Porous asphalt material as well as preparation method and application thereof

A technology of porous materials and asphalt, applied in the field of asphalt, can solve the problems of low specific surface area, poor safety performance and large average pore size of hard carbon materials, and achieve good gas adsorption and storage performance, good dye adsorption performance, and mild production conditions. Effect

Active Publication Date: 2015-09-02
XIAMEN UNIV
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] It can be seen from the above patents and documents that using mesophase pitch as a carbon source and silica or silica gel as a template requires hydrofluoric acid to remove the template. The operation is more complicated and the pollution is serious; The specific surface area of ​​the material is low, and the average pore size is large; the process of preparing porous carbon by heating with coal tar pitch as a carbon source, using a hard template or chemical activation method, has a long activation time, high energy consumption, high cost, and serious pollution
For example, the preparation of porous carbon materials with high specific surface area requires high temperature and high pressure conditions, high requirements for equipment, and poor safety performance
These problems have limited the development of porous materials such as activated carbon prepared from asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous asphalt material as well as preparation method and application thereof
  • Porous asphalt material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation specific surface area is 700m 2 / g, the pore volume is 0.30m 3 / g hypercrosslinked asphalt porous material.

[0028] The present embodiment adopts following formula:

[0029] Petroleum asphalt: 100kg;

[0030] Dimethoxymethane: 49kg;

[0031] Anhydrous ferric chloride: 210kg;

[0032] Dichloroethane: 500L.

[0033] Prepare asphalt porous material with above-mentioned formula composition according to following method:

[0034] 1. Dissolve the weighed petroleum asphalt in 1,2-dichloroethane. After the dissolution is complete, add dimethoxymethane, dissolve, stir and mix evenly, then add ferric chloride, mix evenly.

[0035] 2. Add the mixed composition to 80°C at one time, and crosslink for 12 hours.

[0036] 3. Add the solid obtained in step 2 into methanol, wash away part of the ferric chloride, extract with methanol for 5 hours, then extract with dichloromethane for 5 hours, and dry at 80°C for 12 hours.

[0037] The asphalt porous material prep...

Embodiment 2

[0039] The preparation specific surface area is 760m 2 / g, the pore volume is 0.32m 3 / g hypercrosslinked asphalt porous material.

[0040] The present embodiment adopts following formula:

[0041] Petroleum asphalt: 100kg;

[0042] Dimethoxymethane: 82kg;

[0043] Anhydrous aluminum trichloride: 350kg;

[0044] Dichloroethane: 500L.

[0045] Prepare asphalt porous material with above-mentioned formula composition according to following method:

[0046] 1. Dissolve the weighed petroleum asphalt in 1,2-dichloroethane. After the dissolution is complete, add dimethoxymethane, dissolve, stir and mix evenly, then add ferric chloride, mix evenly.

[0047] 2. Add the mixed composition to 80°C at one time, and crosslink for 12 hours.

[0048] 3. Add the solid obtained in step 2 into methanol, wash away part of the ferric chloride, extract with methanol for 5 hours, then extract with dichloromethane for 5 hours, and dry at 80°C for 12 hours.

Embodiment 3

[0050] The preparation specific surface area is 1452m 2 / g, the pore volume is 0.60m 3 / g hypercrosslinked asphalt porous material.

[0051] The present embodiment adopts following formula:

[0052] Petroleum asphalt: 100kg;

[0053] Biphenyl dichlorobenzyl: 320kg;

[0054] Anhydrous ferric chloride: 420kg;

[0055] Dichloroethane: 500L.

[0056] Prepare asphalt porous material with above-mentioned formula composition according to following method:

[0057] 1. Dissolve the weighed petroleum asphalt in 1,2-dichloroethane. After the dissolution is complete, add dimethoxymethane, dissolve, stir and mix evenly, then add ferric chloride, mix evenly.

[0058] 2. Add the mixed composition to 80°C at one time, and crosslink for 12 hours.

[0059] 3. Add the solid obtained in step 2 into methanol, wash away part of the ferric chloride, extract with methanol for 5 hours, then extract with dichloromethane for 5 hours, and dry at 80°C for 12 hours.

[0060] The asphalt porous mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Login to View More

Abstract

The invention provides a porous asphalt material as well as a preparation method and application thereof and relates to asphalt. The porous asphalt material comprises the raw materials of petroleum asphalt and a cross-linking agent according to the mass ratio of 1: (0.49-6.4). The preparation method comprises the following steps: adding the petroleum asphalt, the cross-linking agent and a cross-linking catalyst into a solvent sequentially, heating for cross-linking reaction, cleaning a product obtained through reaction through methanol, then extracting the product obtained through reaction through methanol and dichloromethane and drying so as to obtain the porous asphalt material. The degree of cross-linking of the prepared porous asphalt material reaches 94% or above, the porous asphalt material passes a nitrogen adsorption test at 77 K, and results of a CO2 adsorption test under 1 bar at 273 k and 298 k, an H2 adsorption test under 1 bar at 77 k and a methylene blue dye adsorption test at 298 k for 1 h by the porous asphalt material show that the porous asphalt material can be applied to the adsorption application fields of gas adsorption and storage, dye adsorption and treatment and the like.

Description

technical field [0001] The invention relates to asphalt, in particular to an asphalt porous material and its preparation method and application. Background technique [0002] Bitumen is a product obtained during the processing of crude oil. It is composed of hydrocarbons and their derivatives of different molecular weights. It is a black or dark brown viscous liquid or solid at room temperature. It is an organic gelatinous substance. . Petroleum pitch is obtained by refining high-viscosity oil through vacuum distillation, and has no fixed chemical composition and physical constants. However, it cannot be used directly because it contains a large amount of colloid and asphaltenes, has a high acid value, and has a low viscosity index. [0003] Porous carbon materials prepared from pitch, such as activated carbon, etc. [0004] Chinese patent 200910043229.2 discloses a preparation method of a porous carbon material for energy storage. In this method, the specific surface ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/26B01J20/30B01D53/02C02F1/28
CPCY02C20/40
Inventor 李磊李文庆张爱娟丁磊
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More