Bamboo-plastic foamed composite door/window material making full use of resources and preparation method thereof

A bamboo-plastic and resource technology, applied in the field of bamboo-plastic foamed composite door and window materials and their preparation, can solve the problems of restricting the application of bamboo-plastic foaming composite materials, the mechanical strength needs to be improved, and the functionalization of composite materials is not perfect, and achieves excellent performance. Formaldehyde adsorption efficiency, increasing formaldehyde adsorption efficiency, improving affinity and fluidity

Inactive Publication Date: 2016-10-12
安徽三乐节能科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In "The Effect of Titanate Coupling Agent on the Properties of Bamboo-plastic Foamed Composite Materials", Zhou Xingxing prepared a bamboo-plastic foamed composite material by using bamboo powder, polypropylene, and high-melt strength polypropylene, but its The mechanical strength needs to be improved, and the functionalization of the composite material is not perfect enough, which limits the application of bamboo-plastic foam composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] A bamboo-plastic foamed composite door and window material that fully utilizes resources is characterized in that it is made of the following raw materials in parts by weight:

[0017] Rice straw powder 2, isotactic polypropylene 70, straw powder 3, high melt strength polypropylene 15, bamboo powder 40, activated carbon 15, diatomaceous earth 2, corundum powder 2, Cu(NO 3 ) 2 25, stearic acid 2, calcium stearate 3, foaming agent AC1601 3, zinc stearate 15, NaOH solution 60, polyacrylate emulsion 3;

[0018] The particle diameter of described bamboo powder is 90-350 μ m, and NaOH solution concentration is 1mol / L, and Cu(NO 3 ) 2 The concentration is 0.1 mol / L, and the solid content of the polyacrylate emulsion is 40-50%.

[0019] A kind of preparation method of described bamboo-plastic foamed composite door and window material fully utilizing resource is characterized in that, is made by the following steps:

[0020] a. Add activated carbon and corundum powder to Na...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bamboo-plastic foamed composite door / window material making full use of resources and a preparation method thereof. The material is characterized by being made from the following raw materials according to parts by weight: 1-2 parts of rice straw powder, 60-70 parts of isotactic polypropylene, 1-3 parts of straw powder, 10-15 parts of high-melt-strength polypropylene, 30-40 parts of bamboo powder, 10-15 parts of activated carbon, 1-2 parts of diatomite, 1-2 parts of corundum powder, 20-25 parts of Cu(NO3)2, 1-3 parts of stearic acid, 1-3 parts of calcium stearate, 1-3 parts of foaming agent AC1601, 10-15 parts of zinc stearate, 50-60 parts of NaOH solution, and 1-3 parts of polyacrylate emulsion; the activated carbon and diamond are modified with polyacrylate and Cu(NO3)2, promoting loading of Cu(NO3)2 on the surface of and in ducts of the activated carbon and diamond, and increasing its adhesion; the addition of rice straw powder and straw powder and the like promotes full use of resources and reduces cost.

Description

technical field [0001] The invention relates to a bamboo-plastic composite material, in particular to a bamboo-plastic foam composite door and window material which fully utilizes resources and a preparation method thereof. Background technique [0002] Bamboo-plastic foam composites have attracted much attention recently because they can overcome the defects of high density and brittleness of bamboo-plastic composites. Bamboo-plastic composite materials mainly include polyvinyl chloride and polyolefin plastics. Polyvinyl chloride-based composite materials will pollute the environment during manufacture, use and disposal. Polyvinyl chloride-based composite materials have low rigidity and maximum service temperature, and are not easy to degrade. Therefore, polypropylene (PP) wood-plastic foam composites have become a recent research hotspot. Bamboo-plastic foam composite materials have a wide range of applications, involving the automobile industry and transportation indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L97/02C08L33/08C08K13/06C08K9/02C08K9/04C08K3/04C08K5/098C08J9/10
CPCC08L23/12C08J9/103C08J2203/04C08J2323/12C08J2423/12C08J2497/02C08K2201/014C08L2203/14C08L2205/025C08L2205/035C08L2205/16
Inventor 陈学军吴珍梅徐琼琼曹蕾沈中
Owner 安徽三乐节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products