Dyeing and finishing technology for cotton/viscose ammonia multi-fiber stretch fabric employing bio-enzyme low-temperature treatment

A technology of low-temperature treatment and biological enzymes, which is applied in the field of textile printing and dyeing, can solve the problems of complex dyeing and finishing process, easy creases and stripes, and deformation of fabric structure, so as to optimize the dyeing process parameters, achieve full dyeing quality, and benefit The effect of smooth production

Active Publication Date: 2016-05-04
HUAFANG
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Cotton-viscose-elastic interwoven fabric is fluffy, crisp, elastic, moisture-wicking, comfortable and close-fitting, and can meet the requirements of high-end fabrics. The difference in properties between cotton and viscose fibers in the actual production process makes the pre-treatment and dyeing and finishing processes more complicated, especially It is difficult to dye, the dark color is not full, the depth is not enough, and the technical requirements are high; during the weaving process of cotton viscoelastic fabric, there is a large residual stress inside the gray fabric, which will cause the fabric structure to deform. Problems such as creases and stripes are prone to occur during the dyeing process of fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dyeing and finishing technology for cotton/viscose ammonia multi-fiber stretch fabric employing bio-enzyme low-temperature treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A kind of dyeing and finishing process of the cotton viscose ammonia multi-fiber elastic fabric that utilizes biological enzyme low-temperature treatment described in this embodiment, the process includes pretreatment process, dyeing process and post-finishing process;

[0056] Described pretreatment process comprises the following steps:

[0057] (1) Enzyme rolling process

[0058] Prepare the treatment solution: add 450L of water, stop heating after raising the temperature to 50°C, add penetrant, and then add biological desizing enzyme, activate for 3 minutes before use, the concentration of penetrant is 5g / L, and the concentration of biological desizing enzyme is 20g / L; The biological desizing enzyme is selected from 2000L of Novozymes, and the penetrant is selected from TA-1 of Binzhou Chenguang Chemical Industry;

[0059] Rolling with enzyme rolling, fix the second fabric guide roller on the 1# groove of the rolling, no creases, adjust the angle between the cloth...

Embodiment 2

[0090] A kind of dyeing and finishing process of the cotton viscose ammonia multi-fiber elastic fabric that utilizes biological enzyme low-temperature treatment described in this embodiment, the process includes pretreatment process, dyeing process and post-finishing process;

[0091] Described pretreatment process comprises the following steps:

[0092] (1) Enzyme rolling process

[0093] Prepare the treatment solution: add 450L of water, stop heating after raising the temperature to 50°C, add penetrant, then add biological desizing enzyme, activate for 3 minutes before use, the concentration of penetrant is 6g / L, and the concentration of biological desizing enzyme is 22g / L;

[0094] Rolling with enzyme, fix the second cloth guide roller on the 1# groove of the rolling, so that no wrinkles can be formed, adjust the angle between the cloth drop frame and the rolling roller, so that no wrinkles can be formed, pile up at room temperature for 15 hours, wash with water, 100 Und...

Embodiment 3

[0124] A kind of dyeing and finishing process of the cotton viscose ammonia multi-fiber elastic fabric that utilizes biological enzyme low-temperature treatment described in this embodiment, the process includes pretreatment process, dyeing process and post-finishing process;

[0125] Described pretreatment process comprises the following steps:

[0126] (1) Enzyme rolling process

[0127] Prepare treatment solution: add 450L of water, stop heating after raising the temperature to 50°C, add penetrant, and then add biological desizing enzyme, activate for 3 minutes before use, wherein the concentration of penetrant is 4.5g / L, and the concentration of biological desizing enzyme is 21g / L;

[0128] Rolling with enzyme rolling, fix the second fabric guide roller on the 1# groove of the rolling, no creases, adjust the angle between the cloth drop frame and the rolling roller, so that no creases can be rubbed, stack at room temperature for 13 hours, wash with water, 95 Under the co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of textile printing and dyeing, and in particular relates to a dyeing and finishing technology for a cotton / viscose ammonia multi-fiber stretch fabric employing bio-enzyme low-temperature treatment. The dyeing and finishing technology comprises a pretreatment technology, a dyeing technology and a post-finishing technology. According to the printing and dyeing method for a cotton / viscose stretch fabric, room-temperature stacked desizing is carried out by a biologic desizing enzyme; and an efficient refining agent is selected, so that various pretreatment indexes are effectively improved; soft and fluffy hand feeling of the cotton / viscose stretch fabric is achieved; energy conservation and emission reduction are achieved through low-temperature desizing; potential drapes in the fabric processing process are eliminated; and smooth production of the dyeing procedure is facilitated. A light-colored fabric is dyed from pad dyeing, and a dark fabric is subjected to cold pad-batch dyeing, so that an improvement of various color fastness indexes is met; dyeing process parameters are optimized; and uniform and full dying material quality is obtained. A softening agent is preferably adopted in fabric post-finishing, so that the hydrophilicity of the fabric is achieved; and the wearing comfort of the fabric is achieved.

Description

technical field [0001] The invention belongs to the technical field of textile printing and dyeing, in particular to a dyeing and finishing process of cotton viscose ammonia multi-fiber elastic fabric treated at low temperature by biological enzyme. Background technique [0002] Cotton-viscose-elastic interwoven fabric is fluffy, crisp, elastic, moisture-wicking, comfortable and close-fitting, and can meet the requirements of high-end fabrics. The difference in properties between cotton and viscose fibers in the actual production process makes the pre-treatment and dyeing and finishing processes more complicated, especially It is difficult to dye, the dark color is not full, the depth is not enough, and the technical requirements are high; during the weaving process of cotton viscoelastic fabric, there is a large residual stress inside the gray fabric, which will cause the fabric structure to deform. Problems such as creases and stripes are prone to occur in the process of f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M16/00D06M15/643D06L3/02D06P3/85D06P1/38D06P1/44D06P5/10D06B7/08D06B15/00D06B17/04D06B21/00D06C7/02D06M101/06D06M101/38D06L4/12D06L4/13
CPCD06B7/08D06B15/00D06B17/04D06B21/00D06C7/02D06M15/643D06M16/003D06M2101/06D06M2101/38D06M2200/50D06P1/38D06P1/445D06P3/008D06P3/8204D06P5/10
Inventor 王力民罗维新李春光王鲁刚王雪芳周勇于剑赵传波卜庆花赵成伟
Owner HUAFANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com