Modified unsaturated polyester resin having excellent acid and alkali resistance, and preparation method thereof

A polyester resin, acid and alkali resistance technology, which is applied in the field of modified unsaturated polyester resin and its preparation, can solve the problem that the acid and alkali resistance of the unsaturated polyester resin cannot be satisfied.

Inactive Publication Date: 2017-04-26
滁州常源新材料有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The acid and alkali resistance of the unsaturated polyester resin used in the prior art cannot meet the needs of the actual production process, so it is urgent to design a modified unsaturated polyester resin with excellent acid and alkali resistance to solve the problem of the existing technology. problem in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of modified unsaturated polyester resin with excellent acid and alkali resistance proposed by the present invention, its raw materials include by weight: 10 parts of maleic anhydride, 10 parts of diethylene glycol, 3.5 parts of dicyclopentadiene, o-phthalic acid 4.5 parts of diformic anhydride, 3 parts of terephthalic acid, 7.5 parts of ethylene glycol, 10 parts of propylene glycol, 3.5 parts of rosin, 2.5 parts of trimethylol propane diallyl ether, 2 parts of hydroquinone, 4.5 parts of styrene , 3 parts of tetrahydrophthalic anhydride, 5 parts of castor oil, 3.5 parts of fumaric acid, 2.5 parts of cobalt isooctanoate, 1.0 parts of cobalt cyclopentanoate, 2 parts of methyl ethyl ketone peroxide, 5 parts of modified nano titanium dioxide, 5 parts of glass flakes, 3.5 parts of precipitated barium sulfate, 3.5 parts of methyltriethoxysilane, 4.5 parts of dimethyldiethoxysilane, 4.5 parts of diphenylsilanediol, 3.5 parts of phenyltriethoxysilane, 2 parts of zinc isooc...

Embodiment 2

[0024] A kind of modified unsaturated polyester resin with excellent acid and alkali resistance proposed by the present invention, its raw materials include by weight: 5 parts of maleic anhydride, 12 parts of diethylene glycol, 2 parts of dicyclopentadiene, o-phthalic acid 6 parts of diformic anhydride, 1 part of terephthalic acid, 9 parts of ethylene glycol, 7 parts of propylene glycol, 5 parts of rosin, 1 part of trimethylolpropane diallyl ether, 3 parts of hydroquinone, 3 parts of styrene 4 parts of tetrahydrophthalic anhydride, 4 parts of castor oil, 5 parts of fumaric acid, 1.5 parts of cobalt isooctanoate, 1.5 parts of cobalt cyclopentanoate, 1 part of methyl ethyl ketone peroxide, 6 parts of modified nano titanium dioxide, 4 parts of glass flakes, 5 parts of precipitated barium sulfate, 2 parts of methyltriethoxysilane, 6 parts of dimethyldiethoxysilane, 4 parts of diphenylsilanediol, 5 parts of phenyltriethoxysilane, 1 part of zinc isooctanoate share.

[0025] The mod...

Embodiment 3

[0033] A kind of modified unsaturated polyester resin with excellent acid and alkali resistance proposed by the present invention, its raw materials include by weight: 15 parts of maleic anhydride, 8 parts of diethylene glycol, 5 parts of dicyclopentadiene, o-phthalic acid 3 parts of diformic anhydride, 5 parts of terephthalic acid, 6 parts of ethylene glycol, 13 parts of propylene glycol, 2 parts of rosin, 4 parts of trimethylol propane diallyl ether, 1 part of hydroquinone, 6 parts of styrene 2 parts, 2 parts of tetrahydrophthalic anhydride, 6 parts of castor oil, 2 parts of fumaric acid, 3.5 parts of cobalt isooctanoate, 0.5 parts of cobalt cyclopentanoate, 3 parts of methyl ethyl ketone peroxide, 4 parts of modified nano titanium dioxide, 6 parts of glass flakes, 2 parts of precipitated barium sulfate, 5 parts of methyltriethoxysilane, 3 parts of dimethyldiethoxysilane, 5 parts of diphenylsilanediol, 2 parts of phenyltriethoxysilane, 3 parts of zinc isooctanoate share.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses modified unsaturated polyester resin having excellent acid and alkali resistance. The modified unsaturated polyester resin comprises the following raw materials: maleic anhydride, diethylene glycol, dicyclopentadiene, phthalic anhydride, terephthalic acid, ethylene glycol, propylene glycol, rosin, trimethylolpropane diallyl ether, hydroquinone, styrene, tetrahydrophthalic anhydride, castor oil, fumaric acid, an air-drying agent, cobalt iso-octoate, cobalt cyclopentanecarboxylate, methyl ethyl ketone peroxide, modified nanometer titania, glass flake, precipitated barium sulphate, methyl triethoxysilane, dimethyldiethoxysilane, diphenyl silanediol, phenyltriethoxysilane and zinc isoocatanoate. The invention further provides a preparation method of the modified unsaturated polyester resin having excellent acid and alkali resistance. The modified unsaturated polyester resin prepared by the invention has excellent acid and alkali resistance, good toughness and high hardness.

Description

technical field [0001] The invention belongs to the technical field of unsaturated polyester resins, and in particular relates to a modified unsaturated polyester resin with excellent acid and alkali resistance and a preparation method thereof. Background technique [0002] Unsaturated polyester is a kind of mature and industrialized thermosetting resin, and the corresponding products are widely used in laminates, building materials, adhesives, coatings, construction industry and electric power industry. Unsaturated polyester raw materials have wide sources and low cost. It can be cured and molded at room temperature, the curing time is controllable, and the molding process is simple. After curing, the surface of the product is bright and plump, with high hardness, good wear resistance, excellent electrical properties and weather resistance. [0003] The acid and alkali resistance of the unsaturated polyester resin used in the prior art cannot meet the needs of the actual ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/08C08L91/00C08K13/06C08K9/06C08K9/04C08K3/22C08K7/00C08K3/40C08K3/30C08K5/098C08K5/5419C08F283/01C08F212/08C08F232/08C08F222/02C08G63/676C08G63/91
CPCC08L51/08C08F283/01C08G63/676C08G63/91C08K2201/011C08K2201/014C08L2205/04C08F212/08C08L91/00C08K13/06C08K9/06C08K9/04C08K2003/2241C08K7/00C08K3/40C08K2003/3045C08K5/098C08K5/5419
Inventor 蔡国平
Owner 滁州常源新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com