High-strength high-hardness high-chromium cast iron plate hammer and preparation method thereof
A high-hardness, cast-iron plate technology, applied in the field of cast-iron materials, can solve problems such as low strength and hardness, crusher damage, plate hammer fracture, etc., and achieve the effect of reasonable composition design, low cost, and improved hardness and strength.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0014] A high-strength, high-hardness, high-chromium cast iron blow bar, the chemical components and mass percentages of which are: Cr23.4-29.8, Ni4.2-5.6, Mo1.2-1.8, Si1.8-2.6, C3.2-4.0 , Mn0.25-0.45, Zr1.4-2.2, Ti1.0-1.5, Ta0.3-0.7, Mg0.5-1.0, Cu0.4-0.6, Al0.3-0.5, Nd0.05-0.1, Er0 .03-0.06, S≤0.03, P≤0.06, the balance is Fe.
[0015] A method for preparing a high-strength, high-hardness, high-chromium cast iron blow bar, comprising the following steps:
[0016] (1) Smelting in an intermediate frequency induction furnace, first add scrap steel, scrap iron, pig iron and ferrochrome to melt, then add ferronickel, ferromolybdenum, ferromanganese, ferrotitanium, copper, tantalum in turn, and adjust after all of them are melted For the composition of molten iron, ferrosilicon and ferrozirconium are added successively within 8-12 minutes before being released from the furnace, and pure aluminum is added for deoxidation within 3-5 minutes before being discharged from the furnace. ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com