Abstract

The invention relates to the technical field of microbial fuel cells, in particular to a method for preparing a microbial fuel cell electrode material employing rape stalks. The method comprises the steps as follows: rape stalks are sheared, dried and mixed with an H2SO4 solution in a hydrothermal reactor; the mass concentration of H2SO4 is 10%, 30% or 50%; reaction is carried out at 150 DEG C for 3 hours; the solution is cooled and then subjected to suction filtration to neutrality; the product is mixed with distilled water at the ratio of 1 to 1.5; the mixture is further put into the hydrothermal reactor, reacts at 120 DEG C for 3 hours, and is dried after suction filtration to obtain hydrothermal carbon; the sample is carbonized in a nitrogen condition in a tube furnace; the carbonization temperature is 400 DEG C; the heating rate is 10 DEG C / min; the nitrogen flow rate is controlled at 0.6L / min; the carbonized sample is soaked with 5wt% HCl for 6 hours and washed to neutrality; and the product is soaked with 3wt% HF for 6 hours, washed to neutrality and dried. The method is simple; and the prepared electrode is large in specific surface area, high in specific capacitance, good in biocompatibility, high in electron transfer rate and good in electricity production effect.

Description

technical field [0001] The invention relates to the technical field of microbial fuel cells, in particular to a method for preparing electrode materials of microbial fuel cells by using rapeseed stalks. Background technique [0002] The depletion of fossil energy and the resulting environmental pollution have been plagued by today's society. The long-term rapid development has caused huge damage to the ecological environment. Environmental Pollution. [0003] A microbial fuel cell (MFC) is a device that converts chemical energy into electrical energy through the oxidation of organic fuel by microorganisms. It can be applied to the treatment of polluted water and soil, realize the energy absorption of organic matter fuel and purify water and soil at the same time, and achieve the dual utilization of environment and energy. [0004] The anode of the microbial fuel cell is the area where the microbial biofilm attaches, which is responsible for the function of transferring ele...

AI Technical Summary

Problems solved by technology

[0009] At present, porous carbon electrodes are mainly used in supercapacitors, and the research on it is mainly to promote its rapid industrial application and increase practical value, such as (patent name: a preparation method of porous carbon and its products, patent application number 201410038075.2), and The application in microbial fuel cells is relatively rare

Images