Environment-friendly plastic-wood composite tray and preparation method thereof

A plastic-wood and pallet technology, applied in the field of environmental-friendly plastic-wood composite pallets and their preparation, can solve the problems of poor toughness, low strength, restricting the scope of use, etc., and achieve the effects of light weight, low cost and various colors

Inactive Publication Date: 2017-01-04
民勤县威瑞环保有限责任公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of its preparation materials, wood-plastic composites have low strength and poor toughness, which obviously restricts its application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An environmentally friendly plastic-wood composite tray, comprising the following raw materials in parts by weight: 15 parts of modified bamboo powder, 5 parts of carbon fiber, 85 parts of waste polyethylene particles, 0.6 part of benzoin butyl ether, N,N-methylenebisacrylamide 3 parts, 2 parts of silicone oil, 0.5 parts of polyethylene wax, 0.5 parts of calcium stearate, 4 parts of nano-diatomaceous earth, 1 part of zinc oxide, 1 part of epoxy soybean oil, 1 part of iron oxide red, 0.2 parts of glycerin.

[0017] The preparation method of the environment-friendly plastic-wood composite pallet includes the following steps:

[0018] (1) Immerse the bamboo powder in 0.4mol / L sodium hydroxide solution, treat it at 95°C for 45 minutes, take out the bamboo powder and then dry it at 105°C. After drying, the bamboo powder and succinic anhydride After mixing at a mass ratio of 1:1, add it to N,N-dimethylformamide for acylation reaction, react at 80°C for 1 hour, and dry the bam...

Embodiment 2

[0022] An environmentally friendly plastic-wood composite tray, comprising the following raw materials in parts by weight: 15-35 parts of modified bamboo powder, 8 parts of carbon fiber, 95 parts of waste polyethylene particles, 1 part of benzoin butyl ether, N,N-methylene bis 4 parts of acrylamide, 5 parts of silicone oil, 2 parts of polyethylene wax, 1.5 parts of calcium stearate, 6 parts of nano diatomaceous earth, 2 parts of zinc oxide, 2 parts of epoxy soybean oil, 2 parts of phthalocyanine green, 0.8 parts of glycerin .

[0023] The preparation method of the environment-friendly plastic-wood composite pallet includes the following steps:

[0024] ⑴Immerse the bamboo powder in 0.6mol / L sodium hydroxide solution, treat it at 100°C for 100 minutes, take out the bamboo powder and then dry it at 110°C. After drying, the bamboo powder and succinic anhydride After mixing at a mass ratio of 1:1, add it to N,N-dimethylformamide for acylation reaction, react at 100°C for 2 hours,...

Embodiment 3

[0028] An environmentally friendly plastic-wood composite tray, including the following raw materials in parts by weight: 25 parts of modified bamboo powder, 6.5 parts of carbon fiber, 90 parts of waste polyethylene particles, 0.8 part of benzoin butyl ether, N,N-methylenebisacrylamide 3.5 parts, 3.5 parts of silicone oil, 1.5 parts of polyethylene wax, 1 part of calcium stearate, 5 parts of nano-diatomaceous earth, 1.5 parts of zinc oxide, 1.5 parts of epoxy soybean oil, 1.5 parts of phthalocyanine blue, and 0.5 parts of glycerin.

[0029] The preparation method of the environment-friendly plastic-wood composite pallet includes the following steps:

[0030] (1) Immerse the bamboo powder in 0.5mol / L sodium hydroxide solution, treat it at 100°C for 75 minutes, take out the bamboo powder and then dry it at 110°C. After drying, the bamboo powder and succinic anhydride After mixing in a mass ratio of 1:1, add it to N,N-dimethylformamide for acylation reaction, react at 90°C for 1....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly plastic-wood composite tray and a preparation method thereof and belongs to the field of plastic-wood composites. The tray is prepared from raw materials in parts by weight as follows: 15-35 parts of modified bamboo sawdust, 5-8 parts of carbon fibers, 85-95 parts of waste polyethylene particles, 0.6-1 part of benzoin butyl ether, 3-4 parts of N,N-methylene bisacrylamide, 2-5 parts of silicone oil, 0.5-2 parts of polyethylene wax, 0.5-1.5 parts of calcium stearate, 4-6 parts of nano diatomaceous earth, 1-2 parts of zinc oxide, 1-2 parts of epoxidized soybean oil, 1-2 parts of color masterbatch and 0.2-0.8 parts of glycerin. The bamboo sawdust and the waste polyethylene particles are modified in sequence, other aids are added, and the plastic-wood composite tray which is low in cost, light in mass, smooth and bright in surface and colorful is prepared rapidly; the energy-saving and environment-friendly effects are realized while resources are saved.

Description

technical field [0001] The invention belongs to the field of plastic-wood composite materials, in particular to an environment-friendly plastic-wood composite tray and a preparation method thereof. Background technique [0002] Wood-plastic composite material is a new composite material with high performance and high added value, which is made of wood fiber as raw material and plastic through compatibilization and blending process. At present, the plastic matrix in the wood-plastic processing industry generally uses high-density polyethylene, polypropylene, polystyrene, polyvinyl chloride, etc. with relatively low melting points. Natural plant fibers with high aspect ratio, such as wood flour, bagasse, rice husk powder, cotton straw, flax. [0003] The promotion and application of wood-plastic composite materials can also solve the problem of environmental pollution caused by waste plastics that cannot be recycled, and make full use of fiber waste resources, which has certa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L97/02C08L83/04C08L91/00C08K13/04C08K7/06C08K5/098C08K3/34C08K3/22C08H7/00C08J3/28
CPCC08L23/06C08H6/00C08J3/28C08J2323/06C08K2201/011C08L2205/025C08L2205/035C08L2205/16C08L97/02C08L83/04C08L91/00C08K13/04C08K7/06C08K5/098C08K3/34C08K2003/2296
Inventor 许开强
Owner 民勤县威瑞环保有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap