Crystallizer covering slag for continuously casting high-manganese high-aluminum steel and preparation method of crystallizer covering slag

A mold flux and high-aluminum steel technology, applied in the field of metallurgy, can solve the problems of reducing the surface tension of the flux, deteriorating the performance of the flux, and increasing the probability of slag entrainment, so as to ensure the network formation ability, avoid uneven cooling, The effect of improving productivity

Active Publication Date: 2016-05-11
CHONGQING UNIV
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patents CN104439133A and CN104607608A respectively disclose mold slag suitable for continuous casting of high manganese and high aluminum steel and medium manganese steel for automobiles, but both patents contain relatively high content of Na 2 O, respectively 4~11% and 10~14%, on the one hand, Na 2 O will also react with the high aluminum content in molten steel and deteriorate the performance of mold flux. On the other hand, Na 2 O can reduce the surface tension of mold slag, which is not conducive to the separation of slag and steel, and will increase the probability of slag entrainment
To sum up, the existing mold powder is not suitable for continuous casting of high manganese and high aluminum steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crystallizer covering slag for continuously casting high-manganese high-aluminum steel and preparation method of crystallizer covering slag

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The preparation method of above-mentioned mold powder comprises the following steps:

[0043] 1) Using wollastonite, limestone, quartz sand, fluorite, bauxite, barium carbonate, magnesia, soda, lithium carbonate and carbonaceous materials as raw materials, calculate the Describe the amount of each raw material, and weigh each raw material according to the calculated amount;

[0044] 2) Mix the wollastonite, limestone, quartz sand, fluorite, lithium carbonate, soda, bauxite, barium carbonate and magnesia weighed in step 1), and keep warm at 1350~1450°C for 30~40 minutes to make each The raw material is melted evenly, and then it is cooled naturally after being taken out of the furnace to obtain a premelt;

[0045] 3) Crushing the premelted material obtained in step 2) so that the particle size of the crushed premelted material is ≤200 mesh, adding the carbonaceous material weighed in step 2), and mixing evenly to obtain a dry material;

[0046] 4) Put water, cellulose ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
melting pointaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a crystallizer covering slag for continuously casting high-manganese high-aluminum steel and preparation method of the crystallizer covering slag. The covering slag is prepared from the following components in parts by weight: 20-38 parts of CaO, 20-35 parts of Al2O3, 5-18 parts of SiO2, 10-22 parts of BaO, 2-7 parts of Li2O, 5-12 parts of F<->, 1-4 parts of MgO, 2-8 parts of C and Fe2O3 which is less than or equal to 2 parts. According to the preparation method disclosed by the invention, wollastonite, limestone, quartz sand, fluorite, bauxite, barium carbonate, magnesia, soda, lithium carbonate and carbonaceous materials are used as raw materials, and the covering slag is prepared through the following steps of: calculating of consumption, melting, smashing, fine grinding, drying and granulation. The covering slag disclosed by the invention has the characteristics of being low in reactivity and good in property stability, the lubrication and the thermal transmission of casting blanks can be effectively coordinated and controlled, the smooth performing of the continuous casting process of the high-manganese high-aluminum steel can be guaranteed, high-manganese high-aluminum steel continuous casting blanks with excellent surface quality are cast, and multi-heat continuous casting can be realized.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to mold mold powder for high manganese and high aluminum steel continuous casting and a preparation method thereof. Background technique [0002] Mold slag is a kind of synthetic slag used in the continuous casting process. It has multiple functions such as heat insulation and heat preservation, prevention of molten steel oxidation, absorption of inclusions, lubrication and control of heat transfer. important. High manganese and high aluminum steel, such as TRIP steel, TWIP steel, austenitic non-magnetic steel 20Mn23AlV, Mn13, etc., have excellent mechanical and mechanical properties and cost performance. The production of high manganese and high aluminum steel, such as 20Mn23AlV austenitic non-magnetic steel, has the following characteristics in the continuous casting process: the content of alloy elements such as Mn and Al in the steel is high, the liquidus tempera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 王谦吴婷何生平
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com