Boric sludge pellet binder/iron smelting auxiliary and preparation method of boric sludge pellet binder/iron smelting auxiliary

A technology of binder and boron mud, applied in the field of metallurgy, can solve the problems of difficult mixing of magnesium components, high roasting temperature of pellets, low compressive strength, etc., and achieves good green strength, low roasting temperature and compressive strength. high effect

Inactive Publication Date: 2015-10-14
YINGKOU LINHEMAO TECH DEV CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a boron mud pellet binder / ironmaking auxiliary and its preparation method, which can completely replace the commonly used bentonite, and can also solve the problem of magnesium content in pellets (ironmaking additives). Auxiliaries) are difficult to add, resulting in problems such as high calcination temperature and low compressive strength of the pellets; boron mud is used as the main raw material, and ironmaking additives such as magnesium are added at the same time, which greatly reduces the harmful effects of silica and other The content of ingredients can significantly improve the fluidity of molten iron and slag during blast furnace ironmaking, and has a good desulfurization effect, and has a significant improvement in the smoothness of the furnace condition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The implementation process and effects of the present invention will be described in detail below through specific examples, in order to better understand the essence and characteristics of the present invention, and not as a limitation to the scope of implementation of this case.

[0021] The boron mud in the raw material used in the present embodiment, its main chemical composition and mass percent are:

[0022] Magnesium oxide 38%, boron 2%, iron 6%, sodium 2.1%, silicon dioxide 26%, sulfur 0.003%, phosphorus 0.004%;

[0023] It can be seen that there are three problems as follows:

[0024] (1) The content of magnesium is insufficient to meet the requirements of iron-making additives;

[0025] (2) Silicon dioxide and sodium are harmful components in the ironmaking process, and the content is relatively high;

[0026] (3) The material has no viscosity.

[0027] In order to solve the above problems, after trial and error research and economic and technical analysis,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
relative humidityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a boric sludge pellet binder / iron smelting auxiliary and a preparation method of the boric sludge pellet binder / iron smelting auxiliary, and belongs to the technical field of metallurgy. The boric sludge pellet binder / iron smelting auxiliary comprises the following raw materials in percentage by weight: 75-84% of boric sludge, 6-10% of boric ore powder and 10-15% of caustic-burned magnesia powder, wherein the content of boron in the boric ore powder is 10-16%, and the content of magnesium in the boric ore powder is 70-90%. The boric sludge pellet binder / iron smelting auxiliary can completely replace bentonite usually used and solve the problems that the calcination temperature of pellets is too high and the compressive strength of the pellets is lower because the magnesium component (the iron smelting auxiliary) in pellet ore is difficult to compound and add; the boric sludge is used as the main raw material, besides iron smelting auxiliaries such as the magnesium component are added, so that the content of noxious constituent such as silicon dioxide is greatly reduced, and the fluidity of molten iron and slag is obviously improved during blast-furnace iron smelting; the boric sludge pellet binder / iron smelting auxiliary has a good desulfurization effect, so that the smooth and stable furnace condition is obviously improved.

Description

technical field [0001] The invention relates to a boron mud pellet binder / ironmaking auxiliary and a preparation method thereof, belonging to the technical field of metallurgy. Background technique [0002] A large amount of borax tailings (also known as borax mud) will be discharged during the production of borax. Because the boron mud is very fine, the -200 mesh sieve pass rate exceeds 70%, the surface will be dusty after air drying, and because the boron mud contains potassium and sodium components, it will pollute the groundwater source. [0003] At present, the country generally adopts a fixed-point centralized stacking method to control it, but it has not received good results. [0004] According to laboratory analysis, the content of magnesium oxide and boron in boron mud is relatively high, which can play an auxiliary role in blast furnace ironmaking. Therefore, using boron mud to prepare pellet binder is a way to turn boron mud from waste into treasure. [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/242
Inventor 张志林
Owner YINGKOU LINHEMAO TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products