Aromatic polyamide fiber and rubber premix master batch

A technology of aromatic polyamide and rubber, which is applied in the field of aramid fiber rubber premix masterbatch, can solve the problems of high raw material cost, poor wear resistance and tear resistance, complex composition and preparation method, etc., and achieve Fewer drying steps, high grip, and increased stress at constant elongation

Active Publication Date: 2017-05-31
中蓝晨光化工有限公司
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the complex composition and preparation method of the aromatic polyamide fiber rubber premixed masterbatch in the prior art, the high raw material cost and the use of the premixed masterbatch composed of existing raw materials to make the final rubber product wear-resistant and anti-friction. To solve the problem of poor tearing performance, we provide an aromatic polyamide fiber rubber premix masterbatch, which is made of aromatic polyamide chopped fibers that are ground in water through high-speed beating and buckling. The aromatic polyamide pulp formed has simple raw materials and preparation methods, and can effectively improve the abrasion resistance and tear resistance of the final rubber product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aromatic polyamide fiber and rubber premix master batch
  • Aromatic polyamide fiber and rubber premix master batch
  • Aromatic polyamide fiber and rubber premix master batch

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A premixed masterbatch of aromatic polyamide fiber rubber, comprising the following raw materials: 20 parts of liquid rubber, 40 parts of aromatic polyamide fiber and 80 parts of dispersing solvent; Liquid rubber containing other solvent components, flowable at normal temperature, low viscosity, easy to mix, said liquid rubber includes polar liquid rubber and non-polar liquid rubber; said dispersing solvent is a low boiling point recyclable solvent;

[0028] In this embodiment, the aromatic polyamide fiber is aromatic polyamide pulp, and the aromatic polyamide pulp is obtained by grinding aromatic polyamide chopped fibers in water through a beater. The moisture content of the pulp is controlled at 50%.

[0029] In this embodiment, polar liquid rubber: liquid fluorine rubber is used.

[0030] In this embodiment, tetrahydrofuran is used as the dispersing solvent.

[0031]In this embodiment, the aromatic polyamide pulp is pulp with a fiber length of 0.5-1.5 mm, which is ...

Embodiment 2

[0033] A kind of aromatic polyamide fiber rubber premix master batch, comprises following raw material: 40 parts of liquid rubber, 70 parts of aromatic polyamide fiber and 110 parts of solvent;

[0034] Except that the above-mentioned raw material ratio is different from embodiment 1, the present embodiment also has the following differences from embodiment 1:

[0035] In this embodiment, the water content of the pulp is controlled to be 65%.

[0036] The polar liquid rubber used in this embodiment is liquid nitrile rubber; specifically, liquid nitrile rubber Nipol1312 is used. The dispersion solvent of the present embodiment adopts acetone;

Embodiment 3

[0038] A premixed masterbatch of aromatic polyamide fiber rubber, comprising the following raw materials: 50 parts of liquid rubber, 80 parts of aromatic polyamide fiber and 130 parts of dispersing solvent;

[0039] Except that the above-mentioned raw material ratio is different from embodiment 1, the present embodiment also has the following differences from embodiment 1:

[0040] In this embodiment, the moisture content of the pulp is 70%. The liquid rubber is non-polar liquid rubber, which is EPDM; specifically, Trilene 65 is used as a liquid EPDM; the dispersion solvent is 120# solvent oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
water contentaaaaaaaaaa
Login to View More

Abstract

The invention provides an aromatic polyamide fiber and rubber premix master batch. The master batch comprises 20-80 parts of liquid rubber, 20-80 parts of aromatic polyamide fibers and an appropriate amount of a dispersing solvent; and the weight of the dispersing solvent is 1-2 times the total weight of the liquid rubber and the aromatic polyamide fibers. The aromatic polyamide fibers comprise an aromatic polyamide pulp and an aromatic polyamide chopped fibers, and the aromatic polyamide pulp is obtained through breaking and grinding the aromatic polyamide chopped fibers in water through a beater. The aromatic polyamide fiber and rubber premix master batch selecting the aromatic polyamide pulp obtained through high-speed beating, breaking and grinding of the aromatic polyamide chopped fibers in water has the advantages of simple composition raw materials, simple preparation method, and effective improvement of the wear resistance and the tear resistance of finally obtained rubber products.

Description

technical field [0001] The invention belongs to the fields of high-performance macromolecule structural material manufacturing technology and rubber modification, and in particular relates to an aromatic polyamide fiber rubber premixed masterbatch. Background technique [0002] Aromatic polyamide chopped strands and pulp have always been concerned by the rubber industry for their excellent physical and chemical properties. After being added to the rubber matrix, the rubber masterbatch can improve the performance of the rubber, but its specific surface area is large and polar, and it is easy to generate static electricity. , which tends to cause the fibers to become tangled and difficult to disperse in the rubber matrix. The traditional method directly mixes aramid pulp and raw rubber. Aramid fiber is not easy to disperse evenly and the fiber itself is twisted into a ball, which ultimately leads to the failure to effectively improve the performance of the product. Therefore,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L27/12C08L9/02C08L23/16C08L9/06C08L9/00C08L11/00C08L23/22
CPCC08L9/00C08L23/22C08L27/12C08L77/06C08L2205/035C08L2205/16C08L9/02C08L23/16C08L9/06C08L11/00
Inventor 李兰英王凤德何鑫业林志娇
Owner 中蓝晨光化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com