A kind of preparation method of high-grafting-rate polyolefin graft and application of the high-grafting-rate polyolefin graft

A technology of polyolefin grafts and high grafting rate, which is applied in the application of high grafting rate polyolefin grafts and the preparation field of high grafting rate polyolefin grafts, can solve the problem of high residual monomer content, High equipment requirements, low grafting rate and other problems, to achieve the effect of low residual monomer, long vacuuming time and low reaction temperature

Active Publication Date: 2019-04-05
ZHUZHOU TIMES NEW MATERIALS TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the preparation of polyolefin grafts is mainly through melt extrusion. During the preparation of polyolefin grafts by melt extrusion, the molecular chains are easily broken, and the macromolecules are easily cross-linked. The cross-linking reaction makes the product gel High content, it is also easy to cause crystal points in the application of multi-layer composite films, resulting in film rupture
In addition, the polyolefin graft prepared by the melt extrusion method has dark color, heavy taste, and high residual monomer content, making it impossible to be used in food packaging films
In the application of compatibilizer and toughening agent, the polyolefin graft prepared by melt extrusion reaction method has a low graft rate, and often needs to add a large amount of graft to achieve the toughening effect or compatibilization purpose. In addition, The crosslinking reaction of the melt grafting method will easily cause the viscosity of the system to increase, the rheological properties will deteriorate, and the processability will be poor, which is not conducive to the application of toughening modification and compatibility modification
In addition, the preparation of polyolefin grafts by melt extrusion requires high equipment requirements, such as corrosion resistance of the extruder, large aspect ratio, high vacuum, complex design and high price.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high-grafting-rate polyolefin graft and application of the high-grafting-rate polyolefin graft
  • A kind of preparation method of high-grafting-rate polyolefin graft and application of the high-grafting-rate polyolefin graft

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of preparation method of high grafting rate polyolefin graft of the present invention comprises the following steps:

[0030] (1) Vacuum the reactor first, then fill the reactor with nitrogen to replace all the air in the reactor with nitrogen, and heat the reactor to 150°C;

[0031] (2) under the protection of nitrogen, 1980g polyethylene is added in the reactor, after the polyethylene melts, add 20g maleic anhydride, 2g triphenyl phosphite and 2g dicumyl peroxide, stir and react for 30min;

[0032] (3) Then vacuumize the reactor to -0.09MPa to continue the reaction for 30 minutes, and finally extrude the reaction material under high pressure and cut it into pellets to obtain the polyolefin graft.

Embodiment 2

[0038] A kind of preparation method of high grafting rate polyolefin graft of the present invention comprises the following steps:

[0039] (1) Vacuum the reactor first, then fill with nitrogen to replace all the air in the reactor with nitrogen, and heat the reactor to 80°C;

[0040] (2) Under the protection of nitrogen, add 1900g ethylene-octene copolymer to the reactor, after the ethylene-octene copolymer melts, add 100g maleic anhydride, 60g triphenyl phosphite and 15g diphenyl peroxide Acyl, stirred and reacted for 360min;

[0041] (3) Then vacuumize the reactor to -0.09MPa to continue the reaction for 60 minutes, and finally extrude the material obtained from the reaction under high pressure, and pelletize the strands to obtain the polyolefin graft.

Embodiment 3

[0047] A kind of preparation method of high grafting rate polyolefin graft of the present invention comprises the following steps:

[0048] (1) Vacuum the reactor first, then fill the reactor with nitrogen to replace all the air in the reactor with nitrogen, and heat the reactor to 180°C;

[0049] (2) 1960g polypropylene is added in the reactor under the protection of nitrogen, after the polypropylene is melted, add 40g maleic anhydride, 4g triphenyl phosphite and 4g dibenzoyl peroxide, stir and react for 5min;

[0050] (3) Then vacuumize the reactor to -0.09MPa to continue the reaction for 30 minutes, and finally extrude the reaction material under high pressure and cut it into pellets to obtain the polyolefin graft.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
Login to View More

Abstract

A preparing method of a polyolefin graft having a high grafting ratio is disclosed. The method includes (1) replacing air in a reaction kettle with nitrogen, and then heating the reaction kettle to 80-180 DEG C, (2) adding a polyolefin under nitrogen protection to the reaction kettle, adding a reaction monomer, an initiator and a crosslinking inhibiting agent after the polyolefin is melted, and reacting the mixture under stirring, and (3) vacuumizing the reaction kettle, then proceeding with the reaction, and subjecting a material prepared by the reaction to high-pressure extrusion, strip drawing and pelletizing to obtain the polyolefin graft. The polyolefin graft prepared by the method has advantages of the high grafting ratio, a low crosslinking degree, weak smell, light color, a low monomer residual amount, high adhesive force, and the like, wherein the grafting ratio of maleic anhydride can reach 4.89%, the monomer residual amount is 0.05% or below, and the adhesive strength can reach 30 N / 15mm.

Description

technical field [0001] The invention relates to a preparation method of a polyolefin graft, in particular to a preparation method of a high grafting rate polyolefin graft and the application of the high grafting rate polyolefin graft. Background technique [0002] Multi-layer composite film is a film that combines different materials together through multi-layer co-extrusion technology, has the advantages of different materials, and has some special functions; multi-layer composite film is generally composed of a base layer, an adhesive layer and a functional layer. Composition, wherein the function of the bonding layer is to improve the compatibility between the base layer and the functional layer, and the bonding layer is mainly a polyolefin graft. [0003] In the application of engineering plastics, due to the polarity difference between different polymers and between polymers and fillers, it is necessary to add a compatibilizer during the modification or alloying process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F255/02C08F222/06C08F220/06C08L77/02C08L51/06
CPCC08F255/02C08L77/02C08L2203/16C08F222/06C08F220/06C08L51/06
Inventor 汤鑫焱胡天辉刘玉峰邓凯桓姜其斌
Owner ZHUZHOU TIMES NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products