High-blackness graphite resin pencil and production process thereof

A high blackness, resin technology, applied in pencil lead, non-moving pencil, printing and other directions, can solve the problems of high resin content, poor physical properties, high cost of pencils, avoid pollution problems, moderate rolling hardness, Great looking effect

Inactive Publication Date: 2017-05-31
ZHEJIANG PENGSHENG STATIONERY CO LTD
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] One of the technical problems to be solved by the present invention is to provide a high-blackness graphite resin pencil and its production process that is environmentally friendly, smooth, with more uniform coloring of the refill, beautiful appearance, and smoother drawing, and its production process, which can replace traditional wooden pencils and solve the problem of Wooden pencils consume a large amount of wood resources, need paint spraying and coloring, etc., which are not energy-saving and environmentally friendly, and can solve the problems of high resin content and non-environmental protection used in resin composite pencils in the prior art and pencils made of degradable plastic raw materials Problems such as high cost and poor physical performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A graphite resin pencil with high blackness comprises a pen holder, a skin and a pen core, and the pen core comprises the following raw materials in parts by weight: 20 parts of polystyrene, 10 parts of SBS, 20 parts of graphite, 30 parts of modified talcum powder, 1 part of lubricating aid, 2 parts of rosin-based resin and 3 parts of modified polycarbonate.

[0036] The modification method of modified talcum powder is:

[0037] 1) Weigh 100 parts of the dried talcum powder material and put it into a temperature-controllable high mixer;

[0038] 2) Weigh 5 parts of modifier propylene glycol laurate and α, ω-bis(trimethylsiloxy) polydimethyl polymethyl (1-butane-polyoxyethylene polyoxypropylene ether) siloxane 3 copies;

[0039] 3) Add the weighed modifier evenly into the talcum powder in the high mixer, and stir for 15 minutes at a temperature of 200°C;

[0040] 4) Take out to obtain modified talcum powder.

[0041] The lubricating aid is ethylene bis stearamide.

...

Embodiment 2

[0053] A high-blackness graphite resin pencil, comprising a penholder, an epidermis and a pen core, the pen core comprising the following raw materials in parts by weight: 25 parts of polystyrene, 13 parts of SBS, 22 parts of graphite, 35 parts of modified talcum powder, 3 parts of lubricating aid, 2.5 parts of rosin-based resin and 4 parts of modified polycarbonate.

[0054] The modification method of modified talcum powder is:

[0055] 1) Weigh 100 parts of the dried talcum powder material and put it into a temperature-controllable high mixer;

[0056] 2) Weigh 5 parts of modifier propylene glycol laurate and α, ω-bis(trimethylsiloxy) polydimethyl polymethyl (1-butane-polyoxyethylene polyoxypropylene ether) siloxane 3 copies;

[0057] 3) Add the weighed modifier evenly into the talcum powder in the high mixer, and stir for 15 minutes at a temperature of 200°C;

[0058] 4) Take out to obtain modified talcum powder.

[0059] The lubricating aid is polyethylene glycol.

[...

Embodiment 3

[0071] A high-blackness graphite resin pencil, comprising a penholder, an epidermis and a pen core, the pen core comprising the following raw materials in parts by weight: 30 parts of polystyrene, 20 parts of SBS, 30 parts of graphite, 50 parts of modified talcum powder, 5 parts of lubricating aid, 3 parts of rosin-based resin and 6 parts of modified polycarbonate.

[0072] The modification method of modified talcum powder is:

[0073] 1) Weigh 100 parts of the dried talcum powder material and put it into a temperature-controllable high mixer;

[0074] 2) Weigh 5 parts of modifier propylene glycol laurate and α, ω-bis(trimethylsiloxy) polydimethyl polymethyl (1-butane-polyoxyethylene polyoxypropylene ether) siloxane 3 copies;

[0075] 3) Add the weighed modifier evenly into the talcum powder in the high mixer, and stir for 15 minutes at a temperature of 200°C;

[0076] 4) Take out to obtain modified talcum powder.

[0077] The lubricant aid is oleic acid amide.

[0078] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-blackness graphite resin pencil which comprises a penholder, a coat and a refill. The refill comprises, by weight, 20-30 parts of polystyrene, 10-20 parts of SBS (styrene butadiene styrene), 20-30 parts of graphite, 30-50 parts of modified talcum powder, 1-5 parts of a lubrication additive, 2-3 parts of rosin resin and 3-6 parts of modified polycarbonate. The high-blackness graphite resin pencil has the advantages that high-polymer materials are adopted, so that the pencil produced according to scientific and reliable formula has physical and mechanical properties and cutting properties of a wood pencil and is resistant to smashing and bending, lubricant in writing and appropriate in concentration and abrasion, and various forming processes can be performed on ordinary processing equipment.

Description

technical field [0001] The invention belongs to the field of pens, and relates to a plastic colored pencil, in particular to an environmentally friendly, smooth, high-blackness graphite resin pencil with more uniform coloring of the pen core, beautiful appearance, and smoother drawing, and a production process thereof. Background technique [0002] Pencil is a very widely used tool for writing and drawing. Its main structure is to form a strip lead embedded in the pen holder. The pen holder of a pencil is usually made of wood, and it is usually necessary to make a log into a pen holder in a shape such as a circle, a regular hexagon, or a regular octagon. Consume a lot of high-quality wood. At present, my country's annual output of wooden pencils is about 8 billion, which is equivalent to destroying 600 square kilometers of forest every year and consuming 400,000 cubic meters of high-quality wood. The consumption of a large amount of forest resources has seriously damaged th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D13/00B43K19/18
CPCB43K19/18C09D13/00
Inventor 栗广奉申剑裘慧国申国应
Owner ZHEJIANG PENGSHENG STATIONERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com