Modified calcium carbonate filler for paint and preparation method thereof

Abstract

The invention discloses a modified calcium carbonate filler for paint and a preparation method thereof. The filler is characterized by being prepared from the following raw materials in parts by weight: 100 to 150 parts of calcium carbonate, 30 to 50 parts of sodium oleate, 0.3 to 0.7 part of sodium dodecyl benzene sulfonate, 1 to 3 parts of sodium bicarbonate, 4 to 8 parts of styrene, 0.02 to 0.05 part of potassium persulfate, 3 to 5 parts of gas-phase silicon dioxide, 2 to 3 parts of organic bentonite, 2 to 3 parts of hectorite powder, 1 to 3 parts of palm oil, 2 to 4 parts of calcium carbide slag powder, and a proper amount of deionized water. The added hectorite powder, palm oil, and calcium carbide slag powder can generate a synergetic effect, and can improve the lipophilicity of calcium carbonate, so the modified calcium carbonate can be well dispersed in paint, and the interface interaction is enhanced. Furthermore, the technology is simple and is easy to promote, the cost is low, no pollution is generated, and thus the application prospect is wide.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a modified calcium carbonate filler for coatings and a preparation method thereof. Background technique [0002] As a filler for rubber and plastic products, calcium carbonate can improve the heat resistance, wear resistance, dimensional stability, rigidity and processability of the product, and reduce the cost of the product, but its surface has hydroxyl groups with strong hydrophilicity. It presents a strong alkalinity. This hydrophilic and oleophobic property makes the affinity between calcium carbonate and organic polymers poor, and it is easy to form aggregates, resulting in uneven dispersion in the polymer, resulting in two materials. The effect of direct application is not good, and calcium carbonate is used as a filler, and its acid resistance, smoothness, whiteness and other properties need to be further improved. Therefore, in order to improve the reinforcing effect of...

AI Technical Summary

Problems solved by technology

[0002] As a filler for rubber and plastic products, calcium carbonate can improve the heat resistance, wear resistance, dimensional stability, rigidity and processability of the product, and reduce the cost of the product, but its surface has hydroxyl groups with strong hydrophilicity. It presents a strong alkalinity. This hydrophilic and oleophobic property makes the affinity between calcium carbonate and organic polymers poor, and it is easy to form aggregates, resulting in uneven dispersion in the polymer, resulting in two materials. The effect of direct application is not good, and calcium carbonate is used as a filler, and its acid resistance, smoothness, whiteness and other properties need to be further improved. Therefore, in order to improve the reinforcing effect of calcium carbonate and the dispersion performance in composite materials And the physical properties of modified calcium carbonate filled composite materials, it is necessary to use different surface modifiers and treatment methods to modify the surface of calcium carbonate powder, thereby broadening the application field of calcium carbonate