Tire tread rubber with low rolling resistance

A tire tread and rolling resistance technology, which is applied in the field of low rolling resistance tire tread compound and tire compound formula, can solve the problem of reducing the rolling resistance of finished tires, the low rolling resistance performance is not significantly improved, and the impact on the wear resistance of the tire tread Performance and other issues, to achieve the effect of reducing rolling resistance

Inactive Publication Date: 2016-11-16
SICHUAN YUANXING RUBBER
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims to solve the problem in the prior art that the low rolling resistance performance of low rolling resistance tires is not significantly improved and will affect the wear resistance of the tire tread, and provides a low rolling resistance tire tread compound that can greatly Reduce the rolling resistance of the finished tire during use without affecting the wear resistance of the tire tread

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A low-rolling-resistance tire tread compound comprises the following raw materials in parts by weight:

[0046] 2 parts natural rubber

[0047] SBR 3 points

[0048] 0.1 parts of phenolic resin

[0049] 1 part epoxy resin

[0050] 2 parts stearic acid

[0051] 2 parts wax

[0052] Anti-aging agent 1 part

[0053] Carbon black N330 21 parts

[0054] White carbon black 2 parts

[0055] Sulfur 0.5 parts

[0056] Accelerator 1.5 parts

[0057] Aromatic oil 15 parts

[0058] Hard clay 4 parts.

Embodiment 2

[0060] A low-rolling-resistance tire tread compound comprises the following raw materials in parts by weight:

[0061] 5 parts natural rubber

[0062] SBR 6 points

[0063] 0.5 parts of phenolic resin

[0064] 2 parts epoxy resin

[0065] 4 parts stearic acid

[0066] 4 parts wax

[0067] Anti-aging agent 3 parts

[0068] Carbon black N330 35 parts

[0069] White carbon black 7 parts

[0070] 1 part sulfur

[0071] Accelerator 2.5 parts

[0072] Aromatic oil 35 parts

[0073] Hard clay 15 parts.

Embodiment 3

[0075] A low-rolling-resistance tire tread compound comprises the following raw materials in parts by weight:

[0076] 3.5 parts of natural rubber

[0077] SBR 4.5 points

[0078] 0.3 parts of phenolic resin

[0079] 1.5 parts of epoxy resin

[0080] 3 parts stearic acid

[0081] 3 parts wax

[0082] Anti-aging agent 2 parts

[0083] Carbon black N330 28 parts

[0084] White carbon black 4.5 parts

[0085] Sulfur 0.75 parts

[0086] Accelerator 2 parts

[0087] Aromatic oil 25 parts

[0088] Hard clay 9.5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to tire tread rubber with low rolling resistance, belonging to the technical field of a tire rubber formula. The tire tread rubber comprises 2-5 parts of natural rubber, 3-6 parts of styrene-butadiene rubber, 0.1-0.5 part of phenolic resin, 1-2 parts of epoxy resin, 2-4 parts of stearic acid, 2-4 parts of wax, 1-3 parts of an anti-aging agent, 21-35 parts of carbon black N330, 2-7 parts of white carbon black, 0.5-1 part of sulfur, 1.5-2.5 parts of an accelerating agent, 15-35 parts of aromatic oil and 4-15 parts of hard clay. By virtue of reasonable formula combination, the proportion of carbon black in the system is reduced, the rolling resistance of a finished product of a tire in use can be greatly reduced, and the wear resistance of the tire tread can not be influenced.

Description

technical field [0001] The invention relates to a tire compound, more specifically, the invention relates to a low rolling resistance tire tread compound, which belongs to the technical field of tire compound formula. Background technique [0002] Tires are circular elastic rubber products that are rolled on the ground and rolled on various vehicles or machinery. Usually installed on the metal hub, it can support the body, buffer the external impact, realize the contact with the road surface and ensure the driving performance of the vehicle. Tires are often used under complex and harsh conditions, and they are subjected to various deformations, loads, forces, and high and low temperature effects during driving, so they must have high load-bearing performance, traction performance, and cushioning performance. At the same time, it is also required to have high wear resistance and flex resistance, as well as low rolling resistance and heat generation. Half of the world's rubb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/00C08L7/00C08L9/06C08L61/06C08L63/00C08L91/06C08K13/02C08K5/09C08K3/04C08K3/36C08K3/06B60C1/00
CPCB60C1/0016C08L91/00C08L2205/02C08L2205/035C08L7/00C08L9/06C08L61/06C08L63/00C08L91/06C08K13/02C08K5/09C08K3/04C08K3/36C08K3/06C08K3/346Y02T10/86
Inventor 刘先春
Owner SICHUAN YUANXING RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com