Corrosion-resistant metal coating and preparation method thereof

A metal coating and corrosion-resistant technology, applied in coatings, anti-corrosion coatings, etc., can solve problems such as coating corrosion, and achieve the effect of improving corrosion resistance and excellent corrosion resistance

Inactive Publication Date: 2016-10-26
WUXI EPIC TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating is easily corroded by sodium chloride, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Corrosion-resistant metal coating, including the following raw materials in parts by weight: 40 parts of nano-zinc oxide, 30 parts of manganese dioxide, 55 parts of cerium oxide, 60 parts of castor oil polyoxyethylene ether, 15 parts of aluminum, 25 parts of copper, methyl 80 parts of 2-hydroxyethyl acrylate, 30 parts of 2-vinylpyrrolidine, and 25 parts of sorbic acid.

[0016] The preparation method of the above-mentioned corrosion-resistant metal coating comprises the following steps: mixing nano-zinc oxide, manganese dioxide, cerium oxide, aluminum, copper, 2-hydroxyethyl methacrylate, 2-vinylpyrrolidine, and sorbic acid in 40 Heating at ~60°C for 20-30 hours, then adding castor oil polyoxyethylene ether, mixing evenly to obtain a mixture, uniformly coating the mixture on the metal base, and drying it.

Embodiment 2

[0018] Corrosion-resistant metal coating, including the following raw materials in parts by weight: 10 parts of nano-zinc oxide, 10 parts of manganese dioxide, 50 parts of cerium oxide, 40 parts of castor oil polyoxyethylene ether, 10 parts of aluminum, 20 parts of copper, methyl 20 parts of 2-hydroxyethyl acrylate, 10 parts of 2-vinylpyrrolidine, and 20 parts of sorbic acid.

[0019] The preparation method of the above-mentioned corrosion-resistant metal coating comprises the following steps: mixing nano-zinc oxide, manganese dioxide, cerium oxide, aluminum, copper, 2-hydroxyethyl methacrylate, 2-vinylpyrrolidine, and sorbic acid in 40 Heat at ~60°C for 20 to 30 hours, then add castor oil polyoxyethylene ether, mix evenly to obtain a mixture, coat the mixture evenly on the metal substrate, and dry it.

Embodiment 3

[0021] Corrosion-resistant metal coating, including the following raw materials in parts by weight: 50 parts of nano-zinc oxide, 50 parts of manganese dioxide, 60 parts of cerium oxide, 80 parts of castor oil polyoxyethylene ether, 20 parts of aluminum, 30 parts of copper, methyl 100 parts of 2-hydroxyethyl acrylate, 50 parts of 2-vinylpyrrolidine, and 30 parts of sorbic acid.

[0022] The preparation method of the above-mentioned corrosion-resistant metal coating comprises the following steps: adding nano-zinc oxide, manganese dioxide, cerium oxide, aluminum, copper, 2-hydroxyethyl methacrylate, 2-vinylpyrrolidine, and sorbic acid in 40 Heat at ~60°C for 20 to 30 hours, then add castor oil polyoxyethylene ether, mix evenly to obtain a mixture, coat the mixture evenly on the metal substrate, and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a corrosion-resistant metal coating and a preparation method thereof. The corrosion-resistant metal coating comprises raw materials in parts by weight as follows: 10-50 parts of nano-zinc oxide, 10-50 parts of manganese dioxide, 50-60 parts of cerium oxide, 40-80 parts of castor oil polyoxyethylene ether, 10-20 parts of aluminum, 20-30 parts of copper, 20-100 parts of 2-hydroxyethyl methacrylate, 10-50 parts of 2-ethylene pyrrolidine and 20-30 parts of sorbic acid. The preparation method of the corrosion-resistant metal coating comprises the steps as follows: nano-zinc oxide, manganese dioxide, cerium oxide, aluminum, copper, 2-hydroxyethyl methacrylate, 2-ethylene pyrrolidine and sorbic acid are heated for 20-30 h at the temperature of 40-60 DEG C, then castor oil polyoxyethylene ether is added, the materials are mixed uniformly, a mixture is obtained, a metallic matrix is uniformly coated with the mixture and is dried, and the corrosion-resistant metal coating is obtained. The corrosion-resistant metal coating has excellent corrosion resistance.

Description

technical field [0001] The invention relates to a corrosion-resistant metal coating and a preparation method thereof. Background technique [0002] Coating is a solid continuous film obtained by one application of paint. It is a thin plastic layer coated on metal, fabric, plastic and other substrates for the purpose of protection, insulation and decoration. The paint can be gaseous, liquid, or solid, and the type and state of the paint are usually determined according to the substrate to be sprayed. Metal coating refers to: the covering layer prepared by thermal spraying method using metal as spraying material. [0003] The Chinese patent application with the application number CN200910219750.7 discloses a magnesium-aluminum dissimilar metal coating and its preparation method, using arc spraying, plasma spraying or supersonic flame spraying, and magnesium with a diameter ratio of 1:1 to 1:3 Wire and aluminum wire are used as two electrodes for arc spraying, or magnesium ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/10C09D7/12
CPCC09D4/06C09D5/10C09D5/103C09D7/61C09D7/63
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More