Double-layer reinforced modified polyolefin drpo corrugated pipe for buried drainage and sewage

A technology of polyolefin and bellows, which is applied in the field of polymer composite materials, can solve problems such as low ring flexibility and insufficient ring stiffness, and achieve the effect of meeting performance requirements and improving ring stiffness and ring flexibility

Active Publication Date: 2017-05-03
源单新材料科技成都有限责任公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a double-layer reinforced modified polyolefin DRPO corrugated pipe for buried drainage and sewage to solve the problems of insufficient ring stiffness and low ring flexibility of existing polyolefin buried drainage and sewage pipes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-layer reinforced modified polyolefin drpo corrugated pipe for buried drainage and sewage
  • Double-layer reinforced modified polyolefin drpo corrugated pipe for buried drainage and sewage

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045]Preparation of Modified Polyolefin Elastomer BPOE

[0046] Configure raw materials by the following parts by weight:

[0047] Ethylene octene copolymer (POE): 100 parts

[0048] Styrene (St): 2 parts

[0049] Glycidyl methacrylate (GMA): 6 parts

[0050] Dicumyl peroxide (DCP): 0.1 part;

[0051] The grafting equipment adopts twin-screw extruder to prepare modified POE by reactive extrusion process, and the process conditions are as follows:

[0052] The temperature of each section of the twin-screw extruder is (°C): 160, 170, 185, 190, 190.

[0053] Preparation of modified talcum powder

[0054] Configure raw materials by the following parts by weight:

[0055] Talcum powder 100 parts,

[0056] 1 part of silane coupling agent,

[0057] Aluminate coupling agent 0.5 parts.

[0058] First dry the weighed talc powder in an oven at 100°C for 3 hours, add it to the high-speed mixer, then add the aluminate coupling agent weighed in proportion, mix at high speed for 5 ...

Embodiment 2

[0067] Preparation of Modified Polyolefin Elastomer BPOE

[0068] Configure raw materials by the following parts by weight:

[0069] Ethylene octene copolymer (POE): 100 parts

[0070] Styrene (St): 7 parts

[0071] Glycidyl methacrylate (GMA): 3 parts

[0072] Dicumyl peroxide (DCP): 0.4 parts;

[0073] The grafting equipment adopts twin-screw extruder to prepare modified POE by reactive extrusion process, and the process conditions are as follows:

[0074] The temperature of each section of the twin-screw extruder is (°C): 160, 170, 185, 190, 190.

[0075] Preparation of modified talcum powder

[0076] Configure raw materials by the following parts by weight:

[0077] Talcum powder 100 parts,

[0078] 3 parts of silane coupling agent,

[0079] Aluminate coupling agent 1.5 parts.

[0080] First dry the weighed talc powder in an oven at 100°C for 3 hours, add it to the high-speed mixer, then add the aluminate coupling agent weighed in proportion, mix at high speed for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an underground double-layer reinforced and modified polyolefin (DRPO) corrugated pipe for water draining and sewage discharging. The pipe is formed by bonding an inner wall and an outer wall through hot melting, wherein the outer wall and the inner wall are both made of modified polyolefin materials. The modified polyolefin materials comprise, by weight, 50-75 parts of polyolefin, 5-10 parts of modified polyolefin elastomer (BPOE) and 20-40 parts of activated talcum powder. The DRPO corrugated pipe is mainly used for underground water draining and sewage discharging pipes.

Description

technical field [0001] The invention belongs to the field of polymer composite materials, and in particular relates to a double-layer reinforced modified polyolefin DRPO corrugated pipe for buried drainage and sewage discharge. Background technique [0002] At present, my country's drainage pipe network system is still dominated by traditional reinforced concrete pipes, ceramic pipes, and cast iron pipes, but their construction is difficult and the connections between pipes are complicated, often resulting in huge construction waste. Especially in long-term use, often due to corrosion, damage, leakage, especially large-area sewage leakage, less and less underground water sources have been seriously polluted. Solving the problem of water shortage and pollution in the city is related to the sustainable development of the city, and it is also a major issue for the current and long-term development of our country. According to the development of plastic pipes in developed count...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L11/11F16L11/15F16L9/12C08L23/06C08L23/14C08L51/06C08K9/06C08K9/04C08K3/34C08F255/02
CPCC08F255/02C08L23/06C08L23/14C08L2203/18C08L2207/062C08L2207/14F16L9/12F16L11/11F16L11/15C08L51/06C08K9/06C08K9/04C08K3/34C08F220/325
Inventor 梁军李莉
Owner 源单新材料科技成都有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products