Closed-cell two-step foamed material prepared from styrene butadiene rubber, natural rubber, butadiene rubber and high styrene resin, and preparation method of closed-cell two-step foamed material

A high-styrene resin and natural rubber technology, applied in the field of foaming materials, can solve chemical weather resistance, poor embossing and shaping, low tensile and tear strength, embossing, poor plasticity, etc. problems, to achieve the effect of wide cold resistance, outstanding performance and low cost

Active Publication Date: 2015-12-23
YIBAO FUJIAN POLYMER MATERIALS
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the maturity of domestic production technology, styrene-butadiene rubber has been widely used in various industries. It has good elasticity, wear resistance, crack resistance, wet skid resistance and price advantages and has become the mainstream rubber type. Low strength, chemical and weather resistance, poor embossing and shaping; natural rubber has good resilience, elongation, tensile strength, and tear strength, but in terms of shortcomings, embossing and plasticity are not good. Good, basically similar to styrene-butadiene rubber; butadiene rubber has very excellent cold resistance (-100°C) elasticity and wear resistance, but poor processability alone, and has a tendency to cold flow; high styrene resin has excellent mechanical stiffness in recent years , wear resistance, etc. are widely used in the field of shoe material foaming materials, but high styrene resin products also have the disadvantages of poor softness and large shrinkage, and they are all one-time vulcanized products with low technological level. In terms of solubility, since the first three belong to rubber materials, while the latter is a thermoplastic elastomer, it is a big difficulty for foamed materials to have poor dispersion after processing and integration. How to improve the process to improve dispersion is good, low cost, and low cost. Good cold resistance, high resilience, high tensile strength, high tear strength, product embossing and other surface treatment wear-resistant, anti-slip comprehensive physical properties, so as to broaden the scope of application, a breakthrough is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Closed-cell two-step foamed material prepared from styrene butadiene rubber, natural rubber, butadiene rubber and high styrene resin, and preparation method of closed-cell two-step foamed material
  • Closed-cell two-step foamed material prepared from styrene butadiene rubber, natural rubber, butadiene rubber and high styrene resin, and preparation method of closed-cell two-step foamed material
  • Closed-cell two-step foamed material prepared from styrene butadiene rubber, natural rubber, butadiene rubber and high styrene resin, and preparation method of closed-cell two-step foamed material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1, the used material source specification of embodiment 2 are as shown in table 1 below:

[0045]

[0046] Table 1. Specifications of each raw material source

[0047] Example 1

[0048] The preparation method of described styrene-butadiene rubber, natural rubber, butadiene rubber and high styrene resin and closed-cell secondary foaming material may further comprise the steps:

[0049](1) Mixed rubber G refining: put 100PHR of high styrene resin, 100PHR of natural rubber, and 0.2PHR of stearic acid into a 75L diamond-shaft W-type hammer internal mixer, pressurize to 7 kg, and knead Refining for 8 minutes, continuously filling cold water to cool down during the kneading process, when the temperature reaches 110°C, the material is discharged to obtain compound G; put the compound G into an 18-inch automatic turning mixer, the temperature is controlled at 80°C, and the 2mm turning The material is 180 seconds, the thickness of 2mm is fluttered, cut into corr...

Embodiment 2

[0059] The preparation method of described styrene-butadiene rubber, natural rubber, butadiene rubber and high styrene resin and closed-cell secondary foaming material may further comprise the steps:

[0060] (1) Mixed rubber G refining: put 100PHR of high styrene resin, 100PHR of natural rubber, and 0.1PHR of stearic acid into a 75L diamond-shaft W-type hammer internal mixer, pressurize to 7 kg, and knead Refining for 8 minutes, continuously filling cold water to cool down during the kneading process, when the temperature reaches 115°C, the material is discharged to obtain the compound G; put the compound G into the 18-inch automatic turning mixer, the temperature is controlled at 85°C, and the 2mm turning The material is 180 seconds, the thickness of 2mm is fluttered, cut into corresponding weights and left to stand separately;

[0061] (2) Natural rubber mastication: put 100PHR of natural rubber and 0.1PHR of stearic acid into a 75L diamond-shaft W-type hammer internal mixe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of foam materials and provides a closed-cell two-step foamed material prepared from styrene butadiene rubber, natural rubber, butadiene rubber and high styrene resin, and a preparation method of the closed-cell two-step foamed material. The closed-cell two-step foamed material retains the relatively good elasticity, wear resistance, fracturing resistance and slippery resistance of the styrene butadiene rubber; the addition of the natural rubber improves the rebound resilience, elongation, tensile strength and tear strength of the material; the cold resistance, wear resistance and elasticity of the material are particularly excellent and heat generated under live load is less due to the addition of butadiene rubber; the use of the high styrene resin improves the mechanical rigidity, hardness and stiffness of products, and makes up the cold flow property of the butadiene rubber at normal temperature. The produced product is remarkable in properties such as cold resistance (the lowest temperature reaches -100 DEG C), embossing and the like, and is free of toxicity, odorless and pollution. During the preparation, firstly, the natural rubber is masticated separately, and the high styrene resin and the natural rubber are blended in a ratio of 1:1; and then the two premixed rubbers are blended with styrene butadiene rubber and butadiene rubber, and the process of rolling and standing is carried out, so that the difficulty that the three types of rubber resins are poor in compatibility is overcome.

Description

technical field [0001] The invention relates to the technical field of foaming materials, in particular to a closed-cell secondary foaming material combined with styrene-butadiene rubber, natural rubber, butadiene rubber and high-styrene resin and a preparation method thereof. Background technique [0002] With the maturity of domestic production technology, styrene-butadiene rubber has been widely used in various industries. It has good elasticity, wear resistance, crack resistance, wet skid resistance and price advantages and has become the mainstream rubber type. Low strength, chemical and weather resistance, poor embossing and shaping; natural rubber has good resilience, elongation, tensile strength, and tear strength, but in terms of shortcomings, embossing and plasticity are not good. Good, basically similar to styrene-butadiene rubber; butadiene rubber has very excellent cold resistance (-100°C) elasticity and wear resistance, but poor processability alone, and has a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/06C08L7/00C08L9/00C08K13/02C08K3/22C08K5/09C08K3/04C08K3/34C08K3/06C08J9/04B29C35/02
Inventor 侯汝红陈奕汲
Owner YIBAO FUJIAN POLYMER MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com