A kind of elastin-like silk fiber porous composite material and its application

A porous composite material and elastin-like technology, which is applied in the field of biomedical materials, can solve the problems of small pore size, biological inertness and non-degradability, difficult plasticity to limit application, unfavorable in-growth of cells and tissues, etc., and achieve porosity. high effect

Active Publication Date: 2019-06-04
NORTHWEST UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, a variety of materials for bone and cartilage tissue engineering have emerged, such as electrospun polymer materials, which have the advantage of constructing micro or nano topological structures similar to extracellular matrix, but the material has a small pore size, which is not conducive to Cells enter the interior of the material thereby limiting tissue ingrowth
Secondly, there are hydrogel materials, which can facilitate the embedding of cells, but their biological inertness, non-degradability and difficulty in shaping limit its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of elastin-like silk fiber porous composite material and its application
  • A kind of elastin-like silk fiber porous composite material and its application
  • A kind of elastin-like silk fiber porous composite material and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment provides a preparation method of elastin-like silk fiber porous composite material, the specific steps are:

[0037] Cut B.mori cocoons into pieces and dry them, store them in a desiccator, use deionized water as a solvent, prepare 1.9M sodium carbonate solution, heat to 100°C, soak the dried cocoon pieces in boiling sodium carbonate solution After taking it out, it was ultrasonically cleaned 3 times with deionized water (10 minutes / time), dialyzed with deionized water to remove salt, and then dried to obtain silk fibers (or B.mori cocoons can also be cut into pieces and placed in deionized In deionized water, after boiling for 0.5 to 24 hours under the condition of higher than atmospheric pressure, the silk fibers are taken out and dried and stored);

[0038]10 mg of freeze-dried silk fibers were immersed in 1 mL of elastin-like protein solution with a mass concentration of 1% and freeze-dried to shape, which was designated as S-ELP. After that, S-ELP w...

Embodiment 2

[0040] This embodiment provides a preparation method of elastin-like silk fiber porous composite material, the specific steps are:

[0041] Cut B.mori cocoons into pieces and dry them, store them in a desiccator, use deionized water as solvent, prepare 1M hydrochloric acid solution, heat to 100°C, soak the dried cocoon pieces in boiling hydrochloric acid solution for 24 hours , after taking it out, use deionized water to ultrasonically clean it 3 times (10 minutes / time), use deionized water to dialyze and desalinate and then dry to obtain silk fiber;

[0042] Submerge 10 mg of freeze-dried silk fiber in 1 mL of elastin-like protein solution with a mass concentration of 0.01%, freeze-dry and form it, then immerse it in a genipin solution with a mass concentration of 0.01%, and react at 4°C for 48 hours to obtain a genipin cross-linked composite material (recorded as S-ELP-Genipin), washed with deionized water for 3 times, vacuum-dried, and sealed at 4°C.

Embodiment 3

[0044] This embodiment provides a preparation method of elastin-like silk fiber porous composite material, the specific steps are:

[0045] Cut B.mori silkworm cocoons into pieces and dry them, store them in a desiccator, use deionized water as solvent, prepare 0.01M sodium hydroxide solution, heat to 100°C, soak the dried silkworm cocoons in boiling hydroxide Sodium solution for 30 minutes, after taking it out, use deionized water to ultrasonically clean it 3 times (10 minutes / time), use deionized water to dialyze and desalinate and then dry to obtain silk fiber;

[0046] Submerge 10 mg of freeze-dried silk fiber in 1 mL of elastinoid solution (prepared with deionized water) with a mass concentration of 1% and lyophilize it, denoting it as S-ELP, and immerse the lyophilized S-ELP in 2% proanthocyanidin In the solution (prepared with deionized water), the proanthocyanidin cross-linked composite material (S-ELP-PA) was obtained after reacting at 37°C for 0.5 hours, washed with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an elastin-like silk fiber porous composite material. The raw materials for its preparation include elastin-like polypeptides and silkworm cocoons. The specific steps include: cutting the silkworm cocoons into pieces and degumming to obtain silk fibers; and combining the elastin-like polypeptides and silk fibers. Cross-linking produces the porous composite material. The composite material of the present invention is easy to process and shape, and the material properties are not affected after irradiation and sterilization with cobalt 60; and the composite material of the present invention has no adverse effects on surrounding tissues and can be integrated with the surrounding tissues; at the same time, the composite material of the present invention , its degradation rate matches the bone or cartilage regeneration rate, and can continuously and stably provide support for cell growth.

Description

technical field [0001] The invention relates to the field of biomedical materials, in particular to an elastin-like silk fiber porous composite material and its application in preparing bone and cartilage scaffold materials for tissue engineering. Background technique [0002] Tumor resection, trauma, and congenital malformations are the main causes of bone and cartilage defects clinically. At present, the gold standard for repairing bone and cartilage defects is autologous tissue transplantation, but autologous tissue transplantation will cause secondary trauma to patients, and the amount of materials obtained is limited. Therefore, the repair of bone and cartilage defects is still a difficult point in the medical field. Tissue engineering (tissue engineering, TE) technology provides an effective method for the repair of bone and cartilage tissue defects. The basic principle of TE is to obtain a small amount of cells (also known as seed cells) from the body, culture and ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K38/08A61L27/36A61L27/22A61L27/56A61L27/58
CPCA61L27/227A61L27/365A61L27/3654A61L27/56A61L27/58A61L2430/02A61L2430/06
Inventor 陈富林陈卓玥李红民谢鑫崔继红余源张婧
Owner NORTHWEST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com