ZnO double-flower-head structure and preparation method thereof

A flower-like structure and flower head technology, applied in the direction of zinc oxide/zinc hydroxide, etc., can solve the problems of poor size control, poor shape uniformity, poor repeatability, etc., and achieve low raw material prices, special shape, and good performance. Effect

Inactive Publication Date: 2015-09-09
UNIV OF JINAN
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Limited by the preparation process, poor repeatability, low crystallinity, poor shape uniformity, and poor size control have become the main problems facing high-efficiency ZnO micro-nano structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ZnO double-flower-head structure and preparation method thereof
  • ZnO double-flower-head structure and preparation method thereof
  • ZnO double-flower-head structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1.1 Add 0.439 g of zinc acetate to a mixed solvent of 30 mL of ethylene glycol and 1.5 mL of water and stir until clear;

[0033] 1.2 Add 3 mL of ethanolamine dropwise to the above solution and stir evenly;

[0034] 1.3 Transfer the above solution to the reactor and react at 150 °C for 12 h;

[0035] 1.4 After the reaction, the product was obtained after centrifugation and washing.

[0036] SEM of the product as figure 1 As shown in the figure, it can be seen that the obtained product is a double flower head structure formed by closely arranged ZnO rods. The two flower heads are connected at the bottom, similar in size, and on the same horizontal line. The diameter of each flower head is 2.1-2.5 μm , with a length of 0.8-1.6 μm; the structural unit ZnO rods have a diameter of 0.15-0.22 μm and a length of 0.8-1.6 μm.

[0037] The XRD pattern of the product is as follows figure 2 As shown, the XRD results are consistent with the standard XRD card (36-1451), which pro...

Embodiment 2

[0040]2.1 Add 0.535 g of zinc nitrate hexahydrate to a mixed solvent of 30 mL of ethylene glycol and 1.5 mL of water and stir until clear;

[0041] 2.2 Add 2.7 mL of ethanolamine dropwise to the above solution and stir evenly;

[0042] 2.3 Transfer the above solution to the reactor and react at 130 °C for 2 h;

[0043] 2.4 After the reaction, after centrifugation and washing, the obtained product is a double flower head structure formed by closely arranged ZnO rods, in which the bottoms of the two divergent flower heads are connected, similar in size, and on the same horizontal line. The diameter is 0.12-0.16 μm, and the length is 0.07-0.14 μm; the diameter of its structural unit ZnO rod is 0.06-0.12 μm, and the length is 0.07-0.14 μm.

[0044] The product is irradiated by a 365 nm ultraviolet lamp, and the illuminated area is 1.5cm 2 Under the condition, its photocurrent intensity can reach -1.50×10 -6 a.

Embodiment 3

[0046] 3.1 Add 0.850 g of zinc nitrate hexahydrate to a mixed solvent of 30 mL of ethylene glycol and 1.6 mL of water and stir until clear;

[0047] 3.2 Add 4.5 mL of ethanolamine dropwise to the above solution and stir evenly;

[0048] 3.3 Transfer the above solution to the reactor and react at 170 °C for 27 h;

[0049] 3.4 After the reaction, after centrifugation and washing, the obtained product is a double flower head structure formed by closely arranged ZnO rods, in which two divergent flower heads are connected at the bottom, similar in size, and on the same horizontal line. The diameter of each flower head is 7.2-7.6 μm, the length is 3.0-5.6 μm; the diameter of its structural unit ZnO rod is 0.38-0.45 μm, and the length is 3.0-5.6 μm.

[0050] The product is irradiated by a 365 nm ultraviolet lamp, and the illuminated area is 1.5cm 2 Under the condition, its photocurrent intensity can reach -1.72×10 -6 a.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a ZnO double-flower-head structure. The preparation method of the ZnO double-flower-head structure comprises the following steps: adding divalent zinc salt into a mixed solvent of ethylene glycol and water, and stirring, so that a transparent solution is obtained; continuously dropwise adding right amount of ethanolamine, so that a precursor solution is obtained; heating the precursor solution to 130-170 DEG C by utilizing a solvothermal method, and carrying out heat preservation for a period of time; and carrying out centrifugal separation and washing after reaction is finished, so that the ZnO double-flower-head structure is obtained. The preparation method of the ZnO double-flower-head structure has the advantages that the needed raw materials are available, a reaction technology is simple, the product size distribution range is narrow, and important significance is provided for fine control and large-scale application of the ZnO double-flower-head structure; and the obtained ZnO double-flower-head structure has good repeatability, the yield is high, the particle size is controllable, and the ZnO double-flower-head structure has relatively good development prospects in the fields of photovoltaic conversion, photocatalysis and the like.

Description

Technical field [0001] The present invention involves a preparation method and income product of the ZNO microman structure, which specifically involves the preparation method and product of the ZNO double flower head structure. Background technique [0002] ZNO is an important semiconductor oxide material with a wide direct band (3.37EV) and a large excitement (60MEV). It can achieve the severe launch of ultraviolet light at room temperature. In recent years, it has been widely used in recent years.In the fields of light emitting diode, dye sensitization solar cells, photocatalytic, osteitted materials, biosensor and other fields, its development prospects are huge.At present, scholars at home and abroad can obtain ZNO micro -nano structures with different appearance methods, and focus on studying the growth habits and mechanisms of the growth habits and mechanisms of ZNO and their composite materials.One of the research hotspots in the field. [0003] By selecting the appropria...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G9/02
Inventor 马谦陈玲王俊鹏车全德傅琳景杨萍
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com