Titanium oxide soluble electrode and preparation method thereof, and application of titanium oxide soluble electrode in preparation of high-purity titanium by means of molten salt electrolysis

A titanium oxide and electrode technology, applied in the preparation of high-purity titanium by molten salt electrolysis, titanium oxide soluble electrode and its preparation field, can solve high-purity titanium pollution, complex process, no titanium oxide block Body and other issues

Active Publication Date: 2016-09-21
成都锦钛精工科技有限公司
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has the following problems: (1) TiC X o y N z etc. as a soluble anode, the C and N elements in it will have certain pollution to the prepared high-purity titanium
(2) The preparation process of its anode still depends on high-temperature reduction conditions (up to 2000°C), and in addition, the anode preparation takes a long time (up to 600min), which cannot substantially reduce production costs
Moreover, most of the existing methods are titanium dioxide powders. To prepare blocks, titanium dioxide powders need to be sintered into blocks to prepare titanium dioxide powders. The process is complicated and takes a long time.
At present, there is no relevant research on the direct preparation of titania blocks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium oxide soluble electrode and preparation method thereof, and application of titanium oxide soluble electrode in preparation of high-purity titanium by means of molten salt electrolysis
  • Titanium oxide soluble electrode and preparation method thereof, and application of titanium oxide soluble electrode in preparation of high-purity titanium by means of molten salt electrolysis
  • Titanium oxide soluble electrode and preparation method thereof, and application of titanium oxide soluble electrode in preparation of high-purity titanium by means of molten salt electrolysis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Ti 9 o 17 Preparation of soluble electrode and its use as anode for electrolytic preparation of high-purity titanium metal.

[0065] (1) Ingredients

[0066] The raw material is micron TiO 2 Powder, micron carbon black powder, according to Ti 9 o 17 The chemical formula of the block and the chemical reaction between the raw materials used are used to calculate the molar ratio of each raw material;

[0067] Micron TiO 2Powder: micron carbon black powder = 9: 1.2

[0068] (2) Mixing and drying

[0069] Put the raw materials measured in step (1) into a rolling ball mill, add WC-8wt% Co cemented carbide balls as grinding balls, add absolute ethanol as a wet grinding medium, and grind and disperse at a ball milling speed of 30r / min for 48 hours , the raw materials are mixed evenly, the addition of absolute ethanol is limited to immersing the raw materials and the grinding balls, and then the grinding balls are separated by sieving to obtain a mixed slurry, and the re...

Embodiment 2

[0075] Ti 9 o 17 Preparation of soluble electrode and its use as anode for electrolytic preparation of high-purity titanium metal.

[0076] (1) Ingredients

[0077] The raw material is micron TiO 2 Powder, graphite powder, according to Ti 9 o 17 The chemical formula of the block and the chemical reaction between the raw materials used are used to calculate the molar ratio of each raw material;

[0078] Micron TiO 2 Powder: graphite powder = 9:2

[0079] (2) Mixing and drying

[0080] Put the raw materials measured in step (1) into a rolling ball mill, add WC-8wt% Co cemented carbide balls as grinding balls, add absolute ethanol as a wet grinding medium, and grind and disperse at a ball milling speed of 30r / min for 48 hours , the raw materials are mixed evenly, the addition of absolute ethanol is limited to immersing the raw materials and the grinding balls, and then the grinding balls are separated by sieving to obtain a mixed slurry, and the resulting mixed slurry is ...

Embodiment 3

[0086] Ti 9 o 17 Preparation of soluble electrode and its use as anode for electrolytic preparation of high-purity titanium metal

[0087] (1) Ingredients

[0088] The raw material is micron TiO 2 Powder, activated carbon powder, according to Ti 9 o 17 The chemical formula of the block and the chemical reaction between the raw materials used are used to calculate the molar percentage of each raw material;

[0089] Micron TiO 2 Powder: activated carbon powder = 9:2.

[0090] (2) Mixing and drying

[0091] Put the raw materials measured in step (1) into a rolling ball mill, add WC-8wt% Co cemented carbide balls as grinding balls, add absolute ethanol as a wet grinding medium, and grind and disperse at a ball milling speed of 30r / min for 48 hours , mix the raw materials evenly, the amount of absolute ethanol is limited to immerse the raw materials and the grinding balls, then sieve and separate the grinding balls to obtain a mixed slurry, dry the resulting mixed slurry an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Resistivityaaaaaaaaaa
Resistivityaaaaaaaaaa
Current densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a titanium oxide soluble electrode; the titanium oxide is TiO, Ti3O5, Ti4O7, Ti5O9, Ti6O11, Ti7O13, Ti8O15 or Ti9O17; the method comprises the steps of firstly, preparing the raw material into a titanium oxide block or a composite titanium oxide block formed by combining the titanium oxide with a titanium rod or a graphite rod; then, carrying out fine finishing on the titanium oxide block or the composite titanium oxide block to obtain the titanium oxide soluble electrode; a technology for preparing the titanium oxide block or the composite titanium oxide block comprises the following steps: (1) blending; (2) mixing and drying; (3) sintering by adopting a discharge plasma sintering system. The invention also provides the titanium oxide soluble electrode prepared by the method, and application of the titanium oxide soluble electrode in preparation of high-purity titanium by means of molten salt electrolysis. After the method is adopted, the titanium-containing soluble electrode which is low in contents of C and N and high in conductivity can be obtained, so that the high-purity metal titanium which is not contaminated by an anode is obtained when the titanium oxide soluble electrode is taken as the anode and / or a cathode for preparing metal titanium by means of electrolysis.

Description

technical field [0001] The invention belongs to the technical field of nonferrous metal metallurgy, and in particular relates to a titanium oxide soluble electrode, a preparation method thereof and an application in the preparation of high-purity titanium by molten salt electrolysis. Background technique [0002] Metal titanium, especially high-purity titanium, has the advantages of low density, high specific strength, good plasticity, corrosion resistance, etc., and has special memory performance and hydrogen storage performance, so it is widely used in aviation, military and atomic energy industries. High-purity titanium can also be used as a bio-substitute material in the medical field and as a target for sputtering coatings in the electronics industry, which has great potential for development. However, the bottleneck in the application of high-purity titanium lies in its difficulty in preparation. At present, the method commonly used in industry to prepare high-purity ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/46C04B35/64C25C7/02C25C3/28
CPCC04B35/46C04B35/64C04B2235/422C04B2235/424C04B2235/425C04B2235/666C04B2235/79C25C3/28C25C7/025
Inventor 赵明建金永中陈婷
Owner 成都锦钛精工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com