Off-the-road tire abrasion-resistant formula and preparation method thereof

A technology for construction machinery and tires, applied in the field of construction machinery tire wear-resistant formulations and their preparation, can solve problems such as tread disintegration and blockage, affecting the service life of tires, etc., to prevent early vulcanization, improve puncture resistance, reduce The effect of scrapping costs

Inactive Publication Date: 2016-01-20
WENDENG SANFENG TIRE CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention mainly solves the problem that the tread of the existing engineering machinery tires is prone to chipping and chipping, thereby affecting the service life of the tires.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1, accurately weigh styrene-butadiene rubber SBR150284Kg, modified styrene-butadiene rubber 16Kg, high wear-resistant carbon black N33069Kg, white carbon black 5Kg, anti-aging agent microcrystalline wax and anti-aging agent 4010NA7.5Kg, active agent ZnO and SA4.5Kg , tackifier A-9010Kg, vulcanizing agent S and accelerator CZ3.66Kg, anti-scorch agent CTP0.4Kg, softener aromatic hydrocarbon oil 10Kg, leveling agent 2.5Kg; Its preparation method comprises following processing steps:

[0027] 1. Put the above weighed styrene-butadiene rubber SBR1502, modified styrene-butadiene rubber, anti-aging agent microcrystalline wax and anti-aging agent 4010NA, active agent ZnO, tackifier A-90, processing aid leveling agent into the internal mixer, Mixing for 35 seconds, mixing temperature 90°C, pressure 0.45Mpa;

[0028] 2. Put in 46Kg of high wear-resistant carbon black N330 and white carbon black, mix for 35 seconds, the mixing temperature is 100°C, and the pressure is 0.45...

Embodiment 2

[0036] Example 2, accurately weigh styrene-butadiene rubber SBR150282Kg, modified styrene-butadiene rubber 18Kg, high wear-resistant carbon black N33067Kg, white carbon black 5Kg, anti-aging agent microcrystalline wax and anti-aging agent 4010NA7.0Kg, active agent ZnO and SA4.0Kg , Tackifier A-909.0Kg, vulcanizing agent S and accelerator CZ3.3Kg, anti-scorch agent CTP0.35Kg, softener aromatic oil 10Kg, leveling agent 2.0Kg; Its preparation method is identical with embodiment 1.

Embodiment 3

[0037] Embodiment 3, accurately weigh styrene-butadiene rubber SBR150082Kg, modified styrene-butadiene rubber 5, super wear-resistant carbon black N22062Kg, anti-aging agent protective wax and anti-aging agent 40205.6Kg, active agent ZnO and SA4.5Kg, tackifier rosin 6.0Kg , vulcanizing agent S and accelerator NS3.3Kg, anti-scorch agent CTP0.2Kg, softener machine oil 8.0Kg, uniform tackifier 2.0Kg,; Its preparation method comprises following processing steps:

[0038] 1. Put styrene-butadiene rubber, modified styrene-butadiene rubber, anti-aging agent, active agent, tackifier, and processing aid into the internal mixer, and mix for 30 seconds at a mixing temperature of 100°C and a pressure of 0.4Mpa;

[0039] 2. Put in 2 / 3 weight of carbon black and white carbon black, knead for 30 seconds, the kneading temperature is 110°C, and the pressure is 0.4Mpa;

[0040] 3. Add another 1 / 3 weight of carbon black, knead for 40 seconds, kneading temperature 125°C, pressure 0.4Mpa;

[0041...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an off-the-road tire abrasion-resistant formula. The off-the-road tire abrasion-resistant formula is characterized by comprising, by weight, 80-100 parts of butadiene-styrene rubber, 0-20 parts of modified butadiene-styrene rubber, 40-70 parts of carbon black, 0-15 parts of white carbon black, 4.5-9.5 parts of anti-aging agent, 4-9 parts of active agent, 4-10 parts of tackifier, 2.7-5.5 parts of vulcanization accelerator, 0.15-0.5 part of scorch retarder, 6-12 parts of softener and 1.5-3 parts of processing agent. The preparation method includes the steps that the butadiene-styrene rubber, the modified butadiene-styrene rubber, the anti-aging agent, the active agent, the tackifier and the processing agent are thrown into an internal mixer to be mixed first; the 2 / 3 weight part of carbon black and the white carbon black are thrown to be mixed; then the other 1 / 3 weight part of carbon black is thrown to be mixed; at last, the softener is thrown to be mixed, and sheet discharging and cooling are carried out. The weather resistance, heat resistance, cut growth resistance and abrasive resistance of a tire are improved, and the formula is particularly suitable for off-the-road tires; when the formula is used in a tread, the service life of the tire can be greatly prolonged, and the chunking and chipping resistance of the tire can be greatly improved.

Description

Technical field: [0001] The invention relates to the technical field of engineering machinery tires, in particular to a wear-resistant formula for engineering machinery tires and a preparation method thereof. Background technique: [0002] OTR tires are mainly used in harsh road conditions such as underground mines and mines. Due to the harsh road conditions, the tire tread is prone to chipping and chipping, which affects its service life. Therefore, the wear resistance and chipping resistance of the tread are improved. Block performance is of great significance to prolong the service life of tires. Invention content: [0003] The purpose of the present invention is to overcome the shortcomings of the above-mentioned prior art, and provide a kind of engineering machinery tire formula. [0004] Another object of the present invention is to provide a method for preparing an engineering machinery tire formula. [0005] The invention mainly solves the problem that the tread ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L15/00C08L91/00C08L91/06C08K13/02C08K3/04C08K3/36B29B7/28B29B7/82B29B7/88
Inventor 王晓东
Owner WENDENG SANFENG TIRE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com