A new type of ultra-soft and wear-resistant imitation jeanette fabric

A technology of imitation peach skin and super softness, which is applied in the field of new super soft and wear-resistant imitation peach skin fabric, which can solve the problems of high price and insufficient antibacterial property of the fabric, and achieve the improvement of softness, super soft hand feeling and antibacterial performance Good results

Active Publication Date: 2018-04-24
CHANGXING RONGFENG TEXTILE CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of enzymes is relatively high, and the antibacterial properties of the fabrics made are not good enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A new type of ultra-soft and wear-resistant imitation jeanette fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of preparation method of novel ultra-soft wear-resistant imitation jeanette fabric, its steps are as follows:

[0022] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0023] Wherein the concentration of the caustic soda that adopts during singeing is 90g / L,

[0024] (2) Grinding: use metal abrasive grains for dry grinding;

[0025] (3) Microbial modification treatment:

[0026] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.3:0.8:0.2;

[0027] The brushed fabric is evenly sprayed with bacteria agent and fermented at 39°C for 95 hours;

[0028] After fermentation, wash with warm water and dry;

[0029] (5) Polishing treatment: polishing the modified fabric;

[0030] (6) Dyeing according to co...

Embodiment 2

[0033] A kind of preparation method of novel ultra-soft wear-resistant imitation jeanette fabric, its steps are as follows:

[0034] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0035] Wherein the concentration of the caustic soda that adopts during singeing is 105g / L,

[0036] (2) Grinding: use metal abrasive grains for dry grinding;

[0037] (3) Microbial modification treatment:

[0038] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.3:0.8:0.1;

[0039] The brushed fabric is evenly sprayed with bacteria agent and fermented at 39°C for 102 hours;

[0040] After fermentation, wash with warm water and dry;

[0041] (5) Polishing treatment: polishing the modified fabric;

[0042] (6) Dyeing according to ...

Embodiment 3

[0045] A kind of preparation method of novel ultra-soft wear-resistant imitation jeanette fabric, its steps are as follows:

[0046] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0047] Wherein the concentration of the caustic soda that adopts during singeing is 99g / L,

[0048] (2) Grinding: use metal abrasive grains for dry grinding;

[0049] (3) Microbial modification treatment:

[0050] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.3:0.8:0.2;

[0051] The brushed fabric is evenly sprayed with bacteria agent and fermented at 39°C for 100 hours;

[0052] After fermentation, wash with warm water and dry;

[0053] (5) Polishing treatment: polishing the modified fabric;

[0054] (6) Dyeing according to c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a novel super-soft wear-resistant polyester peach skin simulating fabric. The processing method of the novel super-soft wear-resistant polyester peach skin simulating fabric is natural, environmentally friendly, free of residues and free of environment pollution, and belongs to the green technology. The hand feeling of the prepared polyester peach skin simulating fabric is super soft and just like tactile impression of skin, and the novel super-soft wear-resistant polyester peach skin simulating fabric has high color and luster of silk, is high in antibacterial performance, and is a novel fabric with large market potential; the looseness degree of the fabric is greatly improved compared with that of a softened ordinary pure-cotton polyester peach skin simulating fabric.

Description

technical field [0001] The invention relates to a novel ultra-soft and wear-resistant imitation jeanette fabric, which belongs to the technical field of textiles. Background technique [0002] Peach skin is a novel thin pile fabric of microfiber fabric, which is born out of artificial suede, and has a softer texture because it has not been wet-processed with polyurethane. And because the down is shorter, there is almost no down on the surface, but the skin can feel it, so that the feel and appearance are more delicate and unique. The luster of peach skin is soft and elegant. Compared with artificial suede, it gives consumers a sense of novelty and suits people's curious consumption psychology, so it quickly became popular in the international market. Tencel is treated to obtain a peach skin feel. The formation of the unique style of peach skin fabrics can be said to be based on ultra-fine denier high-density thin fabrics, and sanding finishing is the key to the product. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M16/00D06M101/06D06M101/04
CPCD06M16/003D06M2101/04D06M2101/06D06M2200/20
Inventor 许蓉许建斌
Owner CHANGXING RONGFENG TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com