A waterproof coating and modification technology, applied in the field of coatings, can solve problems such as chronic bronchitis, achieve high tensile strength, simple construction, health and environmental protection, and speed up the effect of preparation

Inactive Publication Date: 2016-07-27
TIANJIN PENGTENG NEW BUILDING MATERIALS
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Organic waterproof coating is a new type of polymer waterproof coating. It has been widely used in waterproofing projects because of its excellent physical and chemical properties such as good wear resistance, corrosion resistance, chemical resistance, high hardness, and high elasticity. However, a lot of organic solvents are added in the process of preparation and construction of traditional solvent-based waterproof coatings, which poses a great threat to human health and environmental protection. Free polyisocyanates in organic waterproof coatings are harmful to skin, Eyes and respiratory tract have a strong irritating effect, and long-term exposure can cause chronic bronchitis and other diseases. Therefore, we propose an organic modified waterproof coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment proposes a kind of organically modified waterproof coating, including the following raw materials in parts by weight: 30 parts of isocyanate, 25 parts of polyether, 15 parts of modifier, 20 parts of sodium methyl silicate, 5 parts of iron dioxide, two 11 parts of silicon oxide, 6 parts of sodium carbonate, 40 parts of deionized water, 13 parts of perlite, 12 parts of nano mica, 3 parts of chlorine dioxide, 4 parts of bentonite, 7 parts of polyacrylamide, 3 parts of polydimethylsiloxane share;

[0017] Its preparation method comprises the following steps:

[0018] S1: Add isocyanate, polyether and deionized water into the mixer, and stir at 40°C at a stirring speed of 35rpm for 2 hours;

[0019] S2: Add modifier, sodium methyl silicate, iron dioxide, silicon dioxide and sodium carbonate, and then stir for 5 hours at a stirring speed of 20 rpm;

[0020] S3: add perlite, nano-mica, chlorine dioxide, bentonite, polyacrylamide and polydimethylsiloxane in se...

Embodiment 2

[0022] This embodiment proposes an organically modified waterproof coating, including the following raw materials in parts by weight: 31 parts of isocyanate, 26 parts of polyether, 16 parts of modifier, 21 parts of sodium methyl silicate, 6 parts of iron dioxide, two 12 parts of silicon oxide, 7 parts of sodium carbonate, 41 parts of deionized water, 14 parts of perlite, 13 parts of nano mica, 4 parts of chlorine dioxide, 5 parts of bentonite, 8 parts of polyacrylamide, 4 parts of polydimethylsiloxane share;

[0023] Its preparation method comprises the following steps:

[0024] S1: Add isocyanate, polyether and deionized water into the mixer, and stir for 2.2 hours at a stirring speed of 36 rpm at 41°C;

[0025] S2: Add modifier, sodium methyl silicate, iron dioxide, silicon dioxide and sodium carbonate, and then stir for 5.2 hours at a stirring speed of 21 rpm;

[0026] S3: add perlite, nano-mica, chlorine dioxide, bentonite, polyacrylamide and polydimethylsiloxane in sequ...

Embodiment 3

[0028] The present embodiment proposes an organically modified waterproof coating, comprising the following raw materials in parts by weight: 32 parts of isocyanate, 27 parts of polyether, 17 parts of modifier, 22 parts of sodium methyl silicate, 7 parts of iron dioxide, two 13 parts of silicon oxide, 8 parts of sodium carbonate, 42 parts of deionized water, 15 parts of perlite, 14 parts of nano mica, 5 parts of chlorine dioxide, 6 parts of bentonite, 9 parts of polyacrylamide, 5 parts of polydimethylsiloxane share;

[0029] Its preparation method comprises the following steps:

[0030] S1: Add isocyanate, polyether and deionized water into the mixer, and stir at 42°C at a stirring speed of 37rpm for 2.4 hours;

[0031] S2: Add modifier, sodium methyl silicate, iron dioxide, silicon dioxide and sodium carbonate, and then stir for 5.4 hours at a stirring speed of 21 rpm;

[0032] S3: Add perlite, nano-mica, chlorine dioxide, bentonite, polyacrylamide and polydimethylsiloxane ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an organic modified waterproof paint which comprises the following raw materials in part by weight: 30 to 35 parts of isocyanate, 25 to 30 parts of polyether, 15 to 20 parts of modifier, 20 to 25 parts of sodium methyl silicate, 5 to 8 parts of ferrum dioxide, 11 to 15 parts of silicon dioxide, 6 to 9 parts of sodium carbonate, 40 to 45 parts of deionized water, 13 to 16 parts of perlite, 12 to 15 parts of nano mica, 3 to 6 parts of chlorine dioxide, 4 to 7 parts of bentonite, 7 to 9 parts of polyacrylamide and 3 to 5 parts of polydimethylsiloxane. A preparation method of the organic modified waterproof paint comprises the following steps of: S1, adding the isocyanate, the polyether and the deionized water into a stirrer, and stirring for 2 to 3 hours at a temperature of 40 to 45 DEG C at a stirring speed of 35 to 45rpm; S2, adding the modifier, the sodium methyl silicate, the ferrum dioxide, the silicon dioxide and the sodium carbonate, and then stirring for 5 to 6 hours at a stirring speed of 20 to 25rpm. The organic modified waterproof paint has excellent waterproofness, high tensile strength and excellent flexibility, is simple in construction, healthy and environmental-friendly, and takes a very important effect on concrete construction.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an organic modified waterproof coating. Background technique [0002] Organic waterproof coating is a new type of polymer waterproof coating. It has been widely used in waterproofing projects because of its excellent physical and chemical properties such as good wear resistance, corrosion resistance, chemical resistance, high hardness, and high elasticity. However, a lot of organic solvents are added in the process of preparation and construction of traditional solvent-based waterproof coatings, which poses a great threat to human health and environmental protection. Free polyisocyanates in organic waterproof coatings are harmful to skin, Eyes and respiratory tract have a strong stimulating effect, and long-term exposure can cause chronic bronchitis and other diseases. Therefore, we propose an organic modified waterproof coating. Contents of the invention [0003] Based on th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D133/26C09D183/04C09D7/12
CPCC09D175/08C08K2201/011C08L2205/03C09D7/61C09D7/63C09D7/65
Inventor 孙彦青
Owner TIANJIN PENGTENG NEW BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap