Ceramic simulating coating for inner wall decoration

Abstract

The invention discloses a ceramic simulating coating for inner wall decoration. The ceramic simulating coating is composed of the following components in parts by weight: 20-40 parts of urea-formaldehyde resin, 20-30 parts of cyclohexanone 10-20 parts of lithopone, 10-20 parts of epoxy resin, 2-3 parts of phenolic resin varnish, 0.01-0.03 part of tung oil, 3.5-7.5 parts of methyl acetate, 2.3-4.5 parts of cuprous oxide, 5-10 parts of magnesium chloride, 3-7 parts of methyl styrene, 10-15 parts of titanium dioxide, 35-45 parts of white latex, 2.5-4.6 parts of sodium hexametaphosphate, 0.1-0.3 part of calcium hexafluoroacetylacetonate, 1.5-3 parts of magnesium lithium silicate, 0.6-1 part of N,N-dimethylethanolamine, 1-2 parts of phenothiazine, 2.1-3 parts of 1,4-cyclohexanedimethanol, 2.4-3 parts of chromic oxide, 1-2 parts of benzotriazole and 1-3 parts of color paste. The ceramic simulating coating is ideal in performance, low in cost and simple in manufacturing process.

Description

technical field [0001] The invention relates to a building material, in particular to a porcelain-like paint for interior wall decoration. Background technique [0002] Porcelain-like paint is a new surface decoration protective paint developed in recent years. It has strong vitality as soon as it comes out. It is sprayed on the guardrail of the expressway, and its protective effect is better than all kinds of traditional paints. However, it also exposed some unsatisfactory problems such as weather resistance, UV resistance, coating moisture permeability, gas rate, etc., which caused the coating to bulge and bottom plate corrosion, and the surface layer faded and turned yellow; Due to the disadvantages of poor adhesion on the surface of some products, based on the above reasons, it is necessary to further improve it to meet the needs of surface decoration and protection of different materials on various occasions. . Contents of the invention [0003] The object of the p...

AI Technical Summary

Problems solved by technology

However, it also exposed some unsatisfactory problems such as weather resistance, UV resistance, coating moisture permeability, gas rate, etc., which caused the coating to bulge and bottom plate corrosion, and the surface layer faded and turned yellow; The surface of some products has disadvantages such as poor adhesion. Based on the above reasons, it is necessary to further improve it to meet the needs of surface decoration and protection of different materials on various occasions.