A preparation method of silver-coated copper nanoparticles that can be used in conductive inks

A technology of conductive ink and nano particles, which is applied in transportation and packaging, metal processing equipment, coating, etc., can solve the problems of large silver consumption, low cost, and simple preparation process, and achieve green and mild reaction conditions and strong anti-oxidation Ability, high effect of monodispersity

Active Publication Date: 2018-05-15
SHENZHEN INST OF ADVANCED TECH CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The copper-silver bimetallic materials prepared by the above methods have good electrical conductivity, but all have the disadvantages of large silver consumption, complicated preparation process, and high overall cost.
At present, there is no report on the preparation of silver-coated copper core-shell nanoparticles with simple preparation process, low cost and application in large-scale production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of silver-coated copper nanoparticles that can be used in conductive inks
  • A preparation method of silver-coated copper nanoparticles that can be used in conductive inks

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] This embodiment is used for the preparation method of the silver-coated copper nanoparticles of conductive ink, comprises the following steps:

[0040] (1) Prepare solution a; add 0.25 g of copper nitrate trihydrate and 0.50 g of polyvinylpyrrolidone into 100 ml of ethylene glycol, stir for 5 minutes and then heat to 100° C. to obtain solution a;

[0041] (2) Prepare solution b; add 3.2g ascorbic acid in 200ml ethylene glycol, stir well and keep the same temperature as solution a to obtain solution b;

[0042] (3) Add solution b to solution a, and continue to stir for 30 minutes to obtain a mixed solution; then add 0.12 g of silver nitrate to 10 ml of deionized water, and add the above mixed solution after completely dissolving, react for 20 minutes and cool to room temperature, 8000r / min The deionized water was centrifuged and washed 4 times, and the precipitate was taken and dried at room temperature for 6 hours under the condition of a vacuum degree of less than 0.01...

Embodiment 2

[0045] This embodiment is used for the preparation method of the silver-coated copper nanoparticles of conductive ink, comprises the following steps:

[0046] (1) Prepare solution a; add 0.45 g of copper acetylacetonate and 1.05 g of cetyltrimethylammonium bromide into 140 ml of diethylene glycol, stir for 15 minutes and then heat to 120° C. to obtain solution a;

[0047] (2) Prepare solution b; add 2.5g of ascorbic acid into 80ml of diethylene glycol, stir well and keep the same temperature as solution a to obtain solution b;

[0048] (3) Add solution b to solution a, and continue to stir for 20 minutes; then add 0.36 g of silver nitrate to 15 ml of deionized water, add the above solution after completely dissolving, react for 100 minutes, cool to room temperature, and centrifuge and wash with 6000 r / min deionized water 4 times, the precipitate was taken and dried at room temperature for 12 hours under the condition that the vacuum degree was less than 0.01 MPa to obtain silv...

Embodiment 3

[0051] This embodiment is used for the preparation method of the silver-coated copper nanoparticles of conductive ink, comprises the following steps:

[0052] (1) Prepare solution a; add 0.58g of copper hydroxide and 2.16g of polyethylene glycol-2000 into 80ml of glycerol, stir for 30min and then heat to 150°C to obtain solution a;

[0053] (2) Prepare solution b; add 2.9g of ascorbic acid into 150ml of glycerol, stir well and keep the same temperature as solution a to obtain solution b;

[0054] (3) Add solution b to solution a, and continue to stir for 40 minutes; then add 0.29 g of silver nitrate to 8 ml of deionized water, add the above solution after completely dissolving, react for 240 minutes, cool to room temperature, and centrifuge wash with 3000 r / min deionized water 4 times, the precipitate was taken and dried at room temperature for 10 h under the condition of a vacuum degree of less than 0.01 MPa to obtain silver-coated copper nanoparticles.

[0055] The XRD patt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of silver-coated copper nanoparticles used in conductive inks, respectively dissolving copper precursors, protective agents and reducing agents in organic solvents, heating to obtain nano-copper solutions; adding nano-copper solutions to the Silver nitrate solution was added to the mixture, cooled, centrifuged and dried to prepare silver-coated copper nanoparticles for conductive ink. The invention adopts continuous reduction and replacement methods to prepare silver-coated copper nanoparticles for conductive ink; the preparation process does not need to add complex chelating agents, separation and purification, activation sensitization and other intermediate processes, and the reaction conditions are green and mild. In addition, the silver-coated copper nanoparticles produced by the preparation method have good dispersibility, high monodispersity, and strong anti-oxidation ability, and can be produced on a large scale and applied to the field of conductive ink.

Description

technical field [0001] The invention relates to a method for preparing silver-coated copper nanoparticles, in particular to a method for preparing silver-coated copper nanoparticles used in conductive inks, and belongs to the field of bimetallic nanomaterials. Background technique [0002] The rapid development of printed electronics has put forward higher requirements for its core material - conductive ink. At present, there are mostly nano-gold and silver-based conductive inks on the market, but their industrial production is limited due to possible electromigration and high costs. In contrast, nano-copper-based conductive inks have similar conductivity and lower cost to gold and silver conductive inks, and are ideal substitutes for gold and silver conductive inks. However, the easy oxidation of metallic copper greatly reduces its reliability. Based on this, researchers have considered uniformly coating a layer of metallic silver on the surface of nano-copper particles to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B22F1/02
CPCB22F9/24B22F1/065B22F1/17
Inventor 孙蓉张昱朱朋莉欧阳琼林李刚赵涛
Owner SHENZHEN INST OF ADVANCED TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com