Water-borne high permeability crystal waterproof hardening agent

A technology of high penetration and hardening agent, applied in the field of building materials, can solve the problems of limited waterproof engineering application and high price, and achieve the effect of strong water pressure resistance, deep penetration depth and high hardness

Inactive Publication Date: 2017-05-17
常州绿玛特建筑科技有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high price, its application in waterproofing engineering is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A water-based high-permeability crystalline waterproof hardener, comprising the following components by weight percentage:

[0031] Potassium silicate 40%, triethanolamine 0.3%, EDTA-2Na 5%, polyether modified polysiloxane 0.3%, silicoaluminophosphate 2.5%, polyacrylamide 2%, sodium methyl silicate 4.4%, water 45.5 %.

Embodiment 2

[0033] A water-based high-permeability crystalline waterproof hardener, comprising the following components by weight percentage:

[0034] Sodium silicate 40%, triethanolamine 0.5%, EDTA-2Na 2%, polyether modified polyorganosiloxane 0.5%, silicoaluminophosphate 2.5%, polyacrylamide 2%, potassium methyl silicate 8%, water 44.5%.

Embodiment 3

[0036] A water-based high-permeability crystalline waterproof hardener, comprising the following components by weight percentage:

[0037] Lithium silicate 30%, triethanolamine early strength agent 0.8%, EDTA-2Na 3%, polyether trisiloxane 0.5%, silicoaluminophosphate 4%, polyacrylamide 1%, sodium methyl silicate silicone 7% , 53.7% water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-borne high permeability crystal waterproof hardening agent. The proof hardening agent comprises the following components in percent by weight: 20 to 40 percent of alkali metal silicate, 0.25 to 1 percent of an early strength agent, 1 to 6 percent of a catalyst, 0 to 0.5 percent of a surfactant, 1 to 4 percent of a hardening accelerator, 0.5 to 2 percent of water soluble high molecular polymer, 0 to 8 percent of organic silicon, and water for the surplus. The waterproof hardening agent is moderate in cost, can realize complete localization, higher in penetration depth, higher in hardness after being reacted with substance in concrete, and higher in hydraulic pressure resistance capacity.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a water-based high-permeability crystalline waterproof hardener. Background technique [0002] Leakage is one of the common main diseases of concrete buildings. Leakage is very harmful to concrete buildings. One is that leakage will cause corrosion damage to concrete. The so-called dissolution refers to the leaching erosion of concrete by seepage water. As we all know, the hydration products of cement in concrete mainly include calcium silicate hydrate, calcium aluminate hydrate, calcium ferric aluminate hydrate and calcium hydroxide, and sufficient calcium hydroxide is the coagulation and crystallization of other hydration products. guarantee. Among the above hydration products, calcium hydroxide has a higher solubility in water. Under normal circumstances, saturated calcium hydroxide solution exists in the pores of concrete. Once leakage occurs, the seepage wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/68
CPCC04B41/68C04B41/5024C04B2111/27C04B41/5015C04B41/46C04B41/4961C04B41/4834C04B41/4927C04B41/4535
Inventor 杨建辉张菁燕王路艳叶云飞张凯华
Owner 常州绿玛特建筑科技有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com