Preparation method of colorful polyester fiber

A technology for the preparation of colored polyester, which is applied in the direction of adding pigments to single-component polyester artificial filaments and spinning solutions, which can solve the problems of poor spinnability of polyester filaments, high cost of polyester filaments, and polyester filaments. Difficulty in dyeing, etc., to achieve better and brighter colors, higher color fastness, and environmental protection

Active Publication Date: 2015-12-30
JIEDONG PARIS WANZHU SHAHUA TEXTILES CO LTD
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the Chinese patent discloses a preparation method of polyester fiber textile thread. This patent is to dye the polyester fiber after it is formed. The dyeing is difficult, and the subsequent processing technology is cumbersome, the cost is high and it is not environmentally friendly.
Chinese patent "Preparation method of colored flame-retardant matting hollow polyester filament", application number 200910303607.6, application date 2009-06-24, this patent solves the problem of difficult polyester dyeing
But the cost of preparing polyester filament according to the method in this invention is higher, after adding color masterbatch and delustering agent, cause the spinnability of polyester filament to deteriorate, resulting in poor product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of colorful polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation process for colored polyester fibers, the preparation steps are as follows:

[0032] S1. Drying: Dry the polyester fiber, polylactic acid flame retardant, and color masterbatch separately at a drying temperature of 110-120°C and a drying time of 1 hour for later use;

[0033] The polylactic acid flame retardant is prepared by melt copolymerization of melamine or primary amine containing benzimidazole structure or o-phenylenediamine and lactic acid;

[0034] The color masterbatch consists of 60 parts by weight of carrier, 15 parts of toner, 15 parts of dispersant, 4 parts of heat stabilizer, 4 parts of antibacterial agent, 4 parts of antioxidant and 3 parts of additive;

[0035] The carrier in the color masterbatch is prepared from the following raw materials in parts by weight: 20 parts of polyolefin, 15 parts of polyethylene terephthalate, and 10 parts of polyamide resin;

[0036] The dispersant in the masterbatch is any two of polyethylene wax, ethylene...

Embodiment 2

[0047] A preparation process for colored polyester fibers, the preparation steps are as follows:

[0048] S1. Drying: Dry the polyester fiber, polylactic acid flame retardant, and color masterbatch separately. The drying temperature is 110~120°C, and the drying time is 1.5h. Reserve;

[0049] The polylactic acid flame retardant is prepared by melt copolymerization of melamine or primary amine containing benzimidazole structure or o-phenylenediamine and lactic acid;

[0050] The color masterbatch consists of 60 parts by weight of carrier, 15 parts of toner, 15 parts of dispersant, 4 parts of heat stabilizer, 4 parts of antibacterial agent, 4 parts of antioxidant and 3 parts of additive;

[0051] The carrier in the color masterbatch is prepared from the following raw materials in parts by weight: 20 parts of polyolefin, 15 parts of polyethylene terephthalate, and 10 parts of polyamide resin;

[0052] The dispersant in the masterbatch is any two of polyethylene wax, ethylene-vin...

Embodiment 3

[0063] A preparation process for colored polyester fibers, the preparation steps are as follows:

[0064] S1. Drying: Dry the polyester fiber, polylactic acid flame retardant, and color masterbatch separately at a drying temperature of 110-120°C and a drying time of 2 hours for later use;

[0065] The polylactic acid flame retardant is prepared by melt copolymerization of melamine or primary amine containing benzimidazole structure or o-phenylenediamine and lactic acid;

[0066] The color masterbatch consists of 60 parts by weight of carrier, 15 parts of toner, 15 parts of dispersant, 4 parts of heat stabilizer, 4 parts of antibacterial agent, 4 parts of antioxidant and 3 parts of additive;

[0067] The carrier in the color masterbatch is prepared from the following raw materials in parts by weight: 20 parts of polyolefin, 15 parts of polyethylene terephthalate, and 10 parts of polyamide resin;

[0068] The dispersant in the masterbatch is any two of polyethylene wax, ethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a chemical fiber textile flame-retardant material, particularly to a preparation process of a colorful polyester fiber. The preparation process comprises the following steps: drying, grinding, mixing, melting, spinning, after-processing and shaping raw materials to obtain a finished product. The colorful polyester fiber prepared by adopting the process has good spinning property, good flame-retardant effect, high decomposition temperature, good heat stability and excellent dyeing property; the color is brighter compared with the ordinary dyeing fiber, and the color fastness is high.

Description

technical field [0001] The invention relates to the technical field of chemical fiber textile flame-retardant materials, in particular to a preparation process of colored polyester fibers. Background technique [0002] Most of the clothing, decorations and industrial products used in textile materials require that the textiles should have flame retardant properties, such as children's clothing, special industry clothing, textile decorations used in public places such as hotels and entertainment, and transportation. Textiles, packaging textiles, etc. Therefore, flame-retardant textile materials have broad market application prospects and requirements. Due to its excellent properties such as high strength, chemical resistance, good weather resistance, and good dimensional stability, polyester materials are currently the fiber variety with the largest production scale and output in chemical fibers, and it is also one of the fiber varieties with a wide range of applications. Ho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/04
Inventor 黄怀光沈亚林陈少双王树江施纯亮
Owner JIEDONG PARIS WANZHU SHAHUA TEXTILES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com