Modified calcium carbonate for automobile plastic and preparation method thereof

Abstract

The invention discloses modified calcium carbonate for automobile plastic and a preparation method thereof. The modified calcium carbonate is characterized by being composed of the following raw materials in parts by weight: 100 to 150 parts of calcium carbonate, 30 to 50 parts of sodium oleate, 0.3 to 0.7 part of sodium dodecyl benzene sulfonate, 1 to 3 parts of sodium bicarbonate, 4 to 8 parts of styrene, 0.02 to 0.05 part of potassium persulfate, 3 to 5 parts of gas-phase silicon dioxide, 2 to 3 parts of organic bentonite, 2 to 4 parts of zinc oxide, 1 to 2 parts of silane coupling agent kh550, 3 to 4 parts of meerschaum powder, and a proper amount of deionized water. The added zinc oxide and meerschaum powder can be bonded to calcium carbonate under the action of coupling agent, thus the sterilizing performance, thermal insulation property, and anticorrosion performance of calcium carbonate are further enhanced, the modified calcium carbonate can be applied to automobile plastic to prolong the service life of automobile shell, at the same time, anti-aging performance and decorative effect of the automobile plastic are also strengthened, the automobile quality is improved therefore, and the modified calcium carbonate is worthy to promote.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a modified calcium carbonate for automobile plastics and a preparation method thereof. Background technique [0002] As a filler for rubber and plastic products, calcium carbonate can improve the heat resistance, wear resistance, dimensional stability, rigidity and processability of the product, and reduce the cost of the product, but its surface has hydroxyl groups with strong hydrophilicity. It presents a strong alkalinity. This hydrophilic and oleophobic property makes the affinity between calcium carbonate and organic polymers poor, and it is easy to form aggregates, resulting in uneven dispersion in the polymer, resulting in two materials. The effect of direct application is not good, and calcium carbonate is used as a filler, and its acid resistance, smoothness, whiteness and other properties need to be further improved. Therefore, in order to improve the reinforcing effec...

AI Technical Summary

Problems solved by technology

[0002] As a filler for rubber and plastic products, calcium carbonate can improve the heat resistance, wear resistance, dimensional stability, rigidity and processability of the product, and reduce the cost of the product, but its surface has hydroxyl groups with strong hydrophilicity. It presents a strong alkalinity. This hydrophilic and oleophobic property makes the affinity between calcium carbonate and organic polymers poor, and it is easy to form aggregates, resulting in uneven dispersion in the polymer, resulting in two materials. The effect of direct application is not good, and calcium carbonate is used as a filler, and its acid resistance, smoothness, whiteness and other properties need to be further improved. Therefore, in order to improve the reinforcing effect of calcium carbonate and the dispersion performance in composite materials And the physical properties of modified calcium carbonate filled composite materials, it is necessary to use different surface modifiers and treatment methods to modify the surface of calcium carbonate powder, thereby broadening the application field of calcium carbonate