazing flux has higher activity than the existing brazing flux, and can meet the brazing requirements of aluminum-steel, aluminum-copper and aluminum-aluminum structures simultaneously.

Description

technical field [0001] The invention belongs to the field of brazing materials of non-metallic materials, in particular to a CsF-RbF-AlF containing nano-rare earth fluoride which can braze aluminum-steel, aluminum-copper and aluminum-aluminum 3 Flux. Background technique [0002] For the connection of dissimilar materials (that is, two different materials) such as aluminum-steel and aluminum-copper, brazing is more advantageous. During brazing, whether the brazing material can wet, spread and flow on the base metal is the primary problem of whether the "reliable connection" of the base metal can be realized, and the flux is to solve whether the brazing material can be on the base metal during brazing. Wetting, spreading, and flow are the key materials for reliable connection of the same or dissimilar materials. [0003] As we all know, the oxide on the surface of aluminum alloy is mainly Al 2 o 3 , MgO, MnO, CuO, SiO 2 etc., the oxides on the steel surface are mainly Fe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/363
CPCB23K35/3605B23K2103/10B23K2103/18
Inventor 陶纪明薛松柏姚震王健豪朱显明
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com