Transparent polyester type polyurethane hot-melt adhesive composition

A technology of polyester polyurethane and hot melt adhesive, which is applied in the direction of polyurea/polyurethane adhesive, adhesive, adhesive type, etc., and can solve problems such as not mentioning the transparency of materials

Active Publication Date: 2017-04-19
上海理日化工新材料有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the document does not mention the transparency of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent polyester type polyurethane hot-melt adhesive composition
  • Transparent polyester type polyurethane hot-melt adhesive composition
  • Transparent polyester type polyurethane hot-melt adhesive composition

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] For the preparation method of the above-mentioned aliphatic-aromatic copolyester diol, please refer to CN104629663.

[0042] The aforementioned diisocyanates are aromatic diisocyanates or aliphatic / alicyclic diisocyanates or mixtures thereof. Specific examples include diphenylmethane diisocyanate (MDI), hydrogenated MDI, toluene diisocyanate (TDI), hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), naphthalene diisocyanate (NDI), benzene Dimethylene diisocyanate (XDI), hydrogenated XDI, p-phenylene diisocyanate (PPDI), etc., preferably MDI, HDI and IPDI.

[0043] Based on the total weight of the polyester polyurethane to be formed, the above-mentioned diisocyanate is added in an amount of 0.1-5% by weight, preferably 0.2-2% by weight.

[0044] The weight-average molecular weight of the polyol graft-modified styrene-maleic anhydride copolymer used in the present invention is generally 3000-30000, preferably 10000-25000. The content of the maleic anhydrid...

Embodiment

[0064] 1. Source of raw materials

[0065] The aliphatic-aromatic copolyester diol used in this example is self-made. The dimer acid was purchased from the British Croda Company, and the brand name was Pripol 1013. Styrene maleic anhydride copolymer is provided by Polyscope China Branch, the brand name is SZ 10010. The diisocyanates MDI, TDI, TDI and IPDI were purchased from BAYER Company in Germany. Polytetrahydrofuran ether glycol (PTMEG) was purchased from Sanxi Sanwei Company with a molecular weight of 2000. Polypropylene glycol (PPG) polycarbonate diol was purchased from Jiangsu Haian Petrochemical Plant with a molecular weight of 3000. Polycarbonate diol (PCD) was purchased from Ube, Japan, brand UH-CARB200, molecular weight 2000. All other raw materials were purchased from reagent companies.

[0066] 2. Performance test method

[0067] Each performance parameter is tested as follows in the embodiment:

[0068] (1) Melting point (Tm)

[0069] DSC method test, aft...

preparation example 1-1

[0088] Preparation Example 1-1 Copolyester Diol 1

[0089] Add 48 mol of 1,4-butanediol and 4 mol of neopentyl glycol into a 20L reaction kettle equipped with a thermometer, a mechanical stirrer, a fractionating column and a condenser, and raise the temperature to 100°C to completely melt the neopentyl glycol. Stirring was started, and 26 mol of terephthalic acid, 10 mol of isophthalic acid, 4 mol of dimer acid and 10 g of n-ethyl phthalate were added. Continue to raise the temperature. When the temperature rises to about 160°C, water droplets begin to distill. The distillation temperature is 98-105°C. Continue to raise the temperature until the temperature in the kettle reaches about 230°C. molecular weight oligomers. Reduce the stirring speed, slowly add 5 grams of n-ethyl phthalate and 4 grams of trimethyl phosphate, then continue to gradually increase the temperature to about 240-260 ° C, and gradually increase the vacuum degree of the system until the vacuum degree of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Melting pointaaaaaaaaaa
Melt viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a transparent polyester type polyurethane hot-melt adhesive composition. The composition comprises a) 90 to 99 wt% of polyester type polyurethane with a weight average molecular weight of 10, 000 to 200, 000 and b) 1 to 10 wt% of a polyol-grafted styrene-maleic anhydride copolymer, wherein the total weight of the polyester type polyurethane and the polyol-grafted styrene-maleic anhydride copolymer is taken as reference. The polyester type polyurethane hot-melt adhesive composition is to mold, and an adhesive film prepared from the composition is transparent, soft and water-resistant, has good whitening performance and is applicable to slide fasteners, clothes and textiles.

Description

[0001] 1. Technical field [0002] The invention relates to a polyester polyurethane hot-melt adhesive composition and its application, in particular to a low-melting-point polyester polyurethane hot-melt adhesive composition which is transparent, hot water resistant and whitening over time, and its application. [0003] 2. Background technology [0004] Polyester hot-melt adhesive has excellent washing and dry-cleaning resistance, and is widely used in the production of garment interlining (hot-melt interlining). In recent years, polyester hot-melt adhesives (films) have also been widely used for zipper patch adhesives. The following conditions need to be met for taking zipper patch glue: [0005] 1) The appearance of the film is transparent. In order to keep the color of the zipper patch from being covered, it is necessary to use polyester hot melt adhesive with better transparency and lower haze. [0006] 2) Lower melting temperature. In order to protect the clothes from...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J175/06C09J11/08C08G18/42C08G81/00
Inventor 祝爱兰
Owner 上海理日化工新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More