A polyether ether ketone modified polytetrafluoroethylene composite material, bearing cage and preparation method thereof

A technology of bearing cage and polytetrafluoroethylene powder, which is applied in the direction of bearing components, shafts and bearings, mechanical equipment, etc., can solve the problem of not meeting the requirements of long service life cage materials, poor wear resistance and bearing capacity, and low mechanical strength And other problems, to achieve the effect of low friction coefficient, good temperature resistance, long service life

Active Publication Date: 2017-08-25
LUOYANG BEARING RES INST CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a polyether ether ketone modified polytetrafluoroethylene composite material, which solves the shortcomings of the existing modified polytetrafluoroethylene composite materials such as low mechanical strength, poor wear resistance and load-bearing capacity, which cannot meet long-term use. Lifetime Bearing Requirements for Cage Material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A polyether ether ketone modified polytetrafluoroethylene composite material, bearing cage and preparation method thereof
  • A polyether ether ketone modified polytetrafluoroethylene composite material, bearing cage and preparation method thereof
  • A polyether ether ketone modified polytetrafluoroethylene composite material, bearing cage and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The polyether ether ketone modified polytetrafluoroethylene composite material in this embodiment is composed of the following components in mass percentage: 20% polyetheretherketone, 8% tungsten disulfide, and the rest is polytetrafluoroethylene.

[0044] The bearing cage of this embodiment is composed of the following components in mass percentage: 20% of polyether ether ketone, 8% of tungsten disulfide, and the rest is polytetrafluoroethylene. That is, the bearing cage of this embodiment adopts the above-mentioned polyether ether ketone modified polytetrafluoroethylene composite material.

[0045] The preparation method of the bearing cage of the present embodiment comprises the following steps:

[0046] 1) Put the polyether ether ketone powder and tungsten disulfide powder in a vacuum drying oven for vacuum drying. During the drying process, the raw materials are spread in the vacuum drying oven, and the thickness of the laying does not exceed 25mm; the vacuum degre...

Embodiment 2

[0055] The polyether ether ketone modified polytetrafluoroethylene composite material in this embodiment is composed of the following components in mass percentage: polyetheretherketone 18%, tungsten disulfide 5%, and the rest is polytetrafluoroethylene.

[0056] The bearing cage of this embodiment is composed of the following components in mass percentage: 18% of polyether ether ketone, 5% of tungsten disulfide, and the rest is polytetrafluoroethylene. That is, the bearing cage of this embodiment adopts the above-mentioned polyether ether ketone modified polytetrafluoroethylene composite material.

[0057] The preparation method of the bearing cage of the present embodiment comprises the following steps:

[0058] 1) Put polyether ether ketone powder and tungsten disulfide powder in a vacuum drying oven for vacuum drying. During the drying process, the raw materials are tiled in the vacuum drying oven, and the tile thickness does not exceed 25mm; the vacuum degree of vacuum dr...

Embodiment 3

[0066] The polyether ether ketone modified polytetrafluoroethylene composite material in this embodiment is composed of the following components in mass percentage: 20% polyetheretherketone, 5% tungsten disulfide, and the rest is polytetrafluoroethylene.

[0067] The bearing cage of this embodiment is composed of the following components in mass percentage: 20% of polyether ether ketone, 5% of tungsten disulfide, and the rest is polytetrafluoroethylene. That is, the bearing cage of this embodiment adopts the above-mentioned polyether ether ketone modified polytetrafluoroethylene composite material.

[0068] The preparation method of the bearing cage of the present embodiment comprises the following steps:

[0069] 1) Put the polyether ether ketone powder and tungsten disulfide powder in a vacuum drying oven for vacuum drying. During the drying process, the raw materials are spread in the vacuum drying oven, and the thickness of the laying does not exceed 25mm; the vacuum degre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyether-ether-ketone modified polytetrafluoroethylene composite material, a bearing retainer and a making method of the bearing retainer. The composite material comprises, by mass, 18-25% of polyether ether ketone, 5-8% of tungsten disulfide, and the balance of polytetrafluoroethylene. The composite material comprises polytetrafluoroethylene, polyether-ether-ketone and tungsten disulfide. Polyether-ether-ketone has good temperature resistance, hydrolysis resistance, compression strength and corrosion resistance, has a low friction coefficient and has wear fastness, tungsten disulfide has high compression strength and high oxidation resistance, and very low friction coefficient, and polyether-ether-ketone and tungsten disulfide are used to modify polytetrafluoroethylene as fillers, so the obtained composite material reserves the lubrication performance of polytetrafluoroethylene, improves the dimension stability, the compression strength and the wear resistance of polytetrafluoroethylene, and has a greatly higher thermal deformation temperature than a pure polytetrafluoroethylene material, thereby requirements of the material of the retainer by long life bearings are met.

Description

technical field [0001] The invention belongs to the technical field of non-metallic material cages, and specifically relates to a polyether ether ketone modified polytetrafluoroethylene composite material, and also relates to a bearing cage using the composite material and a preparation method thereof. Background technique [0002] Bearing is an important transmission part in mechanical equipment. Its main function is to support the mechanical rotating body, reduce the friction coefficient during its movement and ensure its rotation accuracy. According to the different friction properties of moving elements, bearings can be divided into two categories: rolling bearings and sliding bearings. Rolling bearings are generally composed of four parts: outer ring, inner ring, rolling body and cage. Cage (also known as bearing cage) refers to a bearing part that partially wraps all or part of the rolling elements and moves with them to isolate the rolling elements, usually guide the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/18C08L61/16C08K3/30B29C43/36B29C43/02F16C33/44F16C33/56
CPCY02T10/86
Inventor 王枫王萍孙小波王子君时连卫李雪梅
Owner LUOYANG BEARING RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com