Preparation method of dye sensitization solar battery slurry

A technology for solar cells and dye sensitization, which is applied in the field of preparation of dye-sensitized solar cell paste, can solve problems such as poor mechanical properties, and achieve the effects of low manufacturing cost, good film-forming properties, and strong adhesion

Inactive Publication Date: 2016-11-23
陆鹏
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there is rarely a method that can fully and uniformly prepare carbon nanotubes and titanium dioxide into a composite slurry. The titanium dioxide slurry compounded with carbon nanotubes overcomes the conductivity and poor mechanical properties of electrodes prepared with a single component of titanium dioxide. Disadvantages, expand the application range of titanium dioxide to improve the field of emerging energy materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of a dye-sensitized solar cell paste, comprising the following steps:

[0026] (1) Preparation of titanium dioxide powder: Weigh 10 parts of butyl titanate and dissolve it in 100 parts of absolute ethanol, add 0.1 part of acetylacetone and 5 parts of water during stirring, let stand at 15°C for 48 hours, then vacuum at 60°C Dried to obtain white titanium dioxide powder;

[0027] (2) Preparation of slurry: Weigh 1 part of carbon nanotubes and put them in 100 parts of water, add 5 parts of titanium dioxide powder obtained in step (1), ultrasonically disperse, then add 50 parts of ethanol, stir, and prepare a slurry;

[0028] (3) Curing slurry: Add 10 parts of polyethylene glycol to the slurry prepared in step (2), stir, then add 10 parts of methyl cellulose, and stir to obtain a solidified slurry;

[0029] (4) Concentrated slurry: the solidified slurry obtained in step (3) was evaporated by a rotary evaporator to obtain concentrated dye-sensitized so...

Embodiment 2

[0032] A preparation method of a dye-sensitized solar cell paste, comprising the following steps:

[0033] (1) Preparation of titanium dioxide powder: Weigh 50 parts of titanyl sulfate and dissolve in 200 parts of absolute ethanol, add 2 parts of acetylacetone and 1 part of water while stirring, let stand at 25°C for 24 hours, then dry in vacuum at 60°C , to obtain white titanium dioxide powder;

[0034] (2) Preparation of slurry: Weigh 10 parts of carbon nanotubes and put them in 50 parts of water, add 20 parts of titanium dioxide powder obtained in step (1), ultrasonically disperse, then add 100 parts of ethanol, stir, and prepare a slurry;

[0035] (3) Curing slurry: Add 5 parts of terpineol to the slurry prepared in step (2), stir, then add 20 parts of hydroxypropyl methylcellulose, and stir to obtain a solidified slurry;

[0036] (4) Concentrated slurry: distilling the solidified slurry obtained in step (3) through a distillation tower to obtain concentrated dye-sensitiz...

Embodiment 3

[0039] A preparation method of a dye-sensitized solar cell paste, comprising the following steps:

[0040] (1) Preparation of titanium dioxide powder: Weigh 35 parts of butyl titanate and dissolve in 150 parts of absolute ethanol, add 1 part of acetylacetone and 3 parts of water during stirring, let stand at 25°C for 24 hours, then vacuum at 80°C Dried to obtain white titanium dioxide powder;

[0041] (2) Preparation of slurry: Weigh 6 parts of carbon nanotubes and put them in 80 parts of water, add 10 parts of titanium dioxide powder obtained in step (1), ultrasonically disperse, then add 80 parts of isopropanol, stir, and prepare a slurry;

[0042] (3) Curing slurry: Add 8 parts of polyethylene glycol to the slurry prepared in step (2), stir, then add 15 parts of methyl cellulose, stir to obtain a solidified slurry;

[0043] (4) Concentrated slurry: the solidified slurry obtained in step (3) was evaporated by a rotary evaporator to obtain concentrated dye-sensitized solar c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to photoelectric cell electrode materials, and discloses a preparation method of dye-sensitized solar cell paste. It consists of the following steps: (1) preparing titanium dioxide powder, (2) preparing slurry, (3) curing the slurry and (4) concentrating the slurry; the dye-sensitized solar cell slurry obtained by the method has good film-forming property, The dispersion of particles in the slurry is good, the film layer does not crack after sintering, and the film has strong adhesion to the substrate after sintering; the method has low manufacturing cost, green and environmentally friendly manufacturing process, and the obtained composite film has excellent conductivity, which provides a solid foundation for large-scale industrial production. Easy way.

Description

technical field [0001] The invention relates to photoelectric cell electrode materials, in particular to a preparation method of dye-sensitized solar cell slurry. Background technique [0002] With the development of industry and the increase of human activities, human consumption of energy is increasing day by day, while underground non-renewable mineral energy is becoming increasingly scarce, and the contradiction between energy supply and demand is increasingly intensified. Energy issues have become one of the key issues affecting human survival and development. . Not only that, but the greenhouse gases produced by the burning of fossil energy accelerate the pace of global warming and cause various natural disasters to occur frequently. Therefore, the development and utilization of new, environmentally friendly and renewable energy sources is an urgent task. Solar cells can directly convert light energy into electrical energy, which is a way to effectively utilize solar ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G9/20H01G9/042
CPCY02E10/542H01G9/2031
Inventor 陆鹏
Owner 陆鹏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com