Paint for projection and preparation method of paint

A coating and projection technology, applied in the coating and other directions, can solve the problem of additional purchase of the curtain, and achieve the effect of improving the projection effect, increasing the gain, and improving the reflection performance.

Inactive Publication Date: 2015-09-30
香山红叶集团有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Projection screens, or projection walls, are the image substrates that are often needed for projection...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paint for projection and preparation method of paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1 Coating 1

[0020] In the first step, 25g of acrylic acid, 35g of resin and 3g of titanium dioxide were mixed, and stirred in a stirring tank for 60 minutes to obtain a mixture 1;

[0021] In the second step, take 2 g of microcrystalline cellulose, 4 g of cellulose ether and 0.2 g of N,N-dimethylethanolamine, add the mixture 1 obtained in the first step, and continue stirring for 35 minutes to obtain a mixture 2;

[0022] In the third step, take 2g of borosilicate, 0.5g of nanopowder, 3g of polyimide fiber, 2g of alkylcyclohexylbromobenzene and 1g of 4-n-pentyl-4'-cyanobiphenyl, mix and grind And sieve 900 mesh, obtain mixture 3;

[0023] In the fourth step, add 12 g of ethyl ethoxy propionate to the mixture 2, mixture 3, 0.2 g of defoamer, 3 g of dispersant and 0.3 g of leveling agent obtained in the third step, mix evenly and stir for 60 minutes to obtain coating.

[0024] The components of the resin are: organosilicon modified epoxy resin, alkyd resin an...

Embodiment 2

[0028] Example 2 Coating 2

[0029] In the first step, mix 20 g of acrylic acid, 30 g of resin and 2 g of titanium dioxide, and stir in a stirring tank for 50 minutes to obtain a mixture 1;

[0030] In the second step, take 1 g of microcrystalline cellulose, 3 g of cellulose ether and 0.2 g of N,N-dimethylethanolamine, add the mixture 1 obtained in the first step, and continue stirring for 30 minutes to obtain a mixture 2;

[0031] In the third step, take 1g of borosilicate, 0.3g of nanopowder, 2g of polyimide fiber, 1g of alkylcyclohexylbromobenzene and 1g of 4-n-pentyl-4'-cyanobiphenyl, mix and grind And sieve 900 mesh, obtain mixture 3;

[0032] In the fourth step, add 10 g of ethyl ethoxy propionate, mix well and stir for 50 minutes to obtain coating.

[0033] Wherein, the components of the resin are: silicone-modified epoxy resin, alkyd resin and fluororesin, and the mass-to-number ratio thereof is 1:1:0.5.

[0034] Wherein, the particle size of the borosilicate is 10...

Embodiment 3

[0037] Example 3 Coating 3

[0038] In the first step, mix 30g of acrylic acid, 40g of resin and 4g of titanium dioxide, and stir in a stirring tank for 80 minutes to obtain mixture 1;

[0039] In the second step, take 2 g of microcrystalline cellulose, 5 g of cellulose ether and 0.5 g of N,N-dimethylethanolamine, add the mixture 1 obtained in the first step, and continue stirring for 40 minutes to obtain a mixture 2;

[0040] The third step is to take 2g of borosilicate, 0.8g of nanopowder, 4g of polyimide fiber, 2g of alkylcyclohexylbromobenzene and 3g of 4-n-pentyl-4'-cyanobiphenyl, mix and grind And sieve 950 mesh, obtain mixture 3;

[0041] In the fourth step, add 15 g of ethyl ethoxy propionate and mix uniformly for 100 minutes to obtain coating.

[0042] The components of the resin are: organosilicon modified epoxy resin, alkyd resin and fluororesin, and the mass-to-number ratio thereof is 2:1.5:0.8.

[0043] Wherein, the particle size of the borosilicate is 50 μm, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses paint for projection and a preparation method of the paint. The paint comprises the following components in parts by mass: 20-30 parts of crylic acid, 30-40 parts of resin, 1-2 parts of microcrystalline cellulose, 3-5 parts of cellulose ether, 1-2 parts of borosilicate, 0.3-0.8 part of nano-powder, 2-4 parts of titanium dioxide, 2-4 parts of aromatic polyimide fiber, 1-2 parts of alkyl cyclohexyl bromobenzene, 1-3 parts of 4-n-pentyl-4'-cyanobiphenyl, 0.2-0.3 part of a defoaming agent, 2-4 parts of a dispersing agent, 0.2-0.4 part of a flatting agent, 0.2-0.5 part of N,N-dimethylethanolamine and 10-15 parts of 3-ethoxypropionic acid ethyl ester. The paint for projection and the preparation method of the paint, provided by the invention, have the benefits as follows: the reflecting property of a wall body during projection can be improved by the paint, the viewing angle balance is improved, the gain is increased, the projection effect is further improved, and the pain is environment-friendly, wear-resistant, flame-retardant and has a better stability.

Description

technical field [0001] The invention relates to the technical field of chemical engineering, in particular to a projection coating and a preparation method thereof. Background technique [0002] Coating refers to a class of liquid or solid materials that can form a thin film on the surface of an object under certain conditions for protection, decoration or other special functions. According to the classification of modern chemical products, coatings belong to fine chemical products. Modern coatings are gradually becoming a class of multifunctional engineering materials and an important industry in the chemical industry. [0003] With the development of society, people are doing more and more research on coatings, and their functions are further diversified. [0004] Now in our daily life, projection is becoming more and more popular. Or with the development of projection technology, it has gradually entered the family. On the one hand, projection has great requirements on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/02C09D7/12
Inventor 乌春丽安邦于萍厉祥成姜杰田鹏
Owner 香山红叶集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka